Synthesis and Antibacterial Activity of Metal(loid) Nanostructures by Environmental Multi-Metal(loid) Resistant Bacteria and Metal(loid)-Reducing Flavoproteins

Microbes are suitable candidates to recover and decontaminate different environments from soluble metal ions, either via reduction or precipitation to generate insoluble, non-toxic derivatives. In general, microorganisms reduce toxic metal ions generating nanostructures (NS), which display great applicability in biotechnological processes. Since the molecular bases of bacterial reduction are still unknown, the search for new -environmentally safe and less expensive- methods to synthesize NS have made biological systems attractive candidates. Here, 47 microorganisms isolated from a number of environmental samples were analyzed for their tolerance or sensitivity to 19 metal(loid)s. Ten of them were highly tolerant to some of them and were assessed for their ability to reduce these toxicants in vitro. All isolates were analyzed by 16S rRNA gene sequencing, fatty acids composition, biochemical tests and electron microscopy. Results showed that they belong to the Enterobacter, Staphylococcus, Acinetobacter, and Exiguobacterium genera. Most strains displayed metal(loid)-reducing activity using either NADH or NADPH as cofactor. While Acinetobacter schindleri showed the highest tellurite (TeO32-) and tetrachloro aurate (AuCl4-) reducing activity, Staphylococcus sciuri and Exiguobacterium acetylicum exhibited selenite (SeO32-) and silver (Ag+) reducing activity, respectively. Based on these results, we used these bacteria to synthetize, in vivo and in vitro Te, Se, Au, and Ag-containing nanostructures. On the other hand, we also used purified E. cloacae glutathione reductase to synthesize in vitro Te-, Ag-, and Se-containing NS, whose morphology, size, composition, and chemical composition were evaluated. Finally, we assessed the putative anti-bacterial activity exhibited by the in vitro synthesized NS: Te-containing NS were more effective than Au-NS in inhibiting Escherichia coli and Listeria monocytogenes growth. Aerobically synthesized TeNS using MF09 crude extracts showed MICs of 45- and 66- μg/ml for E. coli and L. monocytogenes, respectively. Similar MIC values (40 and 82 μg/ml, respectively) were observed for TeNS generated using crude extracts from gorA-overexpressing E. coli. In turn, AuNS MICs for E. coli and L. monocytogenes were 64- and 68- μg/ml, respectively.


INTRODUCTION
More than half of the elements in the Periodic Table are represented by metals and metalloids. Whereas some of them are essential for different cellular processes, including electron transfer, enzyme catalysis, and stabilization of protein structure, others such as Ag + , Hg + , SeO 2− 4 , and TeO 2− 4 are highly toxic even at very low concentrations (Pérez et al., 2007;Zannoni et al., 2008;Lemire et al., 2013). Thus, organisms like bacteria must maintain a strict balance of the intracellular concentration of these metal(loid)s. Under aerobic conditions the toxicity of compounds containing these elements is mainly related to the production of reactive oxygen species (ROS), which can attack key cell components including polyunsaturated fatty acids, proteins, and nucleic acids (Borsetti et al., 2005;Tremaroli et al., 2007;Vrionis et al., 2015). Additionally, protein carbonylation (Contreras and Vásquez, 2010), [4Fe-4S] cluster dismantling of iron-sulfur proteins (Calderón et al., 2009), membrane lipid peroxidation (Lemire et al., 2013;Pradenas et al., 2013), blocking of cysteine and methionine residues (Stolz and Oremland, 1999), increased cell permeability, and the interference of metabolic pathways have also been observed (Carotti et al., 2000).
To date, a number of genetic and biochemical mechanisms that microbial systems use to cope with the toxicity of defined metal(loid)s are relatively well known; however, a strategy providing universal resistance to all these toxicants has not been reported so far. In general, one of the most common strategies employed by microbes to tolerate high metal(loid) concentrations, is their chemical modification to less-toxic forms (Silver and Phung, 2005). For instance, this kind of resistance mechanisms have been observed in Rhodobacter capsulatus (Turner et al., 2011), Geobacillus sp. (Correa-Llantén et al., 2013), and Shewanella oneidensis (Klonowska et al., 2005) which reduce Te (IV), Au (III) and Se (IV), respectively.
Metal(loid) reduction by microbial systems could be of great help in decontaminating soluble metal ions from soils, forming insoluble, less-toxic derivatives that often generate metal arrangements at the nanoscale (Narayanan and Sakthivel, 2010;Thakkar et al., 2010), also known as nanostructures (NS) exhibiting one or more dimensions <100 nm. Gold (Correa-Llantén et al., 2013), selenium (Song et al., 2017), silver (Gurunathan et al., 2009), tellurium (Arenas-Salinas et al., 2016), and uranium (Suresh, 2012) NS have been reported, opening a great interest because of their potential application in the field of biotechnology.
Summarizing, since NS production by chemical methods often involve high temperature, anaerobic conditions and toxic reagents that in the end affect the clinical application of nanostructures, the generation and characterization of new metallic NS by biological systems is important either for basic as well as for applied research. In this general context, the search for new environmentally friendly and inexpensive methods for metal(loid)-containing NS generation has made biological systems desirable candidates for both in vivo and in vitro NS production, either using whole microorganisms or purified enzymes.

Isolation and Selection of Metal(loid)-Resistant Bacteria
Twenty-two samples were collected from two different Chilean regions from which bacterial isolates were obtained: (i) north (Blanca, Chaxa and Céjar lagoons, El Tatío geyser, Death Valley) and (ii) mid-south (Maule lagoon, El Teniente copper mine). A sample from Uyuni Salar, Bolivia, was also included in this study. In turn, isolates MF02 and MF05 were kindly provided by Dr. Juan Carlos Tantaléan, Universidad San Luis Gonzaga, Ica, Perú.

Growth, Identification, and Characterization of the Environmental Strains
Cells were grown in LB medium at 37 • C; E. coli BL21 carrying the pET 101/gorA vector was grown in ampicillin (0.1 mg/ml)-supplemented LB medium. This gorA-expressing plasmid was constructed as follows: the gorA gene was amplified from the environmental strain MF01 using primers CACCATGACTAAGCATTATGACTACATCGCA (Gforward) and ACGCATGGTGACAAATTCTTCG (Greverse). PCR products were inserted into the vector Champion TM pET101 Directional TOPO Expression (Invitrogen R ). Correct gene insertion was checked by PCR using primers pETForward (ATGCGTCCGGCGTAGAGG) and pETReverse (GCTAGTTATTGCTCAGCGGTGG). Their identity was confirmed by DNA sequencing. The expression of the cloned gene was induced with 1 mM IPTG for 16 h. GorA was purified by Ni-affinity chromatography (HisTrap HP, GE Healthcare).
Physiological characterization of the isolates was carried out using standard biochemical assays (API ZYM and API 20E; BioMérieux Inc.), which were conducted according to the manufacturer's instructions. Morphological analyses were initially done by Gram staining and in the case of selected strains, also by scanning electron microscopy (SEM) as described by Arenas et al. (2014a). Briefly, samples were visualized and analyzed by low voltage electron microscopy using a LVEM5 Benchtop equipment (Center for Bioinformatics and Molecular Simulation).
Bacterial identification was accomplished by sequencing the 16S rRNA gene using the universal primer 8F (forward) and Phylogenetic trees were constructed using the MEGA 6.06 program applying the neighbor-joining method (Saitou and Nei, 1987), while distances were calculated with bootstrapping (100) applying the Tamura-Nei method (Tamura et al., 2004). Bacterial identity was also assessed by analyzing the fatty acid composition at the DSMZ Institute (Braunschweig, Germany).
Determination of minimal inhibitory concentrations (MIC) was carried out using serial dilutions (1: 2) of sterile solutions of K 2 TeO 3 , AgNO 3 , HAuCl 4 , K 2 CrO 4 , CdCl 2 , NaAsO 2 , CuSO 4 and Na 2 SeO 3 in 1 ml of LB medium in 48-well plates. Subsequently, 10 µl of cultures grown in LB medium up to OD 600 ∼0.6 were added to each well and incubation proceeded with constant shaking at the optimal growth temperature of the particular isolate. MICs were determined after 24 h of incubation. For growth curve construction, overnight cultures were diluted 1:100 with fresh LB medium and incubated with shaking up to OD 600 ∼ 0.6. Then, 10 µL were added to 1 mL of fresh LB medium containing 4 µM K 2 TeO 3 , 15 µM AgNO 3 or HAuCl 4 . Bacterial growth was monitored at 600 nm every 30 min for 14 h in a TECAN Infinite M200 Pro multimode plate reader.

Determination of Enzymatic Activity
Metal(loid)-reducing activity was determined in a final volume of 200 µl which contained 50 mM Tris-HCl buffer pH 8.0 (or 9.0), 50 mM potassium phosphate pH 7.0, 1 mM NADH (or NADPH), 1 mM β-mercaptoethanol and the crude extract; metal(loid)s tested for reduction were TeO 2− 3 (1 mM), SeO 2− 3 (1 mM), AgNO 3 (0.2 mM) and HAuCl 4 (1 mM). Reactions were monitored in a TECAN Infinite M200 Pro multimode plate reader at the wavelength that the metal(loid) absorbs in its elemental state: 500 nm (Te; Pugin et al., 2014), 400 nm (Se; Song et al., 2017), 424 nm (Ag; Kumar et al., 2007), and 540 nm (Au; Correa-Llantén et al., 2013). The optimal buffer and best nicotinamide cofactor were determined for each crude extract; an enzyme unit (U) was defined as the amount of enzyme required to increase the absorbance by 0.001 units/min at the respective wavelength. Metal(loid)-reducing activity was also assessed by native polyacrylamide gel electrophoresis (native PAGE). Briefly, proteins in crude extracts were fractionated in 10% gels; after the run, activity was revealed by submerging the gel in the appropriate buffer containing the metal(loid) and a mixture of 1 mM NADH/NADPH as electron donor.

In vivo and in vitro Synthesis of Nanostructures
The isolates selected for synthesizing NS in vivo were grown to exponential phase (OD 600 ∼0.5) and treated with ¼ of the metal(loid) MIC (TeO 2− 3 , SeO 2− 3 , Ag + or AuCl − 4 ), incubated for 4 h and then centrifuged for 10 min at 9,000 g. The bacterial pellet was sent for thin sectioning and transmission electron microscopy (TEM) analysis (Advanced Microscopy Unit (AMU), at Pontificia Universidad Católica de Chile).
Formation of NS in vitro was carried out using 150 µg/ml of purified recombinant glutathione reductase (GorA) from E. cloacae (isolate MF01). Additionally, crude extracts that contained GorA overexpressed for 2 h were used with reduction buffer (50 mM potassium phosphate pH 7.0, 1 mM NADPH, 1 mM β-mercaptoethanol and 0.15 mM TeO 2− 3 or 1 mM SeO 2− 3 ). In addition, crude extracts (200 µg/ml of protein per reaction) from strains of interest were used for the production of NS by incubation with 1 mM Ag + , AuCl 4 , TeO 2− 3 or 10 mM SeO 2− 3 for 16 h in reduction buffer under optimal pH conditions and the preferred nicotinamide cofactor.

NS Characterization
A drop containing in vitro generated NS was placed on a copper grid and NS morphology was analyzed by TEM using a Hitachi Transmission Electron Microscope HT7700. Their chemical composition was determined through X-ray energy dispersion spectroscopy (EDS) using a SEM Zeiss EVO MA 10, EDS Penta FET Precision X-act Oxford Instruments. Both studies were conducted at the Center for the Development of Nanoscience and Nanotechnology-CEDENNA, USACH. In turn, the hydrodynamic diameter of the metallic nanostructures was assessed by dynamic light scattering (DLS) using a Marlvern Zetasizer Nano ZS equipment at room temperature (25 • C) as described by Arenas-Salinas et al. (2016). Final values were calculated based on three independent measurements of twenty repetitions. Furthermore, metal(loid)s were quantified using total reflection X-ray fluorescence spectrophotometry (TXRF). Briefly, in vitro-synthesized NS were centrifuged at 13,000 × g for 90 min and the sediment was suspended in 200 µl of 65% HNO 3 . Samples were heated at 60 • C ∼2 h and analyzed in a TXRF Bruker S2 PICOFOX Spectrometer at Bioinformatics and Gene Expression laboratory of the Institute of Nutrition and Food Technology (INTA, University of Chile).

NS Antibacterial Activity
A suspension of in vitro synthesized NS was used to challenge Escherichia coli and Listeria monocytogenes. The NS were dialyzed against 50 mM Tris-HCl buffer (pH 8.0 or 9.0) or 50 mM potassium phosphate (pH 7.0), accordingly to the buffer used to generate them. Dialysis was for 4 h at room temperature with constant shaking. The dialyzed material was maintained at 4 • C until further analysis. Concentrations of these metallic NS were calculated by determining the dry weight which was expressed in µg/ml. MIC determinations of the dialyzed NS and growth curves of E. coli BW25113 and L. monocytogenes were carried out as described in section Growth, Identification, and Characterization of the Environmental Strains.

Data Analysis
Plots and statistical analyses were carried out using the GraphPad Prism 6.0 (GraphPad Software, Inc.). Analysis of variance (ANOVA) and t-test were used considering p < 0.05. The statistical significance was indicated as follows: * , for values where p < 0.05, * * , for values where p < 0.01, * * * , for values where p < 0.001 and * * * * , for values where p < 0.000; ns, no significant difference.

Isolation, Identification, and Characterization of Metal(loid) Resistant Bacteria
A total of 47 bacterial strains isolated from environmental samples were assessed for metal(loid) resistance. Cells were routinely grown in LB or LB-agar plates at 37 • C and exposed to different concentrations of 19 different, defined metal(loid)s. None of them grew in Cd 2+ -, Al 3+ -, or Mn 2+containing LB medium nor in R2A, Acidiphilium, or ATB culture media. Table S1 shows the ability to grow in the presence of the indicated metal(loid)s; when reduced, some of them (e.g., Te, Se, Au, and Ag) showed a characteristic color that was monitored spectrophotometrically. In turn, while strain MF47 was the most sensitive to all metal(loid)s tested, strains MF45 and MF46 tolerated only Pb 2+ and Te 4+ , respectively.

Metal(loid) Resistance and Reduction by the Environmental Strains
Minimal inhibitory concentrations of K 2 TeO 3 , AgNO 3 , HAuCl 4 , K 2 CrO 4 , CdCl 2 , NaAsO 2 , CuSO 4 , and Na 2 SeO 3 were determined under aerobic growth conditions for the strains listed in Table S2. MF02 and MF04 were the most resistant and sensitive to tellurite, respectively. All strains exhibited similar resistance levels to HAuCl 4 , CdCl 2 , AgNO 3 , and CuSO 4 , while MF01 and MF03 were the most sensitive to NaAsO 2 . Differences up to 500-fold in the MIC of K 2 CrO 4 were observed, MF02 and MF08 tolerating the highest concentration (400 mM). Finally, while MF01 and MF02 grew in the presence of Na 2 SeO 3 up to 500 mM, MF10 was the most sensitive isolate (3.125 mM). Then, the effect of sublethal concentrations of TeO 2− 3 , AuCl − 4 and Ag + on bacterial growth was assessed (Figure 2). Although an extended lag phase was observed, cells regained growth between ∼4 and ∼7 h after Naphthol-AS-BI-phosphohydrolase  On the other hand, crude cell extracts were assayed to assess tellurium (IV)-, selenium (IV)-, gold (III)-, and silver (I)reducing activity in the presence of NADH or NADPH and in the pH range 7-9 (Figure 3 and Figure S2). The reduction of three metal(loid)s generated a change of the solution's color: black, purple and yellow-orange in the case of tellurite (Figure S2A), AuCl − 4 ( Figure S2B) and Ag + (Figure S2C), respectively. While MF09 was the best tellurium (IV) reducer (pH 8-9 with NADH as cofactor, Figure 3A), selenium (IV) was better reduced by MF02 at pH 7.0 using NADPH as cofactor ( Figure 3B). In turn, MF03 exhibited the best Ag (I)-reducing activity at pH 7.0 in the presence of NADH ( Figure 3C). Finally, a robust gold-reducing activity was observed in MF09 at pH 8.0 with NADH as the enzyme cofactor ( Figure 3D).
To look for proteins which could be responsible of metal(loid) reduction, tellurite-and gold-reducing activities were assessed in situ by polyacrylamide gel electrophoresis under non-denaturing conditions (Figures S3A,B). Reduction bands generated by MF01 extracts were excised from the gel and fractionated by SDS-PAGE ( Figure S3C). Twelve bands were identified by MALDI-TOF ( Figure S3D) which included the enzyme glutathione reductase (GorA), belonging to the flavoprotein family. The ability of GorA from the Antarctic strain Pseudomonas sp. BNF22 to reduce TeO 2− 3 had been observed previously in our laboratory (Pugin et al., 2014). However, its ability to reduce other metal(loid)s and/or its efficiency has not yet been determined, which prompted us to focus on this phenomenon. The gorA gene was amplified from the E. cloacae genome and cloned into the pET/101 expression vector to generate the pET/gorA recombinant plasmid (Figures S3E,F). A kinetic induction assay showed a ∼50 kDa protein band that accumulated over time ( Figure S3G). The enzyme was purified and assayed for tellurium (IV), selenium (IV), gold (III), silver (I), and copper (II) reduction, measured in the presence of NADH or NADPH and in the pH range 6-9. GorA reduced optimally TeO 2− 3 , SeO 2− 3 and Ag + at pH 8.0, 6-7 and 7, respectively ( Figure S3H).

Synthesis and Characterization of Nanostructures
Ultrathin sections of selected strains that were exposed to sublethal concentrations (¼ of the MIC) of defined metal(loid)s were analyzed by transmission electron microscopy (Figure 4). Intracellular, evenly distributed long electron-dense rods, representing most probably tellurium nanostructures (TeNS) were observed in tellurite-exposed MF09 (Figure 4A). In turn, SeNS generated by MF02 appeared as spherical particles located near the cell membrane ( Figure 4B). In both cases, alterations in size, morphology and cell division were observed (not shown). No silver-containing particles were generated by MF03 under the same conditions ( Figure 4C). Finally, small, circular and evenly distributed gold particles were seen when MF09 was treated with sub lethal gold concentrations ( Figure 4D). On the other hand, in vitro generation of NS by bacterial crude extracts lasted ∼16 h, irrespective of the strain or metal(loid) tested. NS morphology, size and chemical composition were determined by transmission electron microscopy (TEM), dynamic light scattering (DLS) and total reflection X-ray fluorescence spectrophotometry (TRXF), respectively. TeNS synthetized using MF09 extracts showed heterogeneous morphology with an average diameter ∼10 nm ( Figure 5A, left panel) and a hydrodynamic diameter ∼9.36 nm (polydispersity index PDI 0.446), in agreement with TEM results (Figure 5A, middle panel). The chemical composition was 23.2% tellurium, 55.8% carbon and low amounts of chlorine, potassium, and phosphorus ( Figure 5A, right panel). Moreover, TXRF analysis indicated that the tellurium concentration in TeNS was 78.66 ± 7.51 µg/ml. In the case of the SeNS generated with crude extracts from MF02, nanoparticles showed a spherical morphology with regular edges-nanospheres-and a size of ∼100 nm ( Figure 5B, middle panel); they showed a gaussian distribution (DLS) with a maximum at 105.1 nm (PDI 0.124) (Figure 5B, middle panel). Selenium content in SeNS was 83.9%, while TRXF showed that Se concentration was 158.98 ± 16,4 µg/ml ( Figure 5B, right panel). On the other hand, AgNS generated using crude extracts from MF03 showed a size of ∼10 nm, spherical-like shape with irregular edges and an electron-dense core ( Figure 5C, left panel). These AgNS also showed a gaussian distribution with a maximum centered at 68.46 nm (PDI 0.43) ( Figure 5B, middle panel), a size larger than that assessed by TEM; AgNS contained mostly carbon and to a lesser extent silver (9.84 ± 1.05 µg/ml, representing 20.7%) (Figure 5C, right panel). The same MF09 crude extract used to prepare TeNS was utilized to generate AuNS, whose morphology was not easy to determine because of the presence of organic material surrounding the particles (Figure 5D, left panel). Nevertheless, these NS were rather spherical with a size ∼50 nm. AuNS showed a size distribution with a maximum at 82.35 nm (Figure 5D, middle panel). These nanoparticles contained 21.2% gold and other elements in lower amounts such as calcium, magnesium, chlorine, sulfur, and phosphorus ( Figure 5A, right panel). TXRF analysis indicated that AuNS exhibited a gold concentration of 77.23 ± 12.61 µg/ml.
Finally, crude extracts from GorA-overproducing E. coli as well as purified GorA were used to synthesize in vitro SeNS and TeNS (Figure 6): (i) both, crude extracts and purified protein were able to generate spherical SeNS with a size of ∼50 nm and irregular edges (TEM). DLS analysis indicated that GorA-synthesized NS are prone to aggregation with a size distribution of 74.75 nm (PDI 0.159) ( Figure 6A); conversely NS obtained using crude extracts did not aggregate and showed a size of 39.09 nm (PDI 0.456) (Figure 6C). SeNS from crude extracts showed a higher amount of selenium (131.65 ± 16.46 µg/ml, representing 29.9%) than GorA-SeNS (164.93 ± 24.7 µg/ml, representing 26.6%) (Figures 6A,C); (ii) in turn, GorA-TeNS showed a rather stick-like morphology (Figure 6B), while nanoparticles synthetized using crude extracts exhibited irregular, non-homogenous morphology, with some of them showing triangular shapes ( Figure 6D). Size distribution (DLS) of GorA-and crude extract-TeNS was 35.11 nm (PDI 0.32) and 31 nm (PDI 0.63), respectively (Figures 6B,D). TeNS from crude extracts showed a higher amount of tellurium (127.36 ± 15.26 µg/ml, representing 10%) than GorA-TeNS (157.6 ± 25.3 µg/ml, representing 8.2%) (Figure 6B,D). Both crude extracts and purified protein showed the presence of other elements (more abundant in the GorA solution) such as potassium, sodium, sulfur, and phosphorus, among others.

NS Antibacterial Activity
The minimal inhibitory concentration of in vitro synthesized NS was determined and along with the construction of growth curves, were used to assess their putative antibacterial effects. Aerobically synthesized TeNS using MF09 crude extracts showed MICs of 45-and 66µg/ml for E. coli and L. monocytogenes, respectively. Similar MIC values (40 and 82 µg/ml, respectively) were observed for TeNS generated using GorA-overproducing E. coli crude extracts. In turn, AuNS MICs for E. coli and L. monocytogenes were 64-and 68µg/ml, respectively. At the tested concentrations, both SeNS and AgNS did not inhibit E. coli or L. monocytogenes growth. However, Te-and Au-containing NS inhibited completely the growth of E. coli and L. monocytogenes ( Figure S4).

DISCUSSION
Environmental bacteria survive in the presence of toxic agents such as metal(loid)s because they have evolved specific mechanism to cope with them (Summers and Silver, 1978;Bollag et al., 1994). Specifically, bacterial metal(loid)-reduction has gained attention among researchers since naturally reducingor genetically modified-bacteria are widely used in the field of bioremediation (Stephen and Macnaughtont, 1999;Das et al., 2016) and biotechnology to generate nano-scaled structures exhibiting biomedical, electronic and pharmacological applications, among others (Suresh, 2012).
In this line, environmental bacteria from different Chilean regions were isolated, identified and characterized. Such regions exhibit a combination of many extreme factors like high salinity, desiccation, high and low temperatures, volcanic intervention, etc., most of them responsible for generating oxidative stress in organisms. Since metal(loid)s are also able to induce oxidative stress (Nies, 1999;Imlay, 2003), it was inferred that those places from where the samples were taken could host metal(loid)-resistant bacteria. The 10 most resistant to-and able of metal(loid)s reduction bacteria were chosen for further analyses because of their potential biotechnological applicability.
Their resistance level to 8 metal(loid)s was evaluated under aerobic conditions (Table S2). In this situation, most of these toxicants exert -at least in part-toxicity because of ROS production (mainly superoxide), causing the inactivation of certain enzymes and metabolic pathways, modification of nucleic acids and lipid peroxidation of the cell membrane (Ahearn et al., 1995;Calderón et al., 2009;Contreras and Vásquez, 2010;Lemire et al., 2013). High levels of tellurite resistance (4 mM) were observed for some isolates, while tellurite MIC did not exceed 0.004 mM for sensitive bacteria such as E. coli (Taylor, 1999). In the case of chromate and selenite, resistance levels observed for some isolates were up to ∼500-(MF02 and MF08) and ∼160-fold (MF01 and MF02) higher than that of other isolates, respectively. Interestingly, phylogenetically related strains (MF01 and MF04, MF09 and MF05, MF07 and MF10) exhibited different levels of resistance, probably because of the different environmental conditions where they thrive. Growth curves also showed that the isolates are differentially affected by these toxicants (Figure 3).
When reduced to their elemental state, tellurite, selenite, auric tetrachloride and silver generate colored, insoluble NS ( Figure S2), which could serve as markers for putative biotechnological applications including medicine, electronics, pharmacy and engineering, among others (Ba et al., 2010;Suresh, 2012;Oves et al., 2013). Most strains exhibited metal(loid)reducing ability (Figure 3, Figure S2), whose optimal reduction condition -pH range and enzyme cofactor among others-was determined. MF09 showed maximal tellurite reduction at pH 8 and 9 using NADH as electron donor (Figure 3A). This could be explained because, in general, redox centers of proteins exhibiting tellurite reductase activity contain reactive vicinal cysteines that are very sensitive to pH (Arenas et al., 2014b). Deprotonation of thiol groups of these cysteines generates the thiolate anion (-S − , pKa ∼8.0) which is highly reactive (Vlamis-Gardikas, 2008). This high pKa implies that most cysteine thiols are protonated at pH 7.0 and hence, inactive.
Similar results were observed during AuCl − 4 reduction by MF09 at pH 8.0 in the presence of NADH (Figure 3D). In turn, optimal selenite and silver reduction by MF03 and MF02, respectively, occurred at pH 7.0. Particularly, while Se 0 is slowly oxidized to SeO 2− 4 in alkaline conditions (Kamal, 1994), SeO 2− 3 is reduced at more acidic pH values, thus favoring the formation elemental Se. On the other hand, pH influences metal(loid) speciation thus causing the formation of complexes and the deprotonation/protonation of functional groups that may participate in the catalytic process (Panda and Deepa, 2011). Also, pH can result in precipitation of defined ions (Atkins and Jones, 2006). For instance, Ag + precipitates as silver hydroxide in alkaline conditions and is spontaneously transformed into the more stable, insoluble, silver oxide (Ag 2 O) (Burriel et al., 2006).
Next, the in vivo generation of tellurium-, selenium-, silver-, and gold-containing NS was evaluated using three of the environmental strains under study (Figure 4). TeNS generated by MF09 exhibited an elongated morphology, a situation that has been previously reported in Rhodobacter capsulatus (Turner et al., 2011). On the other hand, MF02-generated SeNS showed spherical morphology and a size >100 nm ( Figure 4B). Actually, SeNS produced by most microorganisms exhibit spherical morphology and in some cases, transformation from spheres to nanowires do occur (Mane et al., 2015). In turn, MF03 did not form AgNS (Figure 4C), probably because Ag + interacts with-and precipitate with a large number of intra-or extracellular anions (thus decreasing its availability to form NS) (Atkins and Jones, 2006); such is the case when PO 3− 4 present in the culture medium form stable compounds such as Ag 3 PO 4 (Xiu et al., 2011). MF09-generated AuNS were observed as small intracellular deposits evenly distributed in the cell ( Figure 4D). It general, AuNS synthesis is directly dependent on the microorganism and pH of the medium. In this line, marine yeasts form large-sized AuNPs at acidic pH values, while it reduced at alkaline pHs; conversely, fungi belonging to the Verticillium genus form larger AuNPs at alkaline pH values (Dhillon et al., 2012).
It should be noted that the molecular basis of the in vivo metal(loid)-reducing activity is very hard to determine accurately since a large number of factors that are present in the cell context may affect and/or influence this activity; this makes almost impossible to correlate directly in vitro activity and the generation of metal(loid) deposits in vivo and variables such as culture medium, toxicant exposure time, temperature, oxygen availability, among others, should be explored further.
The ability of crude extracts to generate metal(loid)containing NS was used to characterize NS synthesis in vitro, including their morphology, size, composition and metal(loid)concentration ( Figure 5). All the formed structures exhibited sizes <100 nm and hence, fall in the definition of nanostructures, i.e., at least one dimension does not exceed 100 nm (Suresh, 2012). MF09 crude extracts formed TeNS that were smaller in size than AuNS (Figures 5A,D). An important factor that affects NS morphology and size is related to the formation of the NS itself, where NS nucleation and growth are limiting steps for these NS characteristics (Xiong and Lu, 2015). Both TeNS and AuNS contain a high proportion of the respective metal(loid), 22.3 and 21.2%, respectively, in addition to other elements such as carbon. In particular, TeNS exhibited small sizes and poorly defined morphologies. Unfortunately, the presence of organic material hampered the correct visualization of AuNS. This did not affect SeNS observation, which showed a rather spherical morphology with poorly defined edges, and contained as much as 83.9% Se (Figure 5B). This result is consistent with the high Se concentration determined by TXRF (158.98 ± 16.4 µg/ml). Different was the case of AgNS, which contained lower metal abundance ( Figure 5C) and is probably due to the presence of phosphate in the reaction buffer (see above).
Lastly, NS were also generated using purified GorA from E. cloacae (>92% pure) as well as crude extracts of a recombinant E. coli overexpressing the E. cloacae gorA gene (Figure 6). Given that it is a relatively new procedure, not much information is available in the literature. This flavoprotein, which was identified and characterized in this work, exhibits the ability to efficiently reduce SeO 2− 3 and TeO 2− 3 ( Figure S3H). TeNS synthesized using crude extracts showed a rather triangular shape, while those generated by the purified protein were slightly larger size, irregular and exhibited a more spherical morphology (Figures 6B,D). As mentioned, difference in size and morphology could be attributed to the influence of the cellular environment on the metal(loid)-reducing efficiency.
Intracellular tellurite reduction could occur also because the participation of reductants such as gluthatione (GSH) and other cytosolic thiols (painter-type reactions) whose reducing ability would promote Te 0 formation (Chasteen et al., 2009). Given that GorA is responsible for appropriate GSH levels, it is tempting to speculate that TeNS could be formed more efficiently when it is overproduced. This situation could explain why TeNS generated by crude extracts of GorA-overproducing E. coli are larger than those generated by the purified protein. No differences were observed regarding the Te content in TeNS. Actually, elemental analyses showed that Te was present in lower amount regarding other elements such as carbon, oxygen and phosphorus. Based on the stoichiometry of Te and O (oxygen percent is at least twice that of Te) in TeNS generated under aerobic conditions either by GorA or crude extracts, it could be inferred that in NS tellurium is present as tellurium dioxide (TeO 2 ). Nevertheless, additional experimental evidence is required to state it definitely. It has been observed lately that GorA-generated TeNS remain attached to the enzyme, probably through covalent bonding with the active site catalytic cysteine residues (Pugin et al., 2014). Unlike TeNS, SeNS generated using crude extracts of GorA-overproducing cells were smaller than those produced by purified GorA (Figures 6A,C). This could be explained by some kind of electron leak, thus making selenite reduction less efficient (Zare et al., 2013;Mane et al., 2015). However, Se concentration was about the same in SeNS synthesized in both conditions.
Given that antibiotic-resistant, pathogenic bacteria have increased almost exponentially worldwide, the development of tools from biotechnological origin for biomedical applications is mandatory (Yacoby and Benhar, 2008). In this work, the antibacterial activity of the in vitro-generated NS was tested against E. coli and L. monocytogenes. TeNS made by crude extracts of GorA-overproducing E. coli were the most toxic for E. coli and L. monocytogenes. Similar results were observed with MF09-generated AuNS and TeNS ( Figure S4). The effect of NS on E. coli and L. monocytogenes growth was also assessed by constructing growth curves. Results from Figure S4 show that in general all NS inhibited completely the bacterial growth.
Toxic effects of NS are generally related to the specific particle. Thus, AuNS have been widely used in therapeutic as well as diagnostic procedures, and exhibit antibacterial activity against Salmonella sp., Bacillus subtilis, E. coli and Pseudomonas aeruginosa (Das et al., 2009). In particular, chemically-generated AuNS seem to exert their toxicity in two ways: (i) changing membrane potential and inhibiting ATP synthase activity, which results in a general turn down of metabolism and (ii) inhibiting the binding of tRNAs to the ribosome, thus generating a global collapse of biological processes. Other NS are toxic because the release of metal ions, as in the case of some AgNS; in fact, Ag + release causes damage to the cell membrane, inactivates proteins and inhibits DNA replication (Chaloupka et al., 2010;Xiu et al., 2012).
Our results show that in general all tested NS were more toxic for E. coli as compared to L. monocytogenes, which, as a Gram positive organism, possess a cell wall that probably retards or prevents the entry of NS. In this context, no information on the mechanism of NS uptake is available in the literature. Unlike TeNS and AuNS, in vitro-synthesized SeNS and AgNS did not inhibit bacterial growth (not shown). Results with SeNS could be explained because selenium is an essential element for microorganisms (Lemire et al., 2013), and probably higher Se amounts in NS would be needed to generate toxicity. It has been also shown that SeNS inhibits both growth and proliferation of cancer cells in culture (Selenius et al., 2010). On the other hand and although AgNS have been reported as the most toxic NS (Rai et al., 2009;Lin et al., 2012), they did not exhibit toxicity for the tested bacteria.
Finally, it seems very interesting that the same enzyme can reduce two metalloids possessing different chemical characteristics, as for instance, their reactivity with certain enzymes (Rigobello et al., 2011). We trust that the results of this work will help to define the molecular basis governing the biological synthesis of many potentially useful nanostructures.

CONCLUSION
Ten bacteria exhibiting resistance to various metals and metalloids were isolated and characterized from environmental samples. Whole cells as well as crude extracts derived from them were successfully used for the biological synthesis of TeNS, SeNS, AuNS, and AgNS, which exhibited different, specific characteristics. In particular, E. cloacae was used as model to look for toxicant-reducing enzymes. In this context, it was found that purified E. cloacae GorA reduced efficiently TeO 2− 3 and SeO 2− 3 . Finally, especially interesting were TeNS and AuNS, which exhibited antibacterial properties and inhibited E. coli and L. monocytogenes growth.

ACKNOWLEDGMENTS
We would like to thank Natalia Valdes from the Universidad de Santiago de Chile, Facultad de Química y Biología for her support in bioinformatics analysis. Also Yerko Argandoña from the Universidad de Talca, for support in electron microscopy. In addition, to Dr. Rivas-Pardo and Mrs. Paulina Ramirez of Columbia University for his critical review of the manuscript. This paper is dedicated in memory of my daughter María Ignacia Arenas Monterey, our little angel.

SUPPLEMENTARY MATERIAL
The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fmicb. 2018.00959/full#supplementary-material    Figure S4 | Growth curves of E. coli and L. monocytogenes exposed to NS. Effect of TeNS synthesized by crude extracts of cells overexpressing the E. cloacae gorA gene in E. coli (A) and L. monocytogenes (B). Effect of TeNS synthesized using crude extracts of MF09 in E. coli (C) and L. monocytogenes (D). Effect of AuNS synthesized by crude extracts of MF09 in E. coli (E) and L. monocytogenes (F). Black and blue lines represent the growth of control and NS-treated cells, respectively.