Bioleaching and Electrochemical Behavior of Chalcopyrite by a Mixed Culture at Low Temperature

Low-temperature biohydrometallurgy is implicated in metal recovery in alpine mining areas, but bioleaching using microbial consortia at temperatures <10°C was scarcely discussed. To this end, a mixed culture was used for chalcopyrite bioleaching at 6°C. The mixed culture resulted in a higher copper leaching rate than the pure culture of Acidithiobacillus ferrivorans strain YL15. High-throughput sequencing technology showed that Acidithiobacillus spp. and Sulfobacillus spp. were the mixed culture’s major lineages. Cyclic voltammograms, potentiodynamic polarization and electrochemical impedance spectroscopy unveiled that the mixed culture enhanced the dissolution reactions, decreased the corrosion potential and increased the corrosion current, and lowered the charge transfer resistance and passivation layer impedance of the chalcopyrite electrode compared with the pure culture. This study revealed the mechanisms via which the mixed culture promoted the chalcopyrite bioleaching.


INTRODUCTION
Bioleaching as a low-cost biotechnology offers an alternative to traditional pyrometallurgical methods to extract valuable metals from sulfide minerals (Hedrich et al., 2016;Banerjee et al., 2017;Pathak et al., 2017;Hu et al., 2020;Srichandan et al., 2020). Studies on bioleaching have been extensively performed using mesophilic, moderately thermophilic and extremely thermophilic acidophiles (Gu et al., 2013;Acosta et al., 2014;Li et al., 2018;Ai et al., 2019). On the contrary, bioleaching at low temperatures was only discussed in limited documents. Microbial oxidation of sulfide minerals could occur at relatively low temperatures Tuovinen, 1991, 1992;Elberling et al., 2000). It was observed that the microbially mediated dissolution of sulfide minerals could reach 30% of the maximal value at 21 • C (Langdahl and Ingvorsen, 1997). Acidithiobacillus ferrivorans is a well-known cold-adapted acidophile that can use iron and sulfur as a sole energy source (Kupka et al., 2007(Kupka et al., , 2009Hallberg et al., 2010). Studies using At. ferrivorans in bioleaching of sulfide minerals at low temperatures have been performed. The leaching rate of chalcopyrite at 4 • C using At. ferrivorans was higher than using the mesophilic At. ferrooxidans . It was found that S 0 formed during chalcopyrite bioleaching and the content of S 0 increased until dissolution ceased, suggesting S 0 passivation (Liljeqvist et al., 2013;Zeng et al., 2020).
One of the topics of interest is using mixed cultures in the bioleaching of sulfide minerals. It has been shown that using mixed cultures resulted in a higher metal extraction rate than using pure cultures (Akcil et al., 2007;Liu et al., 2011;Panda et al., 2015). On mesophilic and/or moderate thermophilic conditions, Acidithiobacillus spp., Leptospirillum spp., Sulfobacillus spp., and Ferroplasma spp. were frequently detected in mixed cultures (Panda et al., 2013;Donati et al., 2016;Ma et al., 2018). These microorganisms played different roles (e.g., iron or sulfur oxidation, utilization of inorganic or organic substances) in a leaching system (Latorre et al., 2016). Meanwhile, they interacted with each other. For instance, L. ferriphilum enhanced the adhesion of Sb. thermosulfidooxidans to pyrite (Li et al., 2020). On the contrary, bioleaching using mixed cultures at low temperatures was scarcely studied. Liljeqvist et al. (2013) used a T7 mixed culture and a pure culture of At. ferrivorans strain SS3 in chalcopyrite bioleaching at 6 • C. Bacterial community analysis revealed that At. ferrivorans dominated the T7 mixed culture . Halinen et al. (2009) found that during bioleaching of a low-grade, multi-metal black schist at 7 • C, some Acidithiobacillus spp. were present in the initial stage; after 500 days, At. ferrooxidans, Ferromicrobium acidophilum-like species and a gram-positive bacterium were detected.
Bioleaching of sulfide minerals is an electrochemical process in essence, which oxidized metal sulfide to Fe(III), sulfur and sulfate as well as other inorganic sulfur compounds, involving the transfer of electrons. Due to the difficulties in determining the intermediate products, the chemical processes of bioleaching are often hard to describe. Electrochemical approaches can convert the change of chemical substances to electrochemical signals, which can be captured by specific electrochemical equipments. Therefore, electrochemical methods have been commonly applied to investigate the dissolution processes of sulfide minerals. Arena et al. (2016) used electrochemical impedance spectroscopy (EIS) to study chalcopyrite leaching, and found that the addition of bacteria reduced the charge transfer reaction resistance. Zhao et al. (2015) compared the cyclic voltammograms (CV) of chalcopyrite and bornite electrodes. It was found that the anodic and cathodic peaks of the two mineral electrodes appeared in close positions, suggesting that similar oxidation and reduction reactions occurred during the dissolution of these two types of minerals.
Low-temperature bioleaching is critical in the recovery of valuable metals from sulfide minerals in alpine regions. Using microbial consortia instead of pure cultures can be a feasible approach to promote the leaching rate at low temperatures. To this end, chalcopyrite bioleaching by a mixed culture was performed in the present work. CV measurement, potentiodynamic polarization and EIS were used to characterize the dissolution processes and electrochemical behaviors of chalcopyrite. The study would provide insights into the chalcopyrite bioleaching mechanisms by mixed cultures at low temperatures.

Mineral
Chalcopyrite sample was obtained from Guangzhou in Guangdong province of China. XRD analysis showed that the sample contained 97.83% chalcopyrite and 2.17% quartz. The sample consisted of 33.1% copper, 28.7% iron, and 35.4% sulfur. Sample was ground and sieved to obtain fractional sizes ≤75 µm and sterilized by UV irradiation for 24 h in an aseptic room.

Cultures
The microbial consortium used in the present study was enriched from the acid mine drainage of Yulong copper mine. Water samples were collected from five different sites in Yulong copper mine (an acidic mine drainage pond, an acidic tailing pool, two tailing dumps, and an effusion pool). All samples were combined and then cultivated in ironfree 9K medium (Peng et al., 2019) using chalcopyrite (at a pulp density of 3%) as a sole energy source at 6 • C. After 4 months, apparent bacterial growth was observed and this was designated as the mixed culture. The obtained mixed culture was subcultured every 2 months and used as a seed in our lab for chalcopyrite bioleaching at low temperatures. At. ferrivorans strain YL15 was isolated from the acid mine drainage pond (Peng et al., 2017). The strain was routinely cultivated in ironfree 9K medium with chalcopyrite as a sole energy source at 6 • C.

Bioleaching Experiments
Bioleaching of chalcopyrite was conducted in 500 mL shake flasks. Chalcopyrite at a pulp density of 3% and ironfree 9K medium (250 mL) were added to each flask. The mixed culture or the pure culture of the strain YL15 was centrifuged at 10,000 × g for 10 min at 4 • C to harvest cells. The collected cells were washed using aseptic acidified water (pH2.0) for twice and then resuspended with 10 mL 9K medium. Bioleaching using the cells of the mixed culture (designated as group MHJ) and the strain YL15 was, respectively, performed. The initial cell density was approximately 2 × 10 7 cells/mL. The flasks were operated at 160 rpm and 6 • C. An abiotic control was also conducted. Thymol in ethanol (2%, v/v) was added to the abiotic control to inhibit bacterial contamination. All the bioleaching experiments were carried out in triplicate.
Samples were withdrawn from flasks at regular intervals to determine the oxidation reduction potential (ORP), pH, cell density and metal ions concentrations. Every time 1.5 ml of the leaching solution was withdrawn to a sterile tube. The solution was centrifuged at 2,000 × g to let the ore residue settle down. The supernatant was withdrawn for the determination of various parameters. An equal volume of iron-free 9K medium was added to the tube, resuspend the ore residue, and returned to the leaching solution. Concentrations of iron and copper were measured using the method as described previously (Peng et al., 2019). Cells were counted using a blood cell counting chamber under a CX31 optical microscope (Olympus, Tokyo, Japan). The pH value was measured with pHS-3E acid meter (LEICI, Shanghai, China) and ORP (Ag/AgCl) value was assayed against a platinum electrode. XRD analysis of ore residue was performed according to a previous study (Peng et al., 2019).

Sequencing of Prokaryotic 16S rRNA Gene Sequences
Bioleaching samples of the group MHJ were withdrawn at different time points. Sessile cells were detached from the mineral surface by vigorous vortex for 10 min in the presence of 1 gram of glass beads. The obtained samples contained both free and detached cells and were centrifuged at 2,500 × g for 5 min to remove the ore residues. The obtained supernatants were centrifuged at 10,000 × g, 4 • C for 10 min to collect the total cells. Genomic DNA was extracted as previously described (Wu et al., 2019). The integrity of DNA was checked on an agarose gel by ethidium bromide staining. The concentration of DNA was measured using a ND-1000 spectrophotometer (NanoDrop Technologies, Wilmington, DE, United States).
Detailed procedures for amplification and sequencing of prokaryotic V4 hypervariable region of 16S rRNA gene have been described in a previous document (Xiao et al., 2015). Briefly, sequences of the V4 region of the prokaryotic 16S rRNA gene were amplified using the universal primers 515F and 806R (Rinke et al., 2014) linked with barcodes, adapter, a pad and a linker of two bases. The purified PCR products were employed for library construction. The MiSeq 500 kit was used for sequencing (2 × 250 bp paired-ends) on the MiSeq sequencing platform (Illumina, San Diego, CA, United States).
Raw sequences were split into samples based on their barcodes. The raw sequencing data were deposited at Sequence Read Archive under the accession number SRP133342. After sequence trimming, reads assembly and chimeras sequences checking, operational taxonomic unit (OTU) clustering was performed using UPARSE at a 97% similarity level. After that, the taxonomic affiliation of each sequence was analyzed using RDP Classifier against the SILVA 16S rRNA database at a 70% threshold (Leng et al., 2016).

Electrochemical Experiments
Chalcopyrite electrode was prepared by cutting the chalcopyrite sample into an approximately cubic shape. All the electrochemical experiments were performed using 50 mL ironfree 9K medium as the electrolyte and a three-electrode system in the absence of bacteria or in the presence of the mixed culture or the pure culture of strain YL15. The three-electrode system contained a chalcopyrite electrode (working electrode, effective working area ∼1 cm 2 ), a graphite electrode (counter electrode), and a Ag/AgCl electrode (reference electrode). The chalcopyrite electrode was embedded in a special electrode sleeve and polished using 3,000 mesh emery cloth before the tests. Three uniform chalcopyrite electrodes were, respectively, immersed in the leaching solutions of different groups and then withdrawn at day 20 for the electrochemical tests. Electrochemical measurements were performed at 6 • C using a VersaSTAT platform equipped with Model273A potentiostat/galvanostat (EG&G Princeton Applied Research, Oak Ridge, TN, United States) controlled by the Power-Suite program. CV tests were performed at a scan rate of 20 mV/s. The scan range of CV was -800 to +800 mV (vs. open circuit potential, OCP). For potentiodynamic polarization tests, the electrode potential varied from -250 to +600 mV (vs. OCP) at a sweep rate of 2 mV/s. EIS tests were carried out in a frequency range of 10 −1 -10 −5 Hz. EIS data were fitted using the Zview software (version 2.0). All potential values in the present work were against the Ag/AgCl reference electrode.

Bioleaching Experiments
The mixed culture (group MHJ) and the pure culture of At. ferrivorans strain YL15 obtained in our lab were used for bioleaching of chalcopyrite at 6 • C. The bacterial growth during bioleaching is shown in Figure 1A. The bacterial cells of the group MHJ entered the logarithmic phase on day 12, and on day 16 for YL15. The highest cell densities of MHJ and YL15 were 2.2 × 10 8 and 1.9 × 10 8 cells /mL, respectively. The variation of pH during bioleaching is shown in Figure 1B. During the early phase, 9.2 M H 2 SO 4 was added to the leaching solution to maintain the pH at ∼2.5. The pH value in the group MHJ began to decrease on day 12 and achieved ∼2.0 on day 24. The trend of pH during bioleaching by the strain YL15 was similar to the group MHJ, but the process was postponed, and the value was higher than in the group MHJ (decreased to ∼2.1).
The variation of the ORP value is shown in Figure 2A. The ORP value was low in the early stage, but after that, it rocketed up to ∼600 mV in both groups. The value of ORP is mainly controlled by the ratio of Fe(III) to Fe(II). Variations of Fe(III) and Fe(II) concentrations are shown in Figure 2B. The ratio of Fe(III) to Fe(II) was low in the early stage. After that, as microbial oxidation of ferrous iron accelerated, the concentration of Fe(III) increased, accompanied by a decrease in the concentration of Fe(II). This was in accordance with the low ORP value in the early stage and its rapid rise after that (Figure 2A). The ore residues were analyzed using XRD. The results showed that all the ore residues contained only chalcopyrite and quartz, and no iron precipitate such as jarosite was detected. Variation of copper concentration is shown in Figure 3. The copper concentration in the presence of bacteria was higher than that in the abiotic control (Figure 3), suggesting that microorganisms greatly enhanced the dissolution of chalcopyrite. The copper concentration increased significantly after day 12 and reached the highest value on day 44 (11.2%) in MHJ and on day 48 (10.3%) in the YL15-mediated leaching system, respectively. Recently, bioleaching of another chalcopyrite sample using the strain YL15 at 6 • C was performed, and the highest copper leaching rate achieved was 19.3% (on day 80) (Zeng et al., 2020). It suggested that the difference in the mineral sample might result in significant contrast in the highest leaching rate and the leaching course. The results of the present study suggested that the mixed culture was more efficient in chalcopyrite bioleaching than the pure culture. Previously, a T7 mixed culture was used to leach a chalcopyrite concentrate, and 16% of the copper was recovered in a 62-day course (Liljeqvist et al., 2013). However, the T7 mixed culture had comparable leaching performance to the At. ferrivorans strain SS3. This might be due to that the T7 mixed culture was dominated by At. ferrivorans, while the relative abundance of other species was very low .

Microbial Community Dynamics of the Group MHJ
The microbial community of the group MHJ was monitored using high-throughput sequencing of the 16S rRNA gene. Samples were withdrawn on days 20, 30, and 50 (designated as MHJ1, MHJ2, and MHJ3). A total of 673,782 pair-end reads were obtained. Rarefaction curves of all samples based on sequencing reads and number of OTUs reached plateaus, indicating that the sequencing depth was appropriate for estimating the microbial diversity.
At the phylum level, Proteobacteria was the dominant lineage, which accounted for 81.5-94.9% of the total biomass, followed by Firmicutes (5.04-18.39%). Other phyla were also detected, e.g., Cyanobacteria, Thaumarchaeota and Bacteroidetes, but they were at extremely low level (<1%) (Figure 4A). Down to the genus level, a total of 27, 35, and 31 OTUs were detected for MHJ1, MHJ2, and MHJ3, respectively, and 20 OTUs were shared by all samples. Acidithiobacillus dominated the microbial communities, accounted for 94.8, 87.0, and 81.1% in MHJ1, MHJ2, and MHJ3, respectively. Sequences of Sulfobacillus (affiliated to Firmicutes) were detected at a considerable level and increased from 5.04% on day 20 to ∼10% on day 50.
To find out the affiliations of these two lineages, the 16S rRNA gene of sample MHJ3 was amplified using primers 27F and 1492R. The products were transformed to E. coli DH5α to build a clone library as described in a previous document (Liu et al., 2010). Five clones were randomly selected, and only 2 OTUs were detected, one of which was 100% identical to the 16S rRNA gene sequence of strain YL15 (accession number: KY352776.2) and the other one had a 98% identity to an undescribed Sulfobacillus sp. The results implied that the Acidithiobacillus spp. should be At. ferrivorans. The content of Acidithiobacillus decreased and the relative abundance of Sulfobacillus increased as bioleaching continued. This may be due to that the accumulation of organic substances was beneficial to the growth of Sulfobacillus  or that the gram-positive Sulfobacillus might be more resistant to the adverse environment in the late phase than the gram-negative At. ferrivorans (e.g., accumulation of heavy metal ions). Sulfobacillus is commonly considered as a moderate thermophile, although some species can grow at temperatures <20 • C (Melamud et al., 2003). Furthermore, it was documented that a mixed culture was enriched at 5 • C with ferrous sulfate as a sole energy and sequences close to Sb. montserratensis were detected at an abundance >10% (Escobar et al., 2010). These results indicated that there might be novel Sulfobacillus species existing in the low-temperature bioleaching culture.
There were also other genera in the mixed culture, for instance, Stenotrophomonas spp., Pseudomonas spp. and Castellanilla spp., but they were of extremely low abundance (<0.5%) (Figure 4B). These species have been identified in either bioleaching systems or other acidic metal-containing environments. For instance, Castellanilla was the dominant lineage in an ethanol-stimulated acidic nitrate-and uraniumcontaminated aquifer (Spain et al., 2007). In the low-grade copper sulfide bioleaching systems containing acid-processed rice straw (ARW), Stenotrophomonas accounted for >50% of the microbial community (Yin et al., 2019). Pseudomonas was detected in the bioleaching residues from a column bioreactor (Hao et al., 2016). These microorganisms can utilize organic substances as the energy source, and species like Pseudomonas could also secret organic acids such as citric acid, oxalic acid and succinic acid to enhance the dissolution of sulfide minerals (Hao et al., 2016).
Previous work has emphasized the importance of interactions between physiologically distinct acidophilic microorganisms (e.g., autotrophs and heterotrophs) in enhancing sulfide minerals dissolution (Okibe and Johnson, 2004). The existence of heterotrophs (such as Sulfobacillus, Stenotrophomonas, and Pseudomonas) could alleviate the inhibition of organic substances to the autotrophic At. ferrivorans and maintained the robustness of the microbial community (Johnson, 2008). In addition, Sulfobacillus can use inorganic sulfur compounds as a sole energy. Sulfur oxidation activity is essential in a bioleaching system. Firstly, it offers a low-pH condition for the dissolution of sulfide minerals. Secondly, elemental sulfur formed during the leaching process and precipitated on the mineral surface and had passivating effects on chalcopyrite bioleaching (Liljeqvist et al., 2013). Sulfur oxidation activity of the mixed culture was tested at an initial pH of 2.5. The sulfate concentration was measured using the barium sulfate turbidimetry (Liu et al., 2013). It was shown that the mixed culture had a higher sulfur-oxidation activity than the pure culture of strain YL15 (Supplementary Figure 1). Therefore, Sulfobacillus might help to reduce the passivating effect of sulfur during chalcopyrite leaching.

CV Studies
The cyclic voltammetry curves of chalcopyrite at 6 • C are shown in Figure 5. The cyclic voltammetry curves of the three groups were similar. There were four anodic peaks (A1, A2, A3, and A4) and two cathodic peaks (C1 and C2). Peak A3 was a common anodic peak of chalcopyrite electrochemical behavior, which was mentioned as the "leading peak." As shown in Eqs. 1, 2, there was a selective release of iron from the chalcopyrite crystal lattice and formation of intermediate nonstoichiometric chalcopyrite [Cu 1−x Fe 1−y S 2−z (y > x)] and covellite (Gómez et al., 1996;Zeng et al., 2011;Gu et al., 2013).
At more positive potential, peak A4 was a typical oxidation peak of chalcopyrite dissolution. It could be attributed to the oxidation of ferrous iron (López-Juárez et al., 2006) (Eq. 3).
In the reverse potential scanning, there was a peak C1 at ∼ −370 mV. It has been documented that this peak was involved in the reduction of covellite and chalcopyrite (Biegler and Horne, 1985;Arce and González, 2002) (Eqs. 4, 5): Peak C2 occurred at potential <−600 mV. According to Velásquez et al. (2001), this peak could be attributed to the reduction of chalcocite (Eq. 6): During the later reverse scanning, a weak peak A1 occurred. The peak was not frequently reported during the dissolution of chalcopyrite. It might be responsible for the oxidation of copper (Eq. 7) or chalcocite (Zeng et al., 2013) (Eq. 8). 2Cu Cu 2 S → Cu 1.92 S + 0.08Cu At more positive potential, there was a Peak A2 at 270-320 mV. It was reported that this peak might be involved in the oxidation of Cu x S (1 < x < 2) species such as djurleite and geerite (Arce and González, 2002) (Eqs. 9, 10), which are the intermediate products of many copper sulfides.
Cu 1.92 S → Cu 1.6 S + 0.32Cu 2+ + 0.64e − (9) Cu 1.6 S → CuS + 0.60Cu 2+ + 1.20e − It can be seen from Figure 5 that the dissolution process of chalcopyrite with or without bacteria or in the presence of pure or mixed culture were similar. However, in the presence of bacteria, the current intensities of all the anodic and cathodic peaks were higher than the abiotic control, especially for the peaks A4, C1, and C2. It indicated that the addition of bacteria is beneficial to the dissolution of chalcopyrite. Moreover, the intensities of the anodic peaks A2, A3, and A4, and cathodic peaks C1 and C2 in the presence of the mixed culture were higher than those in the presence of pure culture. The enhancement of these peaks implied that the mixed culture increased the dissolution reaction rates of chalcopyrite compared with the pure culture of strain YL15. A further comparison revealed peak shifts on the CV spectra. The peak A4 of the abiotic control was located at ∼715 mV, but shifted to ∼700 mV of the pure-culture group, and ∼675 mV of the mixed-culture group; The peak A2 shifted from ∼315 mV (YL15) to ∼275 mV (MHJ); The peak A3 of the pure-culture group occurred at ∼445 mV, and showed a shift to ∼420 mV of the mixed-culture group. These demonstrated that the dissolution reactions occurred more easily in the presence of bacteria, especially the mixed culture.

Potentiodynamic Polarization Studies
Results of potentiodynamic polarization tests in the absence of bacteria or in the presence of At. ferrivorans YL15/mixed culture at 6 • C are shown in Figure 6 and Table 1. While the I corr values of groups inoculated with bacteria increased compared with the abiotic control, their E corr values decreased. The results suggested that the corrosion rates increased after adding bacteria. This was consistent with the results of leaching rates in different groups (Figure 3), and it further demonstrated that bacteria could enhance the dissolution of chalcopyrite. The mixed culture had advantages over the pure culture of strain YL15. The E corr value of the group inoculated with the strain YL15 was 121.4 mV, but decreased to 116.3 mV of the group inoculated with the mixed culture. The I corr value increased from 1.49 µA/cm 2 of the pureculture group to 1.62 µA/cm 2 of the mixed-culture group. This  implied that the mixed culture promoted the transfer of electrons, thus accelerated the corrosion of chalcopyrite.

EIS Studies
The results of EIS in different systems are shown in Figure 7.
The shapes of different EIS spectra were similar, so the addition of bacteria did not change the control steps of chalcopyrite dissolution. Each group showed an arc in the high-frequency region. This arc should be assigned to the resistance encountered during charge transfer. There was another arc in the lowfrequency region, and this arc could be attributed to the impedance caused by passivation. The EIS data were fitted to an analog circuit with a linear combination of resistors and capacitors. The equivalent circuit of the impedance data in the present study should be R S (R 1 CPE1) (R 2 CPE2), where R S was the solution resistance, R 1 was the charge exchange impedance, and R 2 represented the impedance derived from the passivation layer. The constant phase elements CPE1 and CPE2 were connected with the capacitance of the electrode interface (Zeng et al., 2020). The detailed information on the fitting results using the analog circuit R S (R 1 CPE1) (R 2 CPE2) is shown in Table 2. The total impedance of different tests was MHJ < YL15 < abiotic control, which suggested that microorganisms decreased the impedance during chalcopyrite dissolution. Among the three types of impedances, R 1 accounted for more than 50% of the total resistance, followed by R 2 (took up 14-34% of the total resistance). This implied that the chalcopyrite dissolution process was mainly controlled by the charge transfer.  As shown in Table 2, the solution resistance in different tests was constant, whereas the charge exchange resistance and passivation layer impedance varied a lot among different groups. The charge exchange resistance of the abiotic control was 606.6 , but decreased to 486.3 in the presence of the strain YL15, and 227.4 in the presence of the mixed culture. The passivation layer impedance exhibited a different trend. The impedance of the abiotic control was lower than the other two groups. This was due to that chalcopyrite in the abiotic control was least leached, and relatively low content of passivation substance was produced. Compared with the group inoculated with strain YL15, the R 2 value of the group MHJ decreased, indicating less passivation on the mineral surface. S 0 passivation during chalcopyrite bioleaching at low temperature has been shown (Liljeqvist et al., 2013). The mixed culture could promote the sulfur-oxidation activity (Supplementary Figure 1), and thus it might help reduce the passivation caused by elemental sulfur. Although iron precipitates such as jarosite may not passivate the mineral surface (Peng et al., 2019), the attenuation of the passivation in the group MHJ might also be due to the continued dissolution of copper sulfide intermediates. Taken together, the results of EIS demonstrated that the addition of bacteria, especially the mixed culture, could decrease the impedance of the leaching system and thus accelerated the dissolution of chalcopyrite.

CONCLUSION
A mixed culture was used in chalcopyrite bioleaching at low temperature. The mixed culture was dominated by Acidithiobacillus spp. and Sulfobacillus spp., and it showed a greater leaching efficiency than the pure culture of the At. ferrivorans strain YL15. Electrochemical studies revealed that the mixed culture enhanced the dissolution reactions, decreased the corrosion potential while increasing the corrosion current, and reduced the impedance of the chalcopyrite electrode compared with the pure culture. This study provided insights into the mechanisms through which the mixed culture enhanced the chalcopyrite bioleaching.

DATA AVAILABILITY STATEMENT
The datasets presented in this study can be found in online repositories. The names of the repository/repositories and accession number(s) can be found below: https://www.ncbi.nlm. nih.gov/, SRP133342.

AUTHOR CONTRIBUTIONS
TP, WZ, and XW contributed conception and design of the work. TP, WL, JW, JM, and YP did the experiments. TP and WL drew the illustrations. TP, WL, XW, and WZ wrote the first draft of the manuscript. GQ and GG revised the manuscript. All authors read and approved the submitted version.