Cytotoxic, Antimitotic, DNA Binding, Photocatalytic, H2O2 Sensing, and Antioxidant Properties of Biofabricated Silver Nanoparticles Using Leaf Extract of Bryophyllum pinnatum (Lam.) Oken

Bryophyllum pinnatum is a perennial herb traditionally used in ethnomedicine. In the present report, silver nanoparticles (AgNPs) were synthesized using B. pinnatum leaf extract. BP-AgNPs were confirmed following UV-Vis spectroscopy with SPR peak at 412 nm and further characterized by FTIR, XRD, SEM-EDX, and TEM. Microscopic images confirmed the spherical shape and ~15 nm average size of nanostructures. BP-AgNPs were evaluated for photocatalytic degradation of hazardous dyes (methylene blue and Rhodamine-B) and showed their complete reduction within 100 and 110 min., respectively. BP-AgNPs have emerged as a unique SPR-based novel sensor for the detection of H2O2, which may deliver exciting prospects in clinical and industrial areas. DPPH and ABTS free radical scavenging activity were studied with respective IC50 values of 89 and 259 μg/mL. A strong intercalating interaction of CT-DNA with BP-AgNPs was investigated. Observed chromosomal abnormalities confirm the antimitotic potential of BP-AgNPs in the meristematic root tip. The cytotoxicity of BP-AgNPs against B16F10 (melanoma cell line) and A431 (squamous cell carcinoma cell line), was assessed with respective IC50 values of 59.5 and 96.61 μg/ml after 24 h of treatment. The presented green synthetic approach provides a novel and new door for environmental, industrial, and biomedical applications.


INTRODUCTION
The distinctive features of metal nanoparticles (NPs) have made it attractive to various applications such as optical, electronic, magnetic, and antimicrobial for the last few years. (Punjabi et al., 2018;Arun et al., 2019;Guilger-Casagrande and de Lima, 2019;de Oca-Vásquez et al., 2020). NPs are usually synthesized with distinct physical, chemical, and biological methods, but are inconvenienced by their cost, slow process as well as generation of waste causing environmental pollution and biotic harmfulness (Wang et al., 2016;Unni et al., 2017;Gahlawat and Choudhury, 2019;Hamida et al., 2020;Tortella et al., 2020). The physical methods utilize costly equipments and produce unstable larger nanoparticles, while hydrazine and sodium borohydride like hazardous materials are used as reducing agents in the chemical approaches (Mohanta et al., 2017;Chandraker et al., 2019a). Likewise, cautious isolation of bacteria, fungi, and the management of their noncontaminated culture or their byproducts are tedious issues with the microbial synthesis of NPs (Chandraker et al., 2019b).
Green synthesis using plant extracts is a blameless, facile, rapid, reliable, cost-effective, and eco-friendly approach that gives higher stability and better physicochemical characteristics to NPs (Ravi et al., 2013;Kumari et al., 2020). The phytochemicals and secondary metabolites found in plant extracts act as capping agent, and responsible for the reduction of metal ions and formation of NPs. Green synthesized metal/metal oxide NPs like CuO, FeO, and MgO are being utilized enormously in biomedical and clinical applications (Kumari et al., 2018;Sheel et al., 2020;Verma et al., 2020). Instead, AgNPs are preferred over other noble metal NPs like Au, Pt, Pd, Cu, Fe, etc., due to their extensive uses in bioengineering, cosmetics, food packaging, catalysis, electrochemistry, environmental remediation, and pharmaceutical industries as antiseptic agents (Paul et al., 2018;Mohan et al., 2020;Yousaf et al., 2020). Phytochemicals present in the plant extract are capable of capping and reducing Ag + to Ag 0 (Das et al., 2020). It is, therefore, suitable for large scale fabrication of AgNPs in non-aseptic environments.
The leading mortality rate for cancer is predicted to reach up to 21 million worldwide over the next decade (Siegel et al., 2016). Chemotherapy is a prominent approach of treatment which includes numerous cytotoxic drugs to arrest cancer cells, however, these drugs also harm normal body cells and causes adverse physiological effects (Iqbal et al., 2017). The antagonistic effects can be reduced by using metallic NPs in controlled targeted drug delivery, without affecting the normal cells. The AgNPs are playing an important role in the quality enhancement of anti-cancer drugs with maximum therapeutic effects (Lohcharoenkal et al., 2014;Verma et al., 2019). The cytotoxic agents may interact with the DNA of target cells and disrupt the mitosis and cell cycle. To explore the intracellular action of NPs, studies on their binding with DNA have become a primary interest in recent years (Ribeiro et al., 2018). Apart from some complicated techniques like gel electrophoresis and other electrochemical detection, UV-vis spectroscopy has been established as a convenient, accurate and extremely sensitive mode to illustrate the interaction of NPs with nucleic acids (Komal and Kaushik, 2019).
Removal of water pollutants is a serious concern of researchers worldwide (Yang et al., 2017). Synthetic dyes are one of the chief pollutants as well as hazardous and carcinogenic substances which are processed and released from the paint, fabrics, rubber, leather, paper, cosmetics, and plastic industries. Their catalytic degradation has received widespread attention because of being quick, extremely efficient (as compared to other approaches), and cost-effective approach, which does not trigger secondary contamination.
Hydrogen peroxide (H 2 O 2 ) is a strong oxidizer, frequently used in various manufacturing and food processing industries. Despite, its exposure in industrial processes results in various human health risks and environmental issues because of having toxic effects (Tagad et al., 2013). As per US-EPA, it is detrimental to human and aquatic bodies above permissible limit of 30 PPM in potable water (Bhagyaraj and Krupa, 2020). Therefore, a sensitive, accurate and easy detection method for H 2 O 2 contaminants is highly required.
Bryophyllum pinnatum (Lam.) Oken (family: Crassulaceae) is a perennial herb extensively grown in India, China, Tropical African and American countries, and Australia, and used widely in ethnomedicine. The natural succulent leaves of the plant have a range of therapeutic properties, including antibacterial, hypotensive, gastroprotective, immunomodulator, antidiabetic, anti-inflammatory, and anti-leishmania (Chibli et al., 2014). The plant often reported treating insect bites, kidney stones, boils, burns, gastric ulcers, sores, and eye infections, etc. (Fernandes et al., 2019). In this work, we aimed to synthesize AgNPs using leaf extract of B. pinnatum and explore their potential for photocatalytic, DNA binding, H 2 O 2 sensing, free radical scavenging, antimitotic and cytotoxic activities.

Materials
The leaves of B. pinnatum were collected during January 2019 near the Kapil Dhara fall of the Amarkantak region under the Anuppur district of Madhya Pradesh, India. Plant species authentication was carried out by the subject experts, and the voucher specimen (DOB/19/BP/044) was deposited in the herbarium of Botany department, IGNTU, Amarkantak, India.

Preparation of Leaf Extract
The collected fresh leaves were washed thoroughly twice with double distilled water (DDW) to eliminate dust and natural impurities. The B. pinnatum leaf extract (BPLE) was made with 25 g of fresh leaves, which were cut into equal size. The sliced leaves were boiled in 100 mL of DDW for 20 min at 65 • C, and after cooling, the leaves extract was filtered twice with whatman No. 1 filter paper and kept at 4 • C.

Phytochemical Analysis
Preliminary phytochemical screening was carried out using the standard protocol followed by Ali et al. (2018) and Chandraker et al. (2020) to identify the phytoconstituents present in BPLE.

Green Synthesis of BP-AgNPs and Optimization
Respective volumes (0.5, 1.0, 1.5, and 2.0 mL) of BPLE were added individually to 24.5, 24.0, 23.5, and 23 mL of 1 mM AgNO 3 solutions for a final volume of 25.0 mL in 50 mL Erlenmeyer flasks. Similarly, 23 mL solutions of AgNO 3 were arranged with four concentrations (0.1, 0.25, 0.5, and 1 mM) and mixed with 2.00 mL BPLE. Further, the effect of pH on the synthesis of BP-AgNPs was analyzed. For this study, 2 mL of BPLE was separately added to 23 mL AgNO 3 (1 mM) having variable pH viz., 2, 4, 6, and 8. The pH was adjusted using sulfuric acid, and sodium hydroxide solutions drop by drop. To evaluate the effect of temperature on the green synthesis of BP-AgNPs, the reaction mixture was kept at variable temperatures (27, 40, 60, and 80 • C) in a hot air oven. The color shift from colorless solution to yellowish/dark brown solution suggesting BP-AgNPs synthesis and confirmed the reduction from Ag + to Ag 0 .

Characterization of BP-AgNPs
The synthesis of BP-AgNPs were determined by UV-visible spectroscopy (Shimadzu UV-1800). Fourier Transform Infra-Red spectra obtained with FTIR (Bruker, Germany. Model: Vertex 70) using KBr at a resolution of 0.5 cm −1 in the diffuse reflectance mode and within a range of 500-4,000 cm −1 . Studies of X-Ray Diffraction (XRD) were performed using Bruker D8 at 30 kV and 20 mA current with Cu K (I = 1.54 A) to test the crystallinity of BP-AgNPs. Using Scanning electron microscopy (EVO 18; Carl Zeiss, Germany), the surface morphology and elemental composition (Energy Dispersive X-ray Analysis) of BP-AgNPs were determined. Transmission electron microscopy (Technai G20 FEI) operated at 200 kV, and a 104 beam current was used to determine the size of NPs.

Cytotoxic Activity
Cells were cultured in Dulbecco's Modified Eagle's (DME) medium supplemented with 10% FBS and 1% antibiotic and antimycotic solution at 37 • C with 5% CO 2 . For the control group, cells were cultured in medium containing 0.1% DMSO. For the treatment group, cells were incubated with different nanoparticle dispersed concentrations in DMSO (0.1%). The cytotoxicity of BP-AgNPs against A431 (squamous cell carcinoma cell line) and B16F10 (melanoma cell line) was determined using MTT assay (Singh et al., 2013). Both types of cells were seeded at 5,000 cells/well separately in 96-well plates. After 24 h of seeding, cells were incubated with different concentrations of nanoparticles (10, 25, 50, and 100 µg/ml) for 24 and 48 h. On completion of the treatment time, the media was taken out, and the MTT solution was added to each well and incubated for 4 h. Subsequently, 100 µl of DMSO was added to dissolve the formazan crystals formed. Finally, after incubating the plate at 37 • C for 10 min, absorbance was recorded on a microplate reader at 570 nm. Using the following formula percent cell viability was calculated: Average absorbance of the treated sample Average absorbance of the control sample × 100

Impact on Mitosis in the Onion Root Tip
Onion (Allium cepa; 2n = 16) bulb was purchased from the Lalpur market in front of IGNTU, Amarkantak. The outer scale of bulbs was cleaned, and the bulbs were placed on 100 mL beaker at room temperature (30 ± 1 • C) for root germination (Chandraker et al., 2014). Root tips (2-3 cm) were treated with 20 and 50% of BP-AgNPs suspension for 6 and 12 h, separately. However, DDW was used as a control . After that, roots were submerged in 1 M HCl solution and heated for 4-5 min and transferred to DDW for 2 min. The root tips were crushed with 40% acetocarmine with a dissecting needle, and the coverslip was carefully placed on the slide for microscopic study.
The experiment was performed in triplicate. Chromosomal abnormalities were observed under the microscope, and the mitotic index was calculated as follows.
Where TDC-dividing cells, TC-total number of cell counted.

DNA Interaction Activity
Studies of DNA interaction were performed by the method described by Chandraker et al. (2019b), Different concentrations of CT-DNA (20-260 µl) in Tris-HCl buffer (pH 7.2) were treated with BP-AgNPs (10 µM) in 1 % aqueous DMSO. UV-visible spectrophotometer further examined the specific concentration of the combined solution of CT-DNA and BP-AgNPs.

Photocatalytic Activity
The BP-AgNPs was studied for its catalytic property under sunlight in the degradation of toxic dyes methylene blue (MB) and rhodamine-B (RB). The dye degradation experiment was performed, according to Rodríguez-Cabo et al. (2017). The dye solutions were prepared by dissolving 2.5 mg MB and RB in 250 ml DDW, separately. In both the dye solutions (50 ml), 10 mg of BP-AgNPs were added individually. A control of MB and RB were also prepared without NPs and retained under the same condition. The UV-vis spectra and absorption maxima were monitored at fixed intervals.
Following the standard method of Aadil et al. (2016) with a minor alteration, the H 2 O 2 sensing capability of BP-AgNPs has been noted. In a colloidal solution (3 mL) of BP-AgNPs, 20 mM H 2 O 2 (1 ml) was thoroughly mixed. The initial UV-visual spectrum of BP-AgNPs solution without H 2 O 2 has been recorded. Further, the UV-vis spectra of the reacting solution was observed at fixed intervals.

Antioxidant Activity
The antioxidant activity of BP-AgNPs was evaluated by the DPPH and ABTS free radical scavenging assays. By following the conventional method of Butola and Verma (2019), the DPPH and ABTS reducing potential of BP-AgNPs and the standard reference compound ascorbic acid were determined. DPPH solution (0.1 mM) in methanol was mixed with varying concentration of methanolic BP-AgNPs. After 30 min of incubation in dark, the absorbance (517 nm) was recorded. Similarly, ABTS free radical solution was prepared with potassium persulphate, and treated with different concentrations of BP-AgNPs. After 30 min of incubation, the absorbance was taken at 734 nm. The percentage scavenging activity was calculated using the following formula.
% Scavenging activity = Absorbance of control − Absorbance of sample Absorbance of control × 100

Statistical Analysis
Antimitotic, antioxidant and MTT assays were performed in triplicate and their data expressed in mean ± SE following OriginPro 8.5 software. For MTT assay, data were analyzed by Student's t-test, where P < 0.05 was considered statistically significant.

Phytochemical Analysis
The occurrence of flavonoids, terpenoids, saponins, alkaloids, and tannins in BPLE was confirmed by various qualitative tests ( Table 1). Such phytochemicals might be adsorbed on the surface of Ag+ causing their reduction to Ag 0 , and further, prevent their agglomeration. The previous studies also reported the presence of the same compounds in B. pinnatum (Uchegbu et al., 2017). Among several metabolites, flavonoids were explored to share a significant role in the ethnomedicinal importance of B. pinnatum (Chibli et al., 2014;Fernandes et al., 2019). Besides, pure flavonoids are said to be mainly compound for the transformation of metallic ions to their nanostructures with enhanced anti-microbial and anti-cancer activities (Jain and Mehata, 2017). Similarly, alkaloids, tannins, and saponins have also been reported as green reducing agents to develop novel nanomaterials with versatile applications (Ahmad, 2014;Almadiy and Nenanaah, 2018;Choi et al., 2018). The schematic of BP-AgNPs synthesis is shown in Figure 1.

Green Synthesis of BP-AgNPs and Their Optimization
UV-visible spectroscopy is a relible and basic technique for characterizing nanoparticles. Metallic NPs exhibit absorption bands in the visible region because of surface plasmon resonance (SPR) band (Lopes et al., 2018). Therefore, the synthesis of BP-AgNPs was confirmed by spectroscopic analysis through their distinctive SPR peak at 412 nm, as the band is typical of the nanoscale silver. Whereas, no absorption spectra was detected with an aqueous solution of BPLE and suspension of AgNO 3 salt , separately (Figure 2). Green synthesis of BP-AgNP tends to be highly selective and relies on some essential factors, i.e., extract concentration, pH, temperature, and AgNO 3 concentration. Because of their distinctive properties, these parameters regulate FIGURE 1 | A possible mechanism for the reduction of Ag + to Ag 0 and synthesis of BP-AgNPs.
Frontiers in Molecular Biosciences | www.frontiersin.org the size, shape, yield, stability, and agglomeration of the BP-AgNPs.

Effect of Extract Concentration
A concentration-dependent effect of leaf extract was found in BP-AgNPs synthesis ( Figure 3A). The green synthesis of BP-AgNPs is very low at 0.5 mL concentration of BPLE. This is because of the lesser availability of phytochemicals like phenols, triterpenes, glycosides, alkaloids, flavonoids, steroids, lipids, and organic acids, which act as capping, reducing, and stabilizing agent in phytosyntesis process (Nabikhan et al., 2010). The optimal level of leaf extract was found to be 2.0 mL for green synthesis nanoparticles.

Effect of pH
pH plays a major role in green synthesis of BP-AgNPs. It was confirmed that the size and shape of the NPs could be regulated by adjusting the pH of the solution media (Patra and Baek, 2014). In Figure 3B, the characteristic SPR peak of Ag 0 was not observed at acidic pH. However, a slightly basic medium (pH 8) supports the formation of BP-AgNPs. The obtained result is similar to earlier observations of Gurunathan (2019) and Vanaja et al. (2013) where acidic pH either suppresses NPs formation or gives low absorbance band, whereas, negative ions (OH − ) after dissociation of NaOH in basic medium causes much reduction of Ag + into AgNPs.

Effect of AgNO 3 Concentration
By taking variable concentrations of AgNO 3 in the optimization experiment, it was found that on lower concentrations (0.12-0.5 mM), the absorption peak for AgNPs was not observed ( Figure 3C). This may be due to the very low availability of Ag + ions in the reaction mixture. At 1.0 mM AgNO 3 , significant absorption spectra (412 nm) was found in the UVvis spectrophotometer. Hence, 1 mM AgNO 3 is the optimal concentration for green synthesis of AgNPs. However, in some other reports, a further increase in concentration up to 5 mM showed more absorbance (hyperchromic shift) at the same wavelength and produced larger NPs (Vanaja et al., 2013).

Effect of Temperature
Temperature is also a relevant parameter for NPs synthesis. The physical and chemical methods require respective temperatures >350 and <350 • C, whereas, green synthesis approach follows ambient to 100 • C (Patra and Baek, 2014). In the present study, the synthesis of BP-AgNPs increases with increasing the reaction temperature. The UV-visible spectra ( Figure 3D) showed that 60 • C is the most suitable condition for BP-AgNP synthesis. At room temperatureand 40 • C, synthesis of NPs is very low to moderate, whereas, at 80 • C, nanoparticle synthesis is high but not favored due to aggregation. A similar result was obtained using olive leaf mediated NPs at different temperatures (Khalil et al., 2014). The stability of BP-AgNPs was checked regularly following 8 months of green synthesis. The spectral data suggested adequate stability of NPs with a slight increase in the SPR peak, which may be due to proximity effect or agglomeration.

FT-IR Spectral Analysis
The FT-IR spectrum of BP-AgNPs is shown in Figure 4a, where noticed peaks denote functional groups in various chemical compounds, such as flavonoids, polysaccharides, polyphenols, and triterpenoids. The FTIR bands at 3,000-3, 300, 2904.33, 2358.56, 1594.12, 1385.12, 1021.45, and 669.19 cm −1 . The peak centered on ∼3,300 cm −1 corresponding to O-H stretching, whereas, 2904.33 cm −1 suggests amide C-C stretching. The peak observed at 2358.95 cm −1 may be due to C-H stretching of a methylene group, and the peak at 1594.12 cm −1 corresponds to -C=C-and -C=N stretching. The band at 1385.12 cm −1 corresponds to O-H bend, and 1021.45 cm −1 can be attributed to the stretching vibration of the O-C bend. The final peak observed at 669.17 cm −1 may be due to the N-H stretching of the amide group (Nabikhan et al., 2010). Figure 4b, confirming the presence of Ag in the sample. In the XRD graph at 2θ = 28, 32, and 46, the Bragg reflections were observed that noticeably shows the existence of (111), (200), and (220) lattice plane, respectively. The peak pattern can be an indexed face-centered cubic (fcc) silver (JCPDS, File No. 893722) (Sudhakar et al., 2015). From the analysis of XRD Pattern it was confirmed that green synthesized particles had a nano-size with crystalline nature. Certain extra unattributed peaks near

SEM and EDX Analysis
The topology and morphology of BP-AgNPs were visualized through SEM assessment. The synthesis of consistent and comparatively orbicular BP-AgNPs is confirmed in Figure 4c. Energy-dispersive X-ray analysis (EDX) reveals the composition of elementals in BP-AgNPs. The EDX spectrum, which shows the major elementary peak at 3 keV, indicates metallic silver in Figure 4e. During the capping of AgNP by biomolecules of BPLE, other small peaks of K, Cl, Ca, and O were also created. The quantitative estimate shows that elemental Ag has a maximum weight percentage of 81.77%, while O, Cl, Ca, and K having had 11.43, 5.91, 0.27, and 0.63%, respectively Figure 4f. Figure 4d displays the TEM image which elucidates the formation of isotropic, nearly spherical NPs. The average particle size was measured 15 ± 5 nm, following the particle size determined from the XRD.

In vitro Cytotoxic Activity
MTT assay was performed to determine the cytotoxic property of BP-AgNPs. It is a colorimetric measurement that analyses the emergence of purple-blue formazan crystals by reduction of yellow color dye 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT) by the mitochondrial enzyme succinate dehydrogenase. Based on the viability of cancer cells (human squamous cell carcinoma A431 and mouse melanoma B16F10), the effect of NPs was analyzed. In vitro results displayed a decrease in viability of both A431 and B16F10 cells with an increase in the concentration of BP-AgNP S after 24 h and 48 h of treatment. After 24 h of treatment with BP-AgNPS, there was not much decrease in cell viability at the lower concentrations of 10, 25 and 50 µg/ml, but at higher concentration of 100 µg/ml, cell viability was reduced significantly by ∼50% in A431 cells (p < 0.01) and 80% in B16F10 cancer cells (p < 0.005) in comparison to untreated control cells. Similar results were found after 48 h of treatment, and there was a concentrationdependent decrease in viability of A431 and B16F10 cancer cells. Cell viability was ∼46% in A431 cells (p < 0.01) and 23% in B16F10 cells (p < 0.01) compared to control. BP-AgNPs showed significant cytotoxicity toward skin cancer cells (Figures 5A,B). BP-AgNPs were found to be more effective against B16F10 cell lines with IC 50 : 59.5 µg/ml, rather than A431 cell line showing IC 50 : 96.61 µg/ml after 24 h of treatment. In earlier reports, Butea monosperma mediated Ag and AuNPs were found to be a biocompatible vehicle for chemotherapeutic drugs but did not exhibit cytotoxic effects against the B16F10 cell line (Patra et al., 2015). However, phytosynthesized AgNPs using Impatiens balsamina flowers showed less cytotoxicity and increased IC 50 (196.5 µg/ml) than our report against B16F10 cell line (Nalavothula et al., 2015). Likewise, several research groups documented cytotoxic activity of metallic-NPs against various cancer cell lines in a dose-dependent manner, however, biocompatibility and non-toxicity against normal cells (Ribeiro et al., 2018). In separate experiments, Balasubramani et al. (2015) and Farah et al. (2016) observed a dose-dependent decrease in viability of MCF-7 breast cancer cells with 217 and 257.8 µg/ml IC 50 when treated with Adenium obesum mediated AgNPs and Antigonon letopus mediated AuNPs, respectively. The definite mechanism of NPs' anti-cancer exercise is not yet fully presumed. However, the generation of reactive oxygen species, up-regulation of p53 protein, and expression of caspases are considered to be the major anti-cancer mechanisms (Barabadi et al., 2017). According to Rai et al. (2016) nanoparticle generated ROS promotes caspase-3 activation that is responsible for cell Where P, M, A, and T are prophase, metaphase, anaphase, and telophase, respectively. apoptosis by arresting the G2/M phase of the cancerous cell cycle. Additionally, increased oxidative stress causes oxidation of antioxidant glutathione to glutathione disulfide. Hence, ROS damages not prevented in the cells . Besides, AgNPs have shown to downregulate the action of DNAdependent protein kinase, a damage repair enzyme. Jeyaraj et al. (2013) reported that AgNPs mediated Bcl-2 and Bax gene regulation, which further activates the cascade and controls the caspases 3, 8, and 9 are responsible for the apoptosis of HeLa cell line.

Impact on Mitosis
Allium test is suggested by UNEP, IPCS (International Programme on Chemical Safety), IPPB (International Programme on Plant Bioassay), and WHO as a typical test in cytogenetic monitoring of environmental hazards (Maity et al., 2020). The experiment is also suggested to evaluate the genotoxic effects of novel nanomaterials and considered as a substitute to animal tests (Klančnik et al., 2011). Although severalphysico-chemical mutagens, metal-complexes, and Cu, CdS-NPs have been reported to induce chromosomal (Kumbhakar et al., 2016;Sharma et al., 2018), the cytotoxic effects of Ag-NPs are poorly reported. Root meristem of A. cepa was used to detect the cytotoxic effect of BP-AgNP S at three different concentrations (10, 20, and 30 µg/mL). The present investigation showed that BP-AgNPs decrease the mitotic index (MI) ( Table 2) and induce significant alterations in the treated roots relative to the control samples (DDW and AgNO3 treated roots). BP-AgNPs might have been prompted cytotoxicity in treated roots of meristematic cells, causing DNA damage or cell death (Lateef et al., 2016). The values of MI for BP-AgNPs were found 45.0 ± 0.28, 41.66 ± 0.44, and 39.96 ± 0.08 after 12 h which significantly decreased to 40.63 ± 0.27, 38.70 ± 0.60, and 34.53 ± 0.26 after 24 h at 10, 20, and 30 µg/ml, respectively. However, in the control set and AgNO 3 solution (30 µg/ml), the MI was found to be 55.6 ± 0.4 and 52.76 ± 1.38, respectively. The experiment demonstrated that the cell division was inversely proportional to the BP-AgNP concentrations. The findings were statistically significant (p < 0.05) in all the treated concentrations as compared to the control. Chromosomal abnormalities were severely observed in treated meristematic cells with C-metaphase, anaphase with lagging chromosome, stickiness telophase, vagrants chromosomes, anaphase with chromosome bridge, anaphase with lagging chromosome, sticky metaphase, etc. (Figure 6). Our observations are supported by earlier findings where NPs decrease MI with the increase in mitotic anomalies in Allium cepa (Nagaonkar et al., 2015;Kumbhakar et al., 2016). Few reports advocate that AgNPs might interfere with the normal cycle of mitotic cells causing decreased gene expression encoding cyclin-dependent kinase 2, slower advancement of cells to S-phase, and blockage of G2-phase, leading to cell death. AgNPs are found to alter cytoplasm viscosity which leads to atypical behavior of the spindle causing chromosomal abnormalities and formation of micronuclei (Daphedar and Taranath, 2018;Fouad and Hafez, 2018). NPs are also responsible for the breakage and reunion of chromosomal material resulting in structural and numerical changes in chromosomes (Chromosomal abbreviations).

DNA Interaction Study
The UV-vis spectroscopy is one of the most significant techniques for determining the efficiency of the compounds to interact with DNA. Before the addition of BP-AgNP, the purity and sustainability of CT-DNA were tested at room temperature showing a high absorption peak at 264 nm. The concentration of BP-AgNPs was made constant and CT-DNA was added gradually for the study. There are a few reports which have mentioned such kind of interaction between nanostructures and DNA as providing such an interactive feature. Three possible modes for these interactions are electrostatic linking, groove linking, and intercalation (Ribeiro et al., 2018).

Photocatalytic Activity
Two different types of dyes (thiazine: MB and azo: Rh-B) were selected as model pollutants to study the dye degradation capabilities of BP-AgNPs under solar irradiation. Both the dyes are positively charged (basic). The distinctive absorption maxima for MB and Rh-B were peaked at 663 and 554 nm, respectively (Figures 8A,B). MB and Rh-B are gradually degraded which is expressed by a significant decrease in peak strength with time increase. Until the end of the exposure period, there was no color change in the control set of both the dyes in the absence of BP-AgNPs (Figures 8C,D). The efficacy of BP-AgNPs in dye degradation was determined as follows (Alshehri et al., 2017).
Where C 0 is the initial concentration of the dye solution at t = 0 and Ct is the concentration of the dye solution after a specific exposure to sunlight. In the present work, it is represented in plot that MB and Rh-B were degraded 100% within 110 and 100 min, respectively. However, in similar reports, MB was found to be degraded significantly, after 6 and 72 h from Cordia dichotoma and Morinda tinctoria mediated NPs, respectively (Vanaja et al., 2014;Kumari et al., 2016). Green synthesized NPs from Zanthoxylum armatum were also reported for noteworthy degradation of toxic dyes Safranine-O, Methylred, Methyl-orange, and MB after 24 h (Jyoti and Singh, 2016). Thus, the biofabricated BP-AgNPs can serve as a stable and effective green catalyst for the nano-degradation of MB and Rh-B under visible light. The kinetic study is among the most relevant approaches from which reaction mechanisms are described. In Figures 8E,F, a linear plot (with slope: −0.022 for MB and −0.033 for Rh-B) of ln(C t /C 0 ) vs. time for photocatalytic degradation of MB and Rh-B by BP-AgNPs, shows pseudo-first -order kinetics. The rate constant value of MB degradation is calculated 4.9 × 10 −4 sec −1 and for Rh-B 4.5 × 10 −4 sec −1 . The regression coefficient (for MB R2 = 0.98 and Rh-B R2 = 0.80) revealed that the degradation rate of MB and Rh-B were following the Langmuir-Hinshelwood kinetic model.  H 2 O 2 Sensing Capability BP-AgNPs was evaluated with potential H 2 O 2 sensing capacity in the present report. The comparative spectra at regular interval is shown in Figure 9. The brown color (vial a) constantly diminished and finally appeared colorless (vial b) after 14 min (Figure 9ii). In the control set without H 2 O 2 , no changes in the color and intensity of the SPR absorbance were observed. Mohan et al. (2014) proposed that the inclusion of AgNPs to H 2 O 2 causes the creation of reactive oxygen species, that trigger the degeneration AgNPs. Figure 9(i) indicates a linear plot (slope: 0.021) of C t /C 0 (1-ln) vs. time for BP-AgNPs mediated H 2 O 2 sensing, exhibiting pseudo-first-order kinetics. The sensing rate constant value for H 2 O 2 is estimated at 3.8 × 10-3 s −1 . The regression coefficient of H 2 O 2, R 2 = 0.88 indicated that the sensing capacity of BP-AgNPs has followed the kinetic model of Langmuir-Hinshelwood.
These results indicate that BP-AgNPs can be used successfully to identify H 2 O 2 concentration in several unknown samples or environmental effluents. Similar NPs-based H 2 O 2 sensors were also reported using Bacillus subtilis and Calliandra haematocephala (Mohan et al., 2014;Raja et al., 2017).
The following mechanism shows the probable H 2 O 2 decomposition reaction process by BP-AgNPs (Ghosh et al., 2019).  a diamagnetic compound (bright yellow) when counter with electron or hydrogen molecules. The magnitude of the color transition of DPPH from violet-blue to bright-yellow depends on the nature and amount of the substance. Figures 10A,B are showing dose-dependent free radical scavenging activity of BP-AgNPs. The concentration of BP-AgNPs ranging from 31.25 to 500 µg/mL showed 60.50-87.57% DPPH scavenging activity with 89.05 µg/mL IC 50 . However, for the ascorbic acid 75.64-98.94% scavenging activity reported with 41.5 µg/mL IC 50 at the same concentrations ( Figure 10A). Similarly, ABTS free radical scavenging was observed from 9.16 to 79.32% at 31.25-500 µg/mL BP-AgNPs with an IC 50 value of 259.14 µg/mL, whereas, ascorbic acid displayed 38.39-88.09% inhibition with 173.12 µg/mL IC 50 ( Figure 10B). Similar observations were found with leaf extracts of Prunus japonica and Desmostachya bipinnata showing antioxidant activity in terms of free radical inhibition (Saravanakumar et al., 2017;Guntur et al., 2018). The results firmly advocate the utilization of BP-AgNPs as natural antioxidants to preserve health against oxidative stresses affiliated with degenerative diseases.

CONCLUSIONS
Biofabrication of silver nanoparticles was successfully achieved using BPLE in the present report. A facile, rapid, and ecofriendly green synthesis approach was adopted to get stable and nonaggregated BPAgNPs taking benefit of natural capping, reducing, and stabilizing agents in the form of flavonoids, alkaloids, terpenoids, saponins and tannins present in the plant extract. FTIR spectra revealed the biomolecules adsorbed on the surface of NPs which are responsible for reducing Ag + to Ag 0 in the form of NPs. UV-visual spectroscopy, XRD, SEM, EDX, and TEM revealed the salient SPR peak at 412 nm, face-centered cubic structure, dispersion, elemental composition, and size of BP-NPs, respectively. The outstanding photocatalytic degradation of hazardous dyes (MB, RB), and H 2 O 2 sensing abilities of BP-AgNPs make them suitable agents for nanoremediation of industrial effluents and reactive oxygen species. The biofabricated BP-AgNPs have shown in-vitro antioxidant activity, in-vitro interaction with CT-DNA, induced the chromosomal aberration in the mitotic cells of Allium cepa, and cytotoxic activity against A431 (squamous cell carcinoma) and B16F10 (melanoma) cell line. In our knowledge, this is the first report on various environmental and biological applications of B. pinnatum mediated NPs. Our results suggest potential uses of BP-AgNPs in cell biology. Similarly, The results described here provide the framework for the future implementation of AgNPs in the treatment of skin cancer. The corresponding results of the synthesized BP-AgNPs are related to the decreased expense of a process and the fact that it is a "friendly" biological synthesis method. However, more research is needed to modify the size and shape of metallic NPs.

DATA AVAILABILITY STATEMENT
The original contributions presented in the study are included in the article/supplementary materials, further inquiries can be directed to the corresponding author/s.

AUTHOR CONTRIBUTIONS
The BP-AgNPs was synthesized by SC. The applications of the AgNPs were investigated by SC and ML. The cytotoxicity experiment was performed and reviewed by PD and RPS. The manuscript was written and reviewed by SC and RS. All the experiments were supervised under RS. All authors contributed to the article and approved the submitted version.