Abstract
Silk possesses many beneficial wound healing properties, and electrospun scaffolds are especially applicable for skin applications, due to their smaller interstices and higher surface areas. However, purified silk promotes microbial growth. Selenium nanoparticles have shown excellent antibacterial properties and are a novel antimicrobial chemistry. Here, electrospun silk scaffolds were doped with selenium nanoparticles to impart antibacterial properties to the silk scaffolds. Results showed significantly improved bacterial inhibition and mild improvement in human dermal fibroblast metabolic activity. These results suggest that the addition of selenium nanoparticles to electrospun silk is a promising approach to improve wound healing with reduced infection, without relying on antibiotics.
Introduction
Researchers in the tissue engineering field work toward repairing and/or regenerating damaged tissues and organs through a combination of biomaterial scaffolds, cell signaling moieties, and cell (Langer and Vacanti, 1993). The ideal tissue engineering scaffold closely mimics the physical and chemical makeup of the organ to be replaced and should serve as an artificial extracellular matrix to support cell growth and differentiation. Electrospun scaffolds closely mimic the physical composition of native extracellular matrix (ECM) morphology.
Electrospinning works by applying a high voltage field to a solution of polymer dissolved in a conductive solvent (Sill and von Recum, 2008). The voltage induces electrostatic repulsion within the polymer solution and forms a cone like structure, the Taylor cone, held together by the force balance of the electrostatic repulsion and surface tension. Eventually, the electrostatic repulsion overcomes the surface tension forces holding the polymer solution together. Once this critical limit has been reached, a polymer jet is formed out of the edge of the Taylor cone toward a positively charged collector, and the solvent is evaporated in the flight path from the cone to the collector, leaving a polymer matrix with fibers relevant to physiological regime. The physical parameters of the scaffold may be adjusted based on polymer composition, solvent mixture, voltage, and many other parameters used to create the matrix. Researchers also have a high degree of control over the fiber orientation of electrospun scaffolds by adjusting the type of collector. Because of these processing advantages, electrospinning has been researched for a variety of tissue engineering applications such as cardio (Hajiali et al., 2011; Liu et al., 2011; Du et al., 2012), bone (Shin et al., 2010; Cai et al., 2012; Frohbergh et al., 2012; Liu et al., 2014), neural (Wang et al., 2011; Guan et al., 2013; Kador et al., 2013; Prabhakaran et al., 2013; Baiguera et al., 2014; Irani et al., 2014), skin (Dhandayuthapani et al., 2010; Jin et al., 2011; Kuppan et al., 2011; Rnjak-Kovacina et al., 2011), tendon/ligament (Howell et al., 2004; Sahoo et al., 2010a,b; James et al., 2011; Cardwell et al., 2012), and stem cell expansion/differentiation (Shin et al., 2010; Sahoo et al., 2010a; James et al., 2011; Jin et al., 2011; Wang et al., 2011; Cardwell et al., 2012; Irani et al., 2014).
Electrospun scaffolds promote many beneficial cellular responses for tissue engineering and are generally better for cell proliferation and differentiation than 2D substrates. In particular, silk electrospun scaffolds demonstrate good responses as tissue engineering scaffold for wound healing (Wharram et al., 2010; Gil et al., 2013; Lee et al., 2014). Silk promotes collagen synthesis, re-epithelialization, wound healing, atopic dermatitis alleviation, and scar reduction (Ricci et al., 2004; Fini et al., 2005; Roh et al., 2006; Okabayashi et al., 2009). However, pure silk shows negligible or even negative antibacterial properties (Kaur et al., 2014). Previously, groups have loaded electrospun silk scaffold with silver nanoparticles to impart anti-bacterial properties (Kang et al., 2007). However, silver is a commonly used antibiotic that has become resistant in certain strains of bacteria (Silver, 2003).
Selenium nanoparticles are a novel antibiotic chemistry to which there is no known bacterial resistance (Tran and Webster, 2011, 2013; Wang and Webster, 2012, 2013; Shakibaie et al., 2015). Selenium is a common trace element in the body and is important to healthy nutrition, especially in the formation of selenoproteins (Andrews et al., 2011; Santhosh Kumar and Priyadarsini, 2014). Selenium has been suggested to have anticancer effects as well (Clark et al., 1996). Here, we doped selenium nanoparticles to electrospun silk scaffold to impart antibacterial properties to silk (Rockwood et al., 2011). Human dermal fibroblasts were used to determine the in vitro changes in metabolic activity while Staphylococcus aureus were used to determine the effects of the bacterial inhibition.
Materials and methods
Materials
Bombyx mori silk cocoons were obtained from Mulberry Farms (Fallbrook, CA). Formic acid was purchased from Sigma-Aldrich (Saint Louis, MO). Selenium nanoparticles were synthesized as described below.
Extraction of silk fibroin from Bombyx mori silk cocoons
Silk fibroin was prepared from Bombyx mori cocoons according to previously established protocols with minor modifications (Rockwood et al., 2011). B. mori silk cocoons were cut into small pieces and boiled in 0.02 M Na2CO3 (Sigma-Aldrich) for 30 min to remove the glue-like sericin coating layer from the structural fibroin protein which was then rinsed 3x with distilled water (diH2O). The obtained silk fibroin fibers were dried overnight, dissolved in a LiBr (Sigma-Aldrich) solution (9.3 M) at 60°C for 4 h, and dialyzed through a cellulose membrane (ThermoFisher, Waltham, MA, 3500, MWCO) across distilled water for 4 days. The obtained silk solutions were centrifuged thrice at 4200 g and lyophilized for 4 days before resuspending in formic acid for a final concentration of 8% silk/formic acid.
Electrospinning of silk/formic acid solution
Eight percentage of silk solution was then electrospun at 18,000 volts, room temperature, 0% relative humidity, and 60 cm to collector. These conditions were optimized to produce fibers with dimensions that resemble those from the native extracellular matrix. Afterwards, 70% methanol (Sigma-Aldrich) was used to treat the electrospun silk to prevent hydrolysis of the membrane. Treated silk membranes were dried overnight in the fume hood.
Selenium nanoparticle synthesis
0.1 M sodium selenite [Alfa Aesar, Ward Hill, MA, Na2SeO3(H2O)5] and 0.1 M glutathione, GSH (Alfa Aesar), (C10H17N3O6S) were added onto the treated membranes before 0.2 M sodium hydroxide (NaOH) was added to precipate the sodium nanoparticles. Finally, double distilled deionized water was added thrice to quench the reaction and wash the membranes.
Specimen characterization
Imaging of the specimens was conducted with a Hitachi S4800 Tokyo, Japan Scanning Electron Microscope (SEM, Hitachi S4800 SEM, Tokyo, Japan). A 4.5 nm layer of platinum was sputter coated (Cressington 208; Cressington Scientific Instruments, Watford, UK) onto the membranes to provide a conductive surface. SEM analysis was conducted with a 3 kV accelerating voltage. Characterization was completed using both secondary electrons and backscatter electrons, which impart a stronger signal to heavier elements, such as selenium.
Cellular assays
Mammalian cell activity culture and characterization
Passages 3–12 human dermal fibroblast (HDF, Lonza, Basel, Switzerland) were cultured in Dulbecco's Modified Eagle Medium (DMEM, Sigma Aldrich) supplemented with 10% fetal bovine serum (Hyclone, Logan, UT) and 1% penicillin/streptomycin (P/S, Sigma Aldrich) in a 37°C, humidified, 5% CO2/95% air environment.
MTS assay (Promega, Fitchburg, WI) was used to determine the metabolic cell activity of the HDFs. Before cell seeding, the electrospun silk scaffolds were washed with 70% ethanol (Sigma-Aldrich) before rinsing with double distilled deionized water. HDFs were cultured to ~90% confluence, rinsed with Dulbecco's phosphate-buffered saline without calcium chloride and magnesium chloride (dPBS, Sigma Aldrich), and detached from the tissue culture plate by using 0.25% trypsin-EDTA (Sigma-Aldrich). Detached cells were then centrifuged at 2000 r.p.m. and resuspended at a density of 50,000 cells/ml before seeding onto the silk scaffolds in a 96 well-plate at 100 μl in each well (5000 cells/well). The HDFs incubated for 1, 2, and 4 days. Afterwards, the medium was removed from the sample and 100 μl solution of 1:5 MTS dye with DMEM medium (v/v) were added to each well. Samples were placed back into the incubator for 2.5 h. to allow the MTS to react with the metabolic products of the adherent cells before reading in a SpectraMax M3 microplate reader (Molecular Devices, Sunnyvale, CA) at an absorbance wavelength of 490 nm. The absorbance values of wells containing only DMEM medium without cells were subtracted from the absorbance values of the wells containing cells. The metabolic activity of each well was compared with the metabolic activity of known numbers of cells by a standard curve constructed at the beginning of each trial.
Bacterial cell activity measurement
Staphylococcus aureus (ATCC-12600) were inoculated in 3% tryptic soy broth (TSB, Sigma-Aldrich) overnight. After 24 h., the Staphylococcus aureus were diluted with TSB until absorbance value reached 0.52 at wavelength of 562 nm. This corresponded with a cell density of 109 colony forming units (CFU)/ml. Afterwards, the Staphylococcus aureus were diluted 1000x in TSB before seeding onto the silk samples in a non-treated 96 well-plate in 100 μl of solution (105 CFU/well). After 24 h., the BacTiter Glo assay (Promega), a luciferase based ATP assay was used to quantify the amount of ATP present on the electrospun silk samples. BacTiter Glo reagent was added at the same volume as the medium in each well, 100 μl, at room temperature. The samples were inoculated at room temperature for 5 min. while the BacTiter Glo reagents solubilized the bacterial membrane, after which, the luminescence was measured using the SpectraMax M3. A standard curve was constructed to equate the luminescence readings with known ATP amounts.
Statistics
All experiments were conducted in triplicate and repeated at least three times each. Analysis of variance and student's t-test were used to determine whether the differences in cellular activity over the different time periods were significant.
Results and discussion
To characterize the morphology of the electrospun silk scaffold, scanning electron microscope was used to visualize the surface of the nanocomposite. As shown in Figures 1A,B, the electrospun silk scaffolds contained fiber diameters ~100–200 nm and pore sizes ~2 μm. The silk scaffold contained unaligned fibers with very little beading and uniform thickness, demonstrating a morphology similar to those in the native extra-cellular matrix (ECM). The selenium nanoparticles (SeNP) were then reacted on the scaffold, causing a physisorption of the SeNP onto the silk scaffold. Two reaction conditions were chosen to deposit the SeNPs; SEM images showed that these produced two homogenous and distinct selenium nanoparticle populations: 40 (Figures 1C,D) and 70 nm (Figures 1E,F) nanoparticles.
Figure 1
First, in vitro viability tests were conducted using HDF cells. These cells were seeded onto the silk scaffold without selenium nanoparticles, the silk scaffolds containing the 40 and 70 nm selenium nanoparticles, and on regular polystyrene (PS) tissue culture plate to determine the change in growth of the HDF cells when grown on these substrates (Figure 2). Electrospun silk without addition of selenium nanoparticles produced statistically insignificant change (p > 0.05) in HDF activity as compared activity when grown on normal tissue culture plate across all 3 days tested. The silk/selenium nanocomposites produced significantly higher metabolic activity for HDF as compared to HDF grown on tissue culture plate. The addition of selenium nanoparticles significantly improved the metabolic activity of HDF, especially at the shorter term time points. At 1 and 2 days, silk scaffold doped with 40 nm selenium nanoparticles produced greater than two fold increase in metabolic signal, 264 and 245% on day 1 and 2, respectively, as compared to the tissue culture plate control while the 70 nm scaffold produced 160 and 267% on day 1 and 2, respectively. The day 1 (p < 0.05) and day 2 signal (p < 0.01) from the silk+40 nm SeNP scaffolds and the day 2 signal (p < 0.05) from the silk+70 nm SeNP scaffolds were statistically significant from the signal produced at the same time points on the tissue culture plates. Surprisingly, the silk scaffolds without nanoparticle addition did not produce a statistically significant improvement in HDF growth despite the ECM like morphology. There was mild improvement on day 2 (132% compared to control), but overall, the presence of silk alone did not significant improve HDF response. The short term improvement in activity may have plateaued by day 4 compared to the control, because the HDF may have reached confluency on the silk/selenium nanocomposites.
Figure 2
Finally, the bacteria results were accessed by ATP assay. Here, the performance of the silk scaffolds were compared to Staphylococcus aureus grown in solution in the polystyrene plate. Bacterial growth across all silk samples showed statistically significant reduction as compared to untreated samples grown in solution. Bacteria grown on silk without selenium nanoparticles showed a 74% reduction as compared with the control (p < 0.05). This was somewhat surprising, because this contradicted other reports found in literature (Kaur et al., 2014).
Addition of selenium nanoparticles significantly improved the bacterial load: the addition of the 40 nm selenium nanoparticles reduced bacterial load by 95% and the 70 nm selenium nanoparticles by 96% compared to the control (p < 0.01). The doping of selenium had achieved an additional reduction of 80% for the 40 nm selenium nanoparticle and 87% for the 70 nm selenium nanoparticle as compared to the silk samples. The 70 nm selenium nanoparticle produced an almost one log reduction in ATP content (0.88) as compared to the silk sample and an overall 1.4 log reduction compared to the control.
Conclusion
This study showed for the first time the efficacy of doping selenium nanoparticles with silk to improve bacterial efficacy. Reaction conditions successfully synthesized two different sized populations of selenium nanoparticles onto electrospun silk scaffolds. These nanocomposites were then compared to silk scaffolds and normal tissue culture plates and were found to significantly improve both the mammalian cell response while reducing bacterial cell activity. Addition of the selenium nanoparticles significantly improved the short term human dermal fibroblast metabolic activity while reducing the ATP content of Staphylococcus aureus. Together, these results suggest that selenium nanoparticle may selectively enhance mammalian cells functions while killing or reducing the bacterial load. In summary, this study provides evidence of the potential value of the use of selenium nanoparticles in skin applications due to their selective activity. Future works will focus on determining the mechanism by which selenium nanoparticles achieve this selectivity and the scope of the selenium nanoparticles for inhibiting bacteria in skin applications.
Funding
The authors would like to thank Northeastern University for funding and facilities.
Conflict of interest statement
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Statements
Author contributions
SC and BE made substantial contributions to conception and design, and acquisition of data, and nanalysis and interpretation of data. Equally contributed to planning and idea. AR participated in design of experiment/idea and revising the article. TW edited/revised it critically for important intellectual content and gave final approval of the version to be submitted and any revised version.
Acknowledgments
The authors thank Mr. William H. Fowle (Northeastern University) for help with the SEM and the Nanomedicine Laboratory.
Conflict of interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
References
1
AndrewsP. J. D.AvenellA.NobleD. W.CampbellM. K.CroalB. L.SimpsonW. G.et al. (2011). Randomised trial of glutamine, selenium, or both, to supplement parenteral nutrition for critically ill patients. BMJ342:d1542. 10.1136/bmj.d1542
2
BaigueraS.Del GaudioC.LucatelliE.KuevdaE.BoieriM.MazzantiB.et al. (2014). Electrospun gelatin scaffolds incorporating rat decellularized brain extracellular matrix for neural tissue engineering. Biomaterials35, 1205–1214. 10.1016/j.biomaterials.2013.10.060
3
CaiY.-Z.ZhangG.-R.WangL.-L.JiangY.-Z.OuyangH.-W.ZouX.-H. (2012). Novel biodegradable three-dimensional macroporous scaffold using aligned electrospun nanofibrous yarns for bone tissue engineering. J. Biomed. Mater. Res. Part A.100A, 1187–1194. 10.1002/jbm.a.34063
4
CardwellR. D.DahlgrenL. A.GoldsteinA. S. (2012). Electrospun fibre diameter, not alignment, affects mesenchymal stem cell differentiation into the tendon/ligament lineage. J. Tissue Eng. Regen. Med. 8, 937–945. 10.1002/term.1589
5
ClarkL. C.CombsG. F.Jr.TurnbullB. W.SlateE. H.ChalkerD. K.ChowJ.et al. (1996). Effects of selenium supplementation for cancer prevention in patients with carcinoma of the skin: a randomized controlled trial. JAMA276, 1957–1963. 10.1001/jama.1996.03540240035027
6
DhandayuthapaniB.KrishnanU. M.SethuramanS. (2010). Fabrication and characterization of chitosan-gelatin blend nanofibers for skin tissue engineering. J. Biomed. Mater. Res. Part B Appl. Biomater.94B, 264–272. 10.1002/jbm.b.31651
7
DuF.WangH.ZhaoW.LiD.KongD.YangJ.et al. (2012). Gradient nanofibrous chitosan/poly ε-caprolactone scaffolds as extracellular microenvironments for vascular tissue engineering. Biomaterials33, 762–770. 10.1016/j.biomaterials.2011.10.037
8
FiniM.MottaA.TorricelliP.GiavaresiG.Nicoli AldiniN.TschonM.et al. (2005). The healing of confined critical size cancellous defects in the presence of silk fibroin hydrogel. Biomaterials26, 3527–3536. 10.1016/j.biomaterials.2004.09.040
9
FrohberghM. E.KatsmanA.BottaG. P.LazaroviciP.SchauerC. L.WegstU. G.et al. (2012). Electrospun hydroxyapatite-containing chitosan nanofibers crosslinked with genipin for bone tissue engineering. Biomaterials33, 9167–9178. 10.1016/j.biomaterials.2012.09.009
10
GilE. S.PanilaitisB.BellasE.KaplanD. L. (2013). Functionalized silk biomaterials for wound healing. Adv. Healthc. Mater.2, 206–217. 10.1002/adhm.201200192
11
GuanS.ZhangX.-L.LinX.-M.LiuT.-Q.MaX.-H.CuiZ.-F. (2013). Chitosan/gelatin porous scaffolds containing hyaluronic acid and heparan sulfate for neural tissue engineering. J. Biomater. Sci.24, 999–1014. 10.1080/09205063.2012.731374
12
HajialiH.ShahgasempourS.Naimi-JamalM. R.PeiroviH. (2011). Electrospun PGA/gelatin nanofibrous scaffolds and their potential application in vascular tissue engineering. Int. J. Nanomed.6, 2133–2141. 10.2147/IJN.S24312
13
HowellM. D.JonesJ. F.KisichK. O.StreibJ. E.GalloR. L.LeungD. Y. M. (2004). Selective killing of vaccinia virus by LL-37: implications for eczema vaccinatum. J. Immunol. 172, 1763–1767. 10.4049/jimmunol.172.3.1763
14
IraniS.ZandiM.SalamianN.SaeedS. M.Daliri JoupariM.AtyabiS. M. (2014). The study of P19 stem cell behavior on aligned oriented electrospun poly(lactic-co-glycolic acid) nano-fibers for neural tissue engineering. Polym. Adv. Technol.25, 562–567. 10.1002/pat.3280
15
JamesR.KumbarS. G.LaurencinC. T.BalianG.ChhabraA. B. (2011). Tendon tissue engineering: adipose-derived stem cell and GDF-5 mediated regeneration using electrospun matrix systems. Biomed. Mater.6:25011. 10.1088/1748-6041/6/2/025011
16
JinG.PrabhakaranM. P.RamakrishnaS. (2011). Stem cell differentiation to epidermal lineages on electrospun nanofibrous substrates for skin tissue engineering. Acta Biomater.7, 3113–3122. 10.1016/j.actbio.2011.04.017
17
KadorK. E.MonteroR. B.VenugopalanP.HertzJ.ZindellA. N.ValenzuelaD. A.et al. (2013). Tissue engineering the retinal ganglion cell nerve fiber layer. Biomaterials34, 4242–4250. 10.1016/j.biomaterials.2013.02.027
18
KangM.JungR.KimH.-S.YoukJ. H.JinH.-J. (2007). Silver nanoparticles incorporated electrospun silk fibers. J. Nanosci. Nanotechnol.7, 3888–3891. 10.1166/jnn.2007.056
19
KaurJ.RajkhowaR.AfrinT.TsuzukiT.WangX. (2014). Facts and myths of antibacterial properties of silk. Biopolymers101, 237–245. 10.1002/bip.22323
20
KuppanP.VasanthanK. S.SundaramurthiD.KrishnanU. M.SethuramanS. (2011). Development of Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) fibers for skin tissue engineering: effects of topography, mechanical, and chemical stimuli. Biomacromolecules12, 3156–3165. 10.1021/bm200618w
21
LangerR.VacantiJ. P. (1993). Tissue engineering. Science260, 920–926. 10.1126/science.8493529
22
LeeO. J.JuH. W.KimJ. H.LeeJ. M.KiC. S.KimJ. H.et al. (2014). Development of artificial dermis using 3D electrospun silk fibroin nanofiber matrix. J. Biomed. Nanotechnol.10, 1294–1303. 10.1166/jbn.2014.1818
23
LiuH.LiX.ZhouG.FanH.FanY. (2011). Electrospun sulfated silk fibroin nanofibrous scaffolds for vascular tissue engineering. Biomaterials32, 3784–3793. 10.1016/j.biomaterials.2011.02.002
24
LiuY.CuiH.ZhuangX.WeiY.ChenX. (2014). Electrospinning of aniline pentamer-graft-gelatin/PLLA nanofibers for bone tissue engineering. Acta Biomater.10, 5074–5080. 10.1016/j.actbio.2014.08.036
25
OkabayashiR.NakamuraM.OkabayashiT.TanakaY.NagaiA.YamashitaK. (2009). Efficacy of polarized hydroxyapatite and silk fibroin composite dressing gel on epidermal recovery from full-thickness skin wounds. J. Biomed. Mater. Res. Part B Appl. Biomater.90B, 641–646. 10.1002/jbm.b.31329
26
PrabhakaranM. P.VatankhahE.RamakrishnaS. (2013). Electrospun aligned PHBV/collagen nanofibers as substrates for nerve tissue engineering. Biotechnol. Bioeng.110, 2775–2784. 10.1002/bit.24937
27
RicciG.PatriziA.BendandiB.MennaG.VarottiE.MasiM. (2004). Clinical effectiveness of a silk fabric in the treatment of atopic dermatitis. Br. J. Dermatol.150, 127–131. 10.1111/j.1365-2133.2004.05705.x
28
Rnjak-KovacinaJ.WiseS. G.LiZ.MaitzP. K. M.YoungC. J.WangY.et al. (2011). Tailoring the porosity and pore size of electrospun synthetic human elastin scaffolds for dermal tissue engineering. Biomaterials32, 6729–6736. 10.1016/j.biomaterials.2011.05.065
29
RockwoodD. N.PredaR. C.YucelT.WangX.LovettM. L.KaplanD. L. (2011). Materials fabrication from Bombyx mori silk fibroin. Nat. Protocols6, 1612–1631. 10.1038/nprot.2011.379
30
RohD.-H.KangS.-Y.KimJ.-Y.KwonY.-B.Young KweonH.LeeK. G.et al. (2006). Wound healing effect of silk fibroin/alginate-blended sponge in full thickness skin defect of rat. J. Mater. Sci. Mater. Med.17, 547–552. 10.1007/s10856-006-8938-y
31
SahooS.AngL. T.GohJ. C.-H.TohS.-L. (2010b). Growth factor delivery through electrospun nanofibers in scaffolds for tissue engineering applications. J. Biomed. Mater. Res. Part A.93A, 1539–1550. 10.1002/jbm.a.32645
32
SahooS.TohS. L.GohJ. C. H. (2010a). A bFGF-releasing silk/PLGA-based biohybrid scaffold for ligament/tendon tissue engineering using mesenchymal progenitor cells. Biomaterials31, 2990–2998. 10.1016/j.biomaterials.2010.01.004
33
Santhosh KumarB.PriyadarsiniK. I. (2014). Selenium nutrition: how important is it?Biomed. Preventive Nutr.4, 333–341. 10.1016/j.bionut.2014.01.006
34
ShakibaieM.ForootanfarH.GolkariY.Mohammadi-KhorsandT.ShakibaieM. R. (2015). Anti-biofilm activity of biogenic selenium nanoparticles and selenium dioxide against clinical isolates of Staphylococcus aureus, Pseudomonas aeruginosa, and Proteus mirabilis. J. Trace Elements Med. Biol.29, 235–241. 10.1016/j.jtemb.2014.07.020
35
ShinM.YoshimotoH.VacantiJ. P. (2010). In vivo bone tissue engineering using mesenchymal stem cells on a novel electrospun nanofibrous scaffold, in Advances in Tissue Engineering, Vol. 2, eds JohnsonP. C.MikosA. G. (Mary Ann Liebert), 205–213.
36
SillT. J.von RecumH. A. (2008). Electrospinning: applications in drug delivery and tissue engineering. Biomaterials29, 1989–2006. 10.1016/j.biomaterials.2008.01.011
37
SilverS. (2003). Bacterial silver resistance: molecular biology and uses and misuses of silver compounds. FEMS Microbiol. Rev.27, 341–353.
38
TranP. A.WebsterT. J. (2011). Selenium nanoparticles inhibit Staphylococcus aureus growth. Int. J. Nanomedicine.6:1553. 10.2147/IJN.S21729
39
TranP. A.WebsterT. J. (2013). Antimicrobial selenium nanoparticle coatings on polymeric medical devices. Nanotechnology24, 155101. 10.1088/0957-4484/24/15/155101
40
WangA.TangZ.ParkI.-H.ZhuY.PatelS.DaleyG. Q.et al. (2011). Induced pluripotent stem cells for neural tissue engineering. Biomaterials32, 5023–5032. 10.1016/j.biomaterials.2011.03.070
41
WangQ.WebsterT. J. (2012). Nanostructured selenium for preventing biofilm formation on polycarbonate medical devices. J. Biomed. Mater. Res. Part A100A, 3205–3210. 10.1002/jbm.a.34262
42
WangQ.WebsterT. J. (2013). Short communication: inhibiting biofilm formation on paper towels through the use of selenium nanoparticles coatings. Int. J. Nanomed.8:407. 10.2147/IJN.S38777
43
WharramS. E.ZhangX.KaplanD. L.McCarthyS. P. (2010). Electrospun silk material systems for wound healing. Macromol. Biosci.10, 246–257. 10.1002/mabi.200900274
Summary
Keywords
silk, electrospinning, antibacterial nanoparticles
Citation
Chung S, Ercan B, Roy AK and Webster TJ (2016) Addition of Selenium Nanoparticles to Electrospun Silk Scaffold Improves the Mammalian Cell Activity While Reducing Bacterial Growth. Front. Physiol. 7:297. doi: 10.3389/fphys.2016.00297
Received
26 April 2016
Accepted
28 June 2016
Published
14 July 2016
Volume
7 - 2016
Edited by
Marianna Bei, Harvard Medical School, USA
Reviewed by
Henrique De Amorim Almeida, Polytechnic Institute of Leiria, Portugal; Miguel Angel Mateos Timoneda, Institute for Bioengineering of Catalonia, Spain
Updates
Copyright
© 2016 Chung, Ercan, Roy and Webster.
This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) or licensor are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Stanley Chung chung.st@husky.neu.edu
This article was submitted to Clinical and Translational Physiology, a section of the journal Frontiers in Physiology
Disclaimer
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.