Photocatalytic Hydrogen Production of Nd/Co Co-Doped BiFeO₃ Nanoparticles With a Cellular Architecture

Abstract

Bismuth ferrite (BFO) nanoparticle with general formula Bi_1-xNd_xFe_1-yCo_yO₃ (x=0, 0.05; y=0, 0.05, 0.10, 0.15, 0.20) were prepared using a two-solvent sol-gel method. Interestingly, most of the samples exhibited a cellular architecture. Bandgap engineering of BFO nanoparticles was achieved by co-doping with Nd and Co. Under illumination with ultraviolet light, the concentration of methylene orange increased. The sample of Bi_0.95Nd_0.05Fe_0.85Co_0.15O₃ produced a small amount of hydrogen (8.88molg^-1 after 1.5;h), but the other samples did not produce detectable levels of hydrogen. In this research, the production of hydrogen occurred under illumination by ultraviolet light, demonstrating the splitting of pure water without the use of a sacrificial reagent. A possible reason for this is that the conduction and valence band edges of BiFeO₃ straddle the water redox potential. Consequently, it is possible to realize unassisted water splitting using BFO. The ferromagnetism of all samples increased linearly with the increase of dopant concentration, and the residual magnetization of the Bi_0.95Nd_0.05Fe_0.80Co_0.20O₃ sample reached to 0.679 emu g⁻¹. Moreover, the magnetic properties of bismuth ferrite and Nd/Co Co-doped bismuth ferrite photocatalyst were also investigated to show the simple separation. These results demonstrate that BFO nanoparticles have potential applications in photocatalytic hydrogen production without the use of a sacrificial reagent.

Introduction

Multiferroics have attracted the attention of researchers worldwide in recent years is because they exhibit a magnetoelectric coupling effect and have broad application prospects in information storage, electronic devices, and sensors. Bismuth ferrite (BiFeO₃, or BFO) stands out among multiferroics because of its magnetic and strong ferroelectric properties at room temperature (Dutta et al. 2010). The ferroelectricity of BFO is related to the Bi 6s lone electron pair at the A site, and the magnetic properties are related to the space-modulated spin structure. However, the cycloidal spin structure with a period of 62 nm leads to BFO having weak magnetic properties (Puhan et al. 2019). When other elements are substituted for the A and B positions in BFO nanoparticles, there is a significant effect on the lattice structure and the Bi 6s lone pair, thus affecting ferroelectricity and ferromagnetism (Layek et al. 2013). It has been reported that the incorporation of Nd³⁺ at the A site of BFO can alter the ferromagnetism of the material (Yuan et al. 2006). Wang et al. noted that the incorporation of Nd³⁺/Mn²⁺ at the A and B positions of BFO affects its structure and properties, and the incorporation of Nd³⁺ induces a phase transition from an R3c crystal structure to Pnma (Wang et al. 2019). Co-doping with Co and Eu successfully enhances the magnetic and dielectric properties of BFO nanoparticles. The significant enhancement of the saturation magnetization (M_s) upon co-doping with Eu and Co may be due to the destruction of the space-modulated spin structure (Das et al. 2012).

In addition, BFO has a narrow band gap (2.2 eV) and excellent chemical stability, and can be used as a photocatalyst to degrade organic pollutants and decompose water (Luo and Maggard, 2006; Li et al. 2010; Cheng et al. 2016). Bismuth Ferrite nanohybrids display improved photocatalytic activity and degradative ability (Fatima et al. 2020; Fatima et al., 2018; Iqbal et al. 2019a; Iqbal et al. 2019b). Compared with photoelectrochemical (PEC) water splitting, the photocatalytic dissociation of water has many advantages, such as being suited to splitting water of a nearly neutral pH in a one-step process without the need for an applied external bias. However, unassisted overall water splitting under a single-absorber photocatalytic process must achieve the following two conditions: 1) the valence and conduction gap edges of this photocatalyst must astride across the water oxidation (redox) and proton reduction and potentials; 2) this photocatalyst must possess a adequate narrow bandgap to absorb a majority of the solar spectrum (Fang and Shangguan, 2019). Due to such rigorous requirement, there are very few suitable photocatalyst. Moreover, efficient charge separation is a critical issue. Bismuth ferrite is one kind of special functional material that can be modified to exhibit the required space charge region, with an accumulation layer and a depletion layer, by using n-type and p-type doping. The band bending in this space charge region can be tuned to be favorable for the separation of excited electrons and holes. In addition, for applications in the photocatalyst field, one advantage of BiFeO₃ is its excellent magnetic properties. It is essential to separate photocatalyst after they have been synthesized. Generally, coagulation, flocculation, and sedimentation are widely used as separation processes, but they are complex and expensive (Fang and Shangguan, 2019; Reddy et al. 2019). The separation process is greatly simplified if the photocatalyst is magnetized, as this allows separation by the application of an external magnetic field (Yang et al., 2018).

Chowdhury et al. reported unassisted high-efficiency splitting of pure water using a BiFeO₃ diode (Chowdhury et al. 2018). Cheng et al. reported the production of hydrogen through the use of a ferroelectric polarization-mediated Si/STO/BiFeO₃ tandem photocathode (Cheng et al. 2016). In this work, however, we wanted to prepare a material that could directly produce hydrogen through splitting water solely under illumination, without the use of a sacrificial agent or an external bias field. To achieve this, we simultaneously doped Nd³⁺ and Co²⁺ into the A and B sites of BFO, respectively. Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles with different doping concentrations were synthesized using a sol-gel method. The effects of doping on the morphology, structure, magnetic properties, and bandgap of BFO nanoparticles were investigated.

Experiment

The Bi_1-xNd_xFe_1-yCo_yO_{3 (}x = 0, 0.05; y = 0, 0.05, 0.10, 0.15, 0.20) as abbreviated BFO(BiFeO₃), BNFO (Bi_0.95Nd_0.05FeO₃), BNFCO-5 (Bi_0.95Nd_0.05Fe_0.95Co_0.05O₃), BNFCO-10 (Bi_0.95Nd_0.05Fe_0.90Co_0.10O₃), BNFCO-15 (Bi_0.95Nd_0.05Fe_0.85Co_0.15O₃), BNFCO-20 (Bi_0.95Nd_0.05Fe_0.80Co_0.20O₃) nanoparticles were synthesized by two solvent sol-gel method, all reagents were of analytical grade. Bismuth nitrate pentahydrate (99.0% purity 0.01 mol) and neodymium nitrate hexahydrate (99.0% purity) are dissolved in a mixture of ethylene glycol (20 ml) and acetic acid (20 ml) in a certain proportion, stirred for 90 min at room-temperature. Since the Bi element is easily volatilized by heat, it is excessively 5%. Ferric nitrate (98.5% purity) and cobaltous nitrate (99.0% purity) are dissolved in a mixture of ethylene glycol (20 ml) and acetic acid (20 ml) in a certain proportion, stirred for 90 min at room-temperature. After this, both solutions were mixed and put under constant stirring for 3 h at room-temperature. Afterward, the precursor solution was dried at 80°C for 24 h and then grinded into powder. The powder was raised to 600°C at 2°C/min and calcined at 600° C for 3 h to form Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles.

The phase constitutions and structure of the prepared samples were characterized by an X-ray diffraction (XRD) in the range of 2θ = (20⁰–60⁰) and Raman scattering spectra. The morphology of the prepared samples was determined using scanning electron microscopy (SEM). The band-gap of the prepared samples was studied by UV-vis diffused reflectance spectra via UV-vis spectrophotometer. Room temperature magnetic properties of prepared samples were studied by vibrating sample magnetometer (VSM) in the −20 to 20 kOe field range.

The abilities of photocatalytic hydrogen production were conducted in an evacuation system (Beijing Perfect Light Technology Co., Ltd. China) and a Labsolar-III AG closed gas circulation, of which the system maintained the photo-reaction temperature at 5°C with a low-temperature thermostat bath (Poly Science, United States). The nanoparticles were irradiated by the simulated sunlight, which is A 300 W Xennon lamp (PLS-SXE-300UV, Beijing Trusttech Co. Ltd., China) with a UV-cutoff filter (providing visible light λ ≥ 420 nm). a volume of 1.5 ml of gas was hourly sampled and measured by a gas chromatography equipped with a thermal conductivity detector (TCD) and a 5 Å molecular sieve column, so as to identify and quantify the production of gas. At the same time, inert gas argon (Ar) was applied as the carrier gas. The implementation details and schematic diagram of experimental process is shown in Figure 1.

FIGURE 1

Results and Discussions

The X-ray diffraction (XRD) profiles of different samples are showed in Figure 2. From the result of the XRD patterns, all samples have perovskite structure and no other phases such as Bi₂Fe₄O₉ and Bi₂₅FeO₄₀ could be detected. The diffraction peaks of doped BFO nanoparticles had a tendency to shift toward higher diffraction angles when compared with the peaks of pure BFO. This is because the doped ionic radius is small and the unit cell volume is reduced, which shifts the diffraction peaks to higher diffraction angles. Similar phenomena are observed when other rare earth elements are incorporated (Lü et al. 2017) . As the doping ratio increases, the double diffraction peaks of the sample gradually merge into a single peak in the diffraction angle (2θ) range 31°33°. These results indicate that structural changes have occurred in the after doping.

FIGURE 2

Figure 3 shows the Raman spectra of different samples at 300 K. In our BFO samples, the first four strong peaks at 146.00, 175.25, 213.25, and 435.25 cm⁻¹ manifest the A₁-1, A₁-2, A₁-3, and A₁-4 modes, and the remaining six small peaks at 283.25, 333.50, 370.00, 472.50, 558.50, and 611.25 cm⁻¹ are assigned to the E-2, E-3, E-4, E-5, E-6, and E-7 modes, respectively. Table 1 lists the values found in the literature and in this study for the BFO samples. The difference in the peak positions observed by different researchers may be caused by different preparation methods.

FIGURE 3

As the doping ratio increases, we can see that the peak position of the A₁-1 mode gradually shifts towards the blue and the relative peak intensity gradually decreases. It is considered that the 472.5 cm⁻¹ mode in the BFO Raman spectrum corresponds to the bending vibration mode of the Fe–O bond, and the 558.5 cm⁻¹ mode corresponds to the stretching vibration mode of the Fe–O bond. The peak intensity of the 472.5 cm⁻¹ mode is gradually increased after the incorporation of Nd³⁺ and Co²⁺, indicating that the bond angle of the Fe–O bond changes after the impurity is incorporated. The A₁-1 mode of the Bi_0.95Nd_0.05Fe_0.80Co_0.20O₃ (BNFCO-20) sample disappeared, while a new Raman mode appeared at 677.75 cm⁻¹. This apparent difference indicates a structural phase change in the sample. The structural phase transition destroys the helical spin structure, which enhances the magnetic properties of the sample. The residual magnetization of the BNFCO-20 sample measured in this experiment is 0.68 emu g⁻¹ higher than that of the undoped BFO sample.

Figure 4 shows the surface morphological features of the Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles by using scanning electron microscopy (SEM). As can be seen, the prepared samples are stacked together to form a regular honeycomb shape. This did not occur in previous experiments. When Nd³⁺ and Co²⁺ are incorporated, the size of the Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles gradually becomes smaller, which is in good agreement with the XRD results. The decrease in grain size destroys the cycloidal spin period (62 nm) of the BFO structure, which is consistent with the trend of the magnetic properties of the samples. This agglomeration of the nanoparticles may affect their photocatalytic properties.

FIGURE 4

Figure 5 shows UV–Visible spectra of the Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles. Compared with pure BFO, the absorption spectra of all doped samples shown a clear red shift. In this paper, the band gap of all samples is calculated by using Eq. 1.

FIGURE 5

As shown in Table 1, the band gap energy of BFO is greatly reduced when Nd³⁺ and Co³⁺ are incorporated. The band gap energy of the un-doped BFO sample was 2.063 eV, which is in good agreement with the previously reported values. The reason for the reduction in the band gap of all Bi_1-xNd_xFe_1-yCo_yO₃ nanoparticles samples may be due to the Fe-O octahedral distortion of the molecular orbitals (Sati et al. 2014). The incorporation of metal ions produces a degeneracy of the impurity level, causing the acceptor level or the donor level to move to reduce the forbidden band width (Chen et al. 2010). The results show that the presence of Nd³⁺ and Co²⁺ can reduce the band gap of BFO and make it better to absorbing visible light.

The photocatalytic activity of pure and co-doped BFO nanoparticles was studied by the degradation of 30 mg of the powder samples dissolved in 50 ml deionized water along with the addition of 0.01 g/L methylene orange (MO). The degradation of MO with the BFO nanoparticles in the dark condition for 15 h is similar to that of the blank test, which demonstrates that the absorption of RhB on the BFO is limited after the adsorption-desorption equilibrium was reached. From Figure 5B, we can see that the value of methylene orange (MO) peak is not decreased gradually but increased, which is special and interesting for normal photocatalytic degradation . The only possible reason is that the water is splitted and reduced under the illuminating of ultraviolet visible light, which lead to the increase of intensity of methylene orange. However, another possible reason must excluded is that the water might be evaporated under the illuminating of ultraviolet visible light. Consequently, the reaction of photocatalytic degradation without the catalyst under the same condition is conducted, which is prepared to quantitate the evaporative capacity of water during the whole reaction. The results are showed in the Figure 5C. Compared with these two group data as showed in Figures 5B,C we could draw a conclusion that the evaporation of water indeed take place during the illuminating of ultraviolet visible light, but the splitting of water without any external field bias and unassisted overall water splitting indeed occurs. The decrease is 4.5% for the blank group but the increase reaches the 7.1%. In order to further prove the splitting of water, the online detection of production of hydrogen were conducted under the protection of N₂ atmosphere. As showed in Figure 5D, the amount of hydrogen production of Bi_0.95Nd_0.05Fe_0.85Co_0.15O₃ reached 8.88umol/g after 1.5 h, however the other samples could not be detected the production of hydrogen. In order to easily understand the strength for production of hydrogen gas using doped BFO, a comparative result in form of table is shown in Table 3.

On the basis of above results, a tentative schematic illustration of the energy band diagram of the Nd and Co co-doped BFO photocatalyst is depicted in Figure 6, to explain how the photo-generated electrons in surface contribute to the hydrogen production. As we know the possible reason of unassisted water splitting with BFO is that the valence band edge and the conduction band edge of BFO straddle the water redox potentials. At the same time, the valence band edge and the conduction band edge should bend in favor of the separation of the excited electrons and holes. Firstly the band gap of Bi_0.95Nd_0.05Fe_0.85Co_0.15O₃ is 1.78 eV and the potential of water is 1.23 eV, which the valence band edge and the conduction band edge of BFO just straddle the water redox potentials. There are report that the optimum band gap of BFO for hydrogen production is 1.77 eV (Vishwakarma et al. 2017). A suitable band gap size is beneficial and necessary. The transfer of mobile charge carriers between the semiconductor and the contact phase produces a space-charge layer. Figure 6 illustrates the space-charge layers produced from the mobility of charge across a semiconductor solution interface (Linsebigler et al. 1995) . The space-charge layer formed is a depletion layer, and the bands bend upward toward the surface. Because of the positive charges existence on the interface, the accumulation layer is formed and the bands would bend down in the interface. Bands with curved interfaces are stuck at either end of the water band gap like pommel horses. Because BFO is semiconductor material, when semiconductor BFO absorbs ultraviolet-light energy, electrons are excited to the conduction band (CB), while holes are present in the valence band (VB). The band curvature of the interface prevents the recombination of electrons and holes. The electrons present in the CB with protons to generate hydrogen, and the holes combine with reductive reactants to create oxidative products (Shen et al. 2015; Reddy et al. 2019). To sum up, the possible reason for this is that the conduction and valence band edges of BiFeO3 straddle the water redox potential. Consequently, it is possible to realize unassisted water splitting using BFO.

FIGURE 6

Whether the bands are bent in depletion or in accumulation, the width of the space-charge region is proportional to the Debye length (Guo et al. 2010; Fang and Shangguan, 2019) L_D.Where ε₀ is the permittivity of free space, ε_r is the dielectric constant of the material, and N_D is the donor density. According to Eq. 2, we can see that an increase in the dielectric constant can increase the Debye length and, therefore, the width of the space-charge region (Guo et al. 2010).

The magnetic hysteresis (M-H) loops of the samples at room temperature are shown in Figure 6. It was found that doping Nd³⁺ and Co²⁺ had a significant effect on the ferromagnetic properties of BFO nanoparticles. It can be seen from Figure 7A that the magnetic hysteresis loop of the un-doped BFO is almost a straight line. This phenomenon proves that the prepared BFO sample does not contain other impurity phases. As shown in Figure 6, as the amount of Co²⁺ doping increases, the magnetic hysteresis loop of the sample becomes more and more obvious, and the residual magnetization and saturation magnetization gradually increase. The magnetization can be increased by increasing the doping amount of Co²⁺, which may be mainly caused by the following two aspects. First, as the doping amount increases, the crystal structure gradually changes and the Pnma phase begin to appear in the parent R3c phase. The content of R3c and Pnma is 77.73 and 22.27% respectively in the sample Bi_0.95Nd_0.05Fe_0.85Co_0.15O₃. These results came from the Rietveld refinement (not shown). These changes cause the spin coupling of the cycloid to be gradually broken and increase the magnetization. Second, as the incorporation of Co increases, the cycloid spin cycle with a grain size smaller than that of the BFO structure destroys its periodicity, resulting in an increase in magnetization (Reddy et al. 2018). It is found from Figure 7B that an exchange bias effect occurs after the incorporation of 5% of Nd³⁺, that is, the M-H ring undergoes an asymmetric movement along the H axis. The exchange bias effect is due to the coexistence of anisotropic FM and AFM domains (Wu et al. 2018). These results suggested that the magnetic properties of BFO nanoparticles can be enhanced by Co²⁺ and Nd³⁺ doping, which means that the photocatalyst can be separated easily by applying an external magnetic field.

FIGURE 7

Cellular architecture of Nd and Co co-doped in BFO nanoparticles, fabricated by two-solvent sol-gel method, are demonstrated as spectral photocatalytic that perform unassisted high efficiency directly produce hydrogen through splitting the water due to the optimum band-gap engineering of BFO nanoparticles was controlled by co-doping of Nd and Co. So the new material that could directly produce hydrogen through splitting the water only under the illuminating without any sacrificial agent without external bias field is urgent. Hence, Cellular architecture of Nd and Co co-doped in BFO nanoparticles, fabricated by two-solvent sol-gel method, are demonstrated as spectral photocatalytic that perform unassisted high efficiency directly produce hydrogen through splitting the water due to the optimum band-gap engineering of BFO nanoparticles was controlled by co-doping of Nd and Co.

References

• 1

  ChenX.ShenS.GuoL.MaoS. S. (2010). Semiconductor-based photocatalytic hydrogen generation. Chem. Rev.110 (11), 6503–6570. 10.1021/cr1001645

  • CrossRef
  • Google Scholar
  • View reference in article

• 2

  ChengX.ShenH.DongW.ZhengF.FangL.SuX.et al (2016). Nano-Au and ferroelectric polarization mediated Si/ITO/BiFeO₃Tandem photocathode for efficient H₂ production. Adv. Mater. Inter.3 (19), 1600485. 10.1002/admi.201600485

  • CrossRef
  • Google Scholar
  • View reference in article

• 3

  ChowdhuryF. A.TrudeauM. L.GuoH.MiZ. (2018). A photochemical diode artificial photosynthesis system for unassisted high efficiency overall pure water splitting. Nat. Commun.9 (1), 1707. 10.1038/s41467-018-04067-1

  • CrossRef
  • Google Scholar
  • View reference in article

• 4

  DasK.SarkarB.GhoshS.DeS.SinhaG.LahtinenJ. (2012). Enhanced magnetic and dielectric properties of Eu and Co co-doped BiFeO₃ nanoparticles. Appl. Phys. Lett.101 (4), 42401. 10.1063/1.4738992

  • CrossRef
  • Google Scholar
  • View reference in article

• 5

  DuttaD. P.JayakumarO. D.TyagiA. K.GirijaK. G.PillaiC. G. S.SharmaG. (2010). Effect of doping on the morphology and multiferroic properties of BiFeO3 nanorods. Nanoscale2 (7), 1149. 10.1039/c0nr00100g

  • CrossRef
  • Google Scholar
  • View reference in article

• 6

  FangW.ShangguanW. (2019). A review on bismuth-based composite oxides for photocatalytic hydrogen generation. Int. J. Hydrog. Energ.44 (2), 895–912. 10.1016/j.ijhydene.2018.11.063

  • CrossRef
  • Google Scholar
  • View reference in article

• 7

  FatimaS.AliS. I.IqbalM. Z.RizwanS. (2020). Congo red dye degradation by graphene nanoplatelets/doped bismuth ferrite nanoparticle hybrid catalysts under dark and light conditions. Catalysts10 (4), 367. 10.3390/catal10040367

  • CrossRef
  • Google Scholar
  • View reference in article

• 8

  FatimaS.Irfan AliS.YounasD.IslamA.AkinwandeD.RizwanS. (2019). Graphene nanohybrids for enhanced catalytic activity and large surface area. MRS Commun.9 (1), 27–36. 10.1557/mrc.2018.194

  • CrossRef
  • Google Scholar
  • View reference in article

• 9

  FukumuraH.HarimaH.KisodaK.TamadaM.NoguchiY.MiyayamaM. (2007). Raman scattering study of multiferroic BiFeO3 single crystal. J. Magn. Magn. Mater.310 (2), e367–e369. 10.1016/j.jmmm.2006.10.282

  • CrossRef
  • Google Scholar
  • View reference in article

• 10

  GuoR.FangL.DongW.ZhengF.ShenM. (2010). Enhanced photocatalytic activity and ferromagnetism in Gd doped BiFeO3 nanoparticles. J. Phys. Chem. C114 (49), 21390–21396. 10.1021/jp104660a

  • CrossRef
  • Google Scholar
  • View reference in article

• 11

  IqbalM. A.TariqA.ZaheerA.GulS.RizwanS. (2019a). Ti₃C₂-MXene/Bismuth ferrite nanohybrids for efficient degradation of organic dyes and colorless pollutants. ACS Omega4 (24), 20530–20539. 10.1021/acsomega.9b02359

  • CrossRef
  • Google Scholar
  • View reference in article

• 12

  IqbalM.FatheemaJ.NoorQ.RaniM. (2019b). Co-existence of magnetic phases in two-dimensional MXene. Mater.Today. Chem.16, 100271. 10.1016/j.mtchem.2020.100271

  • CrossRef
  • Google Scholar
  • View reference in article

• 13

  KothariD.ReddyV. R.SatheV.GuptaA.BanerjeeA.AwasthiA. (2008). Raman scattering study of polycrystalline magnetoelectric BiFeO₃. J. Magn. Magn. Mater.320 (3-4), 548–552. 10.1016/j.jmmm.2007.07.016

  • CrossRef
  • Google Scholar
  • View reference in article

• 14

  LayekS.SahaS.VermaH. C. (2013). Preparation, structural and magnetic studies on BiFe_1-xCr_xO₃ (x= 0.0, 0.05 and 0.1) multiferroic nanoparticles. AIP. Adv.3 (3), 032140. 10.1063/1.4799063

  • CrossRef
  • Google Scholar
  • View reference in article

• 15

  LiS.LinY.-H.ZhangB.-P.WangY.NanC.-W. (2010). Controlled fabrication of BiFeO₃ uniform microcrystals and their magnetic and photocatalytic behaviors. J. Phys. Chem. C.114 (7), 2903–2908. 10.1021/jp910401u

  • CrossRef
  • Google Scholar
  • View reference in article

• 16

  LinsebiglerA. L.LuG.YatesJ. T.Jr (1995). Photocatalysis on TiO2 surfaces: principles, mechanisms, and selected results. Chem. Rev.95 (3), 735–758. 10.1021/cr00035a013

  • CrossRef
  • Google Scholar
  • View reference in article

• 17

  LüF. C.YinK.FuK. X.WangY. N.RenJ.XieQ. (2017). Enhanced magnetic and dielectric properties of Y doped bismuth ferrite nanofiber. Ceram. Int.43 (18), 16101–16106. 10.1016/j.ceramint.2017.08.171

  • CrossRef
  • Google Scholar
  • View reference in article

• 18

  LuoJ.MaggardP. A. (2006). Hydrothermal synthesis and photocatalytic activities of SrTiO3-coated Fe2O3 and BiFeO3. Adv. Mater.18 (4), 514–517. 10.1002/adma.200500109

  • CrossRef
  • Google Scholar
  • View reference in article

• 19

  PuhanA.BhushanB.KumarV.PandaH. S.PriyamA.DasD.et al (2019). Tailoring the structural, optical and magnetic properties of BiFeO₃ multiferroic nanoparticles by Ba, Cr co-doping. Mater. Sci. Eng.241, 48–54. 10.1016/j.mseb.2019.02.009

  • CrossRef
  • Google Scholar
  • View reference in article

• 20

  ReddyB. P.SekharM. C.PrakashB. P.SuhY.ParkS. H. (2018). Photocatalytic, magnetic, and electrochemical properties of La doped BiFeO₃ nanoparticles. Ceram. Int.44 (16), 19512–19521. 10.1016/j.ceramint.2018.07.191

  • CrossRef
  • Google Scholar
  • View reference in article

• 21

  ReddyC. V.ReddyK. R.HarishV. V. N.ShimJ.ShankarM. V.ShettiN. P.et al (2019). Metal-Organic Frameworks (MOFs)-based efficient heterogeneous photocatalysts: synthesis, properties and its applications in photocatalytic hydrogen generation, CO₂ reduction and photodegradation of organic dyes. Int. J. Hydrog. Energ.45 (13), 7656–7679. 10.1016/j.ijhydene.2019.02.144

  • CrossRef
  • Google Scholar
  • View reference in article

• 22

  SatiP. C.AroraM.ChauhanS.KumarM.ChhokerS. (2014). Effect of Dy substitution on structural, magnetic and optical properties of BiFeO₃ ceramics. J. Phys. Chem. Sol.75 (1), 105–108. 10.1016/j.jpcs.2013.09.003

  • CrossRef
  • Google Scholar
  • View reference in article

• 23

  ShenL.LuoM.LiuY.LiangR.WuL. (2015). Noble-metal-free MoS₂ co-catalyst decorated UiO-66/CdS hybrids for efficient photocatalytic H₂ production. App. Catal. B.166-167, 445–453. 10.1016/j.apcatb.2014.11.056

  • CrossRef
  • Google Scholar
  • View reference in article

• 24

  SinghM.JangH.JoM.RyuS. (2006). Polarized Raman scattering of multiferroic BiFeO₃ epitaxial films with rhombohedral R3c symmetry. Appl. Phys. Lett.88 (4), 42907. 10.1063/1.2168038

  • CrossRef
  • Google Scholar
  • View reference in article

• 25

  VishwakarmaA. K.TripathiP.SrivastavaA.SinhaA. S. K.SrivastavaO. N. (2017). Band gap engineering of Gd and Co doped BiFeO3 and their application in hydrogen production through photoelectrochemical route. Int. J.Hydrog. Energ.42 (36), 22677–22686. 10.1016/j.ijhydene.2017.07.153

  • CrossRef
  • Google Scholar
  • View reference in article

• 26

  WangY.GuoZ.JiaQ.DongJ.ZhangJ.ChenD. (2019). Effect of Nd/Mn substitution on the structure and magnetic properties of nano-BiFeO3. J. Alloy. Compd.786, 385–393. 10.1016/j.jallcom.2019.01.369

  • CrossRef
  • Google Scholar
  • View reference in article

• 27

  WuH.XueP.LuY.ZhuX. (2018). Microstructural, optical and magnetic characterizations of BiFeO3 multiferroic nanoparticles synthesized via a sol-gel process. J. Alloy. Compd.731, 471–477. 10.1016/j.jallcom.2017.10.087

  • CrossRef
  • Google Scholar
  • View reference in article

• 28

  YangY.KangL.LiH. (2018). Enhancement of photocatalytic hydrogen production of BiFeO₃ by Gd³⁺ doping. Ceram. Int.45 (6), 8017–8022. 10.1016/j.ceramint.2018.12.150

  • CrossRef
  • Google Scholar
  • View reference in article

• 29

  YangY.SunJ. Y.ZhuK.LiuY. L.ChenJ.XingX. R. (2009). Raman study of BiFeO3 with different excitation wavelengths. Phys. B.404 (1), 171–174. 10.1016/j.physb.2008.10.029

  • CrossRef
  • Google Scholar
  • View reference in article

• 30

  YuanG. L.LiuJ. M.LiuZ. G. (2006). Structural transformation and ferroelectromagnetic behavior in single-phase Bi_1-xNd_xFeO₃ multiferroic ceramics. Appl. Phys. Lett.89 (5), 052905, 10.1063/1.2266992

  • CrossRef
  • Google Scholar
  • View reference in article

• 31

  YuanG. L.OrS. W.ChanH. L. W. (2007). Raman scattering spectra and ferroelectric properties of Bi1−xNdxFeO3 (x=0-0.2) multiferroic ceramics. J. Appl. Phys.101 (6), 064101. 10.1063/1.2433709

  • CrossRef
  • Google Scholar
  • View reference in article