Abstract
Dopamine is one of the most important neurotransmitters and plays a crucial role in various neurological, renal, and cardiovascular systems. However, the abnormal levels of dopamine mainly point to Parkinson’s, Alzheimer’s, cardiovascular diseases, etc. Hydroxyapatite (HAp), owing to its catalytic nature, nanoporous structure, easy synthesis, and biocompatibility, is a promising matrix material. These characteristics make HAp a material of choice for doping metals such as cobalt. The synthesized cobalt-doped hydroxyapatite (Co-HAp) was used as a colorimetric sensing platform for dopamine. The successful synthesis of the platform was confirmed by characterization with FTIR, SEM, EDX, XRD, TGA, etc. The platform demonstrated intrinsic peroxidase-like activity in the presence of H2O2, resulting in the oxidation of 3,3′,5,5′-tetramethylbenzidine (TMB). The proposed sensor detected dopamine in a linear range of 0.9–35 μM, a limit of detection of 0.51 µM, limit of quantification of 1.7 µM, and an R2 of 0.993. The optimization of the proposed sensor was done with different parameters, such as the amount of mimic enzyme, H2O2, pH, TMB concentration, and time. The proposed sensor showed the best response at 5 mg of the mimic enzyme, pH 5, 12 mM TMB, and 8 mM H2O2, with a short response time of only 2 min. The fabricated platform was successfully applied to detect dopamine in physiological solutions.
1 Introduction
Dopamine is an important neurotransmitter in the human body, and it is implicated in various debilitating diseases. It plays a central role in the renal, neurological, cardiovascular, hormonal, and metabolic systems (). Dopamine plays an important role in the brain’s ability to receive signals, and low levels of it can cause a variety of neurological diseases, including epilepsy, schizophrenia, and Parkinson’s disease (). Its normal level ranges from 1.3 to 2.6 μM. Beyond the given limits, it can point to heart diseases, Parkinson’s disease, cardiovascular problems (), abnormal thyroid hormone levels, neuromuscular problems, and schizophrenia (). The correlation between dopamine and several devastating and fatal illnesses underscores the need to sense it accurately, selectively, and cost-effectively.
In recent years, various sophisticated methods have been reported for the sensing of dopamine, such as fluorescence (), electrochemistry (), chemiluminescence (), high-performance liquid chromatography (), electrochemiluminescence (), etc. Despite their merits, the majority of these techniques require complex sample pretreatment. These techniques are not only expensive to acquire and sustain but also laborious and time-consuming. The need for highly skilled operators is another major limitation of the aforementioned techniques. Background interference and low reproducibility have also been reported for the mentioned methods. These shortcomings associated with the reported techniques put a question mark on their viability as techniques of choice for dopamine sensing and biosensing. Therefore, much work needs to be done to provide straightforward, quick, and effective techniques for the high-sensitivity detection of dopamine. Colorimetric assays offer a viable alternative in comparison to the above-stated techniques. They have attracted considerable attention owing to their naked-eye observation capability, easy operation, and lower cost (). Moreover, the naked eye observation can further be confirmed through a UV-Vis spectrophotometer for accurate quantification (). Natural enzyme-based sensing platforms have been used for the detection of various biomarkers, but they are expensive, have a low shelf life, are difficult to handle, are temperature-sensitive, and lose their activity under harsh conditions ().
The emergence of mimetic enzymes (nanozymes) is a new viable alternative to overcome the limitations of natural enzymes (). Nanozymes are artificial enzymes based on nanomaterials that mimic the role of natural enzymes. Their superior catalytic properties and ability to endure harsh conditions have impressed researchers (). They are also used in bioassays (), as industrial catalysts (), in food processing (), agriculture (), and environmental monitoring (). Mimic enzymes offer the advantages of lower cost, high stability, a large surface area, and easy operation (). Transition metal-based enzyme mimics are the most effective class of artificial enzymes owing to their high conductivity and different oxidation states. It has been reported that Co−Fe3O4/graphene (), Co3O4@NiO (), CoFe2O4/CoS (), and CoS nanospheres () function as good peroxidase mimetic catalysts with favorable catalytic activity and high stability. Cobalt nanoparticles have been extensively used as nanozymes for sensing and catalytic activities due to their high stability and low cost. However, the problem of agglomeration limits their use as reliable players in the fabrication of sensing platforms for bioanalysis (). Researchers have used various strategies to overcome the problem of agglomeration in metal nanoparticles.
For this purpose, in most cases, metal nanoparticles are mixed with other functional elements to provide a synergistic effect. Different matrix materials have been used to achieve the deagglomeration of the metal nanoparticles. Hydroxyapatite (HAp) has fantastic osteointegrative and osseoconductive properties. It is a nanoporous substance that is biocompatible, catalytic (owing to the presence of basic and acidic moieties), bioactive, degradable, and ubiquitous (). These qualities make it a popular candidate for its use as a matrix material for the fabrication of metal-based mimic enzymes (). It can easily be synthesized from waste materials such as bovine bone (), fish bone (), coral (), egg shells, etc (). HAp is a promising material for the fabrication of such platforms due to its exceptional ability to withstand a wide range of cationic and anionic substituents (). Doping with different kinds of metal ions improves the physical, chemical, and biological properties of HAp ().
In this work, we have used cobalt-doped HAp nanocomposite as a peroxidase mimic for the colorimetric sensing and biosensing of dopamine for the first time. Co-doped HAp, as a mimic enzyme, can catalyze the oxidation of TMB with the assistance of H2O2. The colorless solution changes to a blue-green product in the presence of H2O2, acting as an oxidizing agent. This transformation can be observed with the naked eye and confirmed with a UV-Vis spectrophotometer. As dopamine was added to the reaction mixture, it reduced the oxidized TMB to TMBred, with the consequent disappearance of the blue-green color to colorless. The fabricated sensing platform was successfully applied in a physiological solution for the sensing of dopamine.
2 Experimental
2.1 Chemicals and materials
CoCl2.6H2O, dopaime, NaOH, HCl, 3,3′,5,5′-Tetramethylbenzidine (TMB), DMSO, H2O2, 35%, and NaH2PO4 were purchased from Sigma-Aldrich. Double-distilled water was used for the preparation of solutions. Bio-World-provided phosphate-buffered saline (pH 7.4) was used in the reactions as a medium.
2.2 Instrumentation
Using Fourier transform infrared spectroscopy on the Cary 630 FTIR spectrometer (Agilent Technologies, Danbury, Connecticut, USA), the distinctive peaks of HAp and Co-HAp were characterized. The materials’ FTIR spectra were obtained within the given range of 4,000–400 cm−1. The parameters set for FTIR experiments were 256 scans per sample and 4 cm−1 resolution. Scanning electron microscopy linked to energy dispersive X-ray spectroscopy (SEM-EDX) using a TESCAN VEGA (LMU) SEM with an INCAx-act (Oxford Instruments) EDX attachment working at 20 kV was used to analyze the morphology of the produced materials. The produced materials’ phase was investigated using X-ray diffraction (Shimadzu, LabX XRD-6100 with Cu-Kα radiation) with a scan range of 10°–80°. The voltage for acceleration was set at 30 kV, while the current was set at 20 mA. Cu Kα radiations were utilized with a monochromatic wavelength of (λ = 1.5405 Å). Using JCPDS, file No. 04–0783, the phase of the produced HAp and Co-HAp nanocomposite was identified. Under nitrogen gas flow, thermal gravimetric analysis (TGA) was performed at temperatures between 50°C and 800°C at a heating rate of 10°C/min. Using a UV-Vis spectrophotometer (Shimadzu, UV, 1,800, Japan), absorption spectra were captured.
2.3 Preparation of HAp from waste bones
The waste bones of goats were used to prepare HAp. The bones were boiled for two to 3 hours to remove the remains of organic components. To ensure further cleaning, the bones were treated with an acetone solution (70% v/v solution in water) for 3 hours. Water was used to rinse the bones several times. The treated bones were dried for 24 h at 100°C in an oven. The dried bones were pulverized with the help of a pestle and mortar. To obtain the desired HAp, calcination was carried out at 800°C for 3 hours in a furnace (). The work received ethical approval from the concerned forum of Kohat University of Science and Technology, KUST, Kohat via No. KUST/Ethical Committee/1023.
2.4 Preparation of Co-HAp nanocomposite
Cobalt (II) chloride hexahydrate (CoCl2.6H2O) was mixed with the synthesized HAp powder for doping at a weight ratio of 1:9, respectively. The ingredients were mixed with a pestle and mortar to form a homogenous mixture. The mixture was calcined at 800°C for 3 hours in a furnace. The overall process for the preparation HAp and Co-HAp is shown in the Scheme 1.
SCHEME 1
2.5 Dopamine sensing through Co-HAp nanocomposite
The synthesized Co-HAp nanocomposite (5 mg) was suspended in a 500 μL PBS solution. At the same time, 100 μL of TMB solution (12 mM in DMSO) and 100 μL of H2O2 (8 mM) were added to the solution mixture. The catalytic ability was measured by recording the changes in absorbance over time and acquiring the absorption spectra. TMB was used as a substrate for the colorimetric detection of dopamine, and the peroxidase-like activity was measured. The expected colorimetric change was confirmed using both the naked eye and UV-Vis spectra.
In order to validate the catalytic role of Co-HAp in the reaction system, the sensing of dopamine was performed under different conditions. These include TMB + Co-HAp, TMB + H2O2, and TMB + H2O2+Co-HAp.
2.6 Sensing of dopamine in physiological solution
The physiological solution was utilized to detect dopamine. In this solution, three different concentrations of dopamine were spiked. In the prepared samples, colorimetric detection of dopamine was performed and confirmed by a UV-Vis spectrophotometer ().
3 Results and discussion
3.1 Characterization of HAp and Co-HAp nanocomposite
3.1.1 FTIR analysis of the prepared HAp and Co-HAp nanocomposite
Figure 1i demonstrate the FTIR spectra of the pure HAp and Co-HAp nanocomposite. The FTIR spectrum of the synthesized HAp nanoparticles indicated peaks at 568, 1030, 1430, and 3,627 cm−1. The peak around 568 cm−1 represents the bending mode of phosphate functionality, while the band at 1030 cm−1 indicates the stretching mode of the phosphate moiety. The peak in the range of 1400–1600 cm−1 shows the presence of a carbonate group in the HAp. The peak at 3,627 cm−1 represents the hydroxyl group that comes from moisture. Co-HAp nanocomposite indicated peaks at 565 cm−1 and 1025 cm−1. These peaks represent the phosphate functionality in the synthesized nanocomposite (). There is no more peak of carbonate functionality due to the removal of carbonyl functionality in the form of carbon dioxide. However, there is no significant difference between the pure and Co-doped HAp ().
FIGURE 1
3.1.2 XRD analysis of the prepared HAp and Co-HAp
Figure 1ii displays the XRD pattern of the synthesized HAp and Co-HAp. Using the JCPDS database Card-No. (09–0432), (), the distinct diffraction peaks were compared based on the anatase HAp and Co-HAp phases. According to the standard data sheet the XRD pattern of the doped samples 1 (B) was found to be comparable to that of crystalline HAp (Ca10(PO4)6(OH)2). With the exception of a minor widening of the peaks at 32°, 33°, and 34° 2θ, the XRD profiles of the doped HAp did not change significantly from those of pure HAp and did not show any new peaks belonging to cobalt. The probable anionic replacement of OH ions in the HAp by chloride ions of cobalt chloride, in addition to the replacement of calcium by cobalt, might be the cause of this drop in crystallinity. Crystal lattice distortion, crystallite size, and percentage crystallinity are the factors that influence peak broadening (). Using the Scherrer equation for the anatse phase of HAp and Co-HAp and the most intense peak, the average particle size was determined (). The average crystal sizes of the anatase phases of HAp and Co-HAp were estimated to be about 38 and 32 nm, respectively.
3.1.3 SEM analysis of the prepared HAp and Co-HAp
Figure 1iii represents the SEM image of HAp and Co-HAp nanocomposite (iv). The HAp and Co-HAp nanocomposites show a spherical morphology. A decrease in particle size was observed with the doping of cobalt into the HAp structure, which increases its surface area. Both pure and doped HAp show nanoporous structures, which can be helpful in providing the necessary surface area for catalytic reactions.
3.1.4 EDX analysis of prepared HAp and Co-HAp
Figure 1v, vi; Table 1 show the elemental composition of HAp and Co-HAp. The EDX spectrum of pure HAp shows the presence of calcium, oxygen, and phosphorus in the weight percentage of 37.78, 49.97, and 12.25, respectively, as shown in Table 1. Whereas Co-HAp, along with the already present elements calcium (32.59%), oxygen (45.32%), and phosphorus (16.0%), shows the presence of chlorine and cobalt in the weight percentages of 2.19 and 3.90, respectively. This confirms the successful doping of Co on the surface of the synthesized HAp.
TABLE 1
| Element | HAp | Co-Hap | ||
|---|---|---|---|---|
| Weight % | Atomic % | Weight % | Atomic % | |
| P | 12.25 | 8.86 | 16.00 | 12.04 |
| Ca | 37.78 | 21.13 | 32.59 | 18.59 |
| O | 49.97 | 70.01 | 45.32 | 66.02 |
| Cl | --- | --- | 2.19 | 1.44 |
| Co | --- | --- | 3.90 | 1.91 |
| Total | 100.00 | 100.00 | 100.00 | 100.00 |
EDX analysis by weight of the synthesized HAp and Co-HAp nanocomposite.
3.1.5 TGA analysis of prepared HAp and Co-HAp
In order to ascertain the performance of the fabricated platform in harsh thermal conditions, it is essential to determine its thermal stability. Figure 1vii shows the thermal gravimetric analysis study of the synthesized HAp and Co-HAp nanocomposite. The TGA of pure HAp from 200 to 400°C is 0.601% weight loss, and from 500 to 800°C, the weight loss is 1.612%. The overall weight loss in pure HAp is 2.213%. The TGA of Co-HAp weight loss is 1.172%; it is from 500 to 800°C. There is no considerable weight loss in Co-HAp because HAp is already thermally stable even at higher temperatures.
3.2 Proof of catalytic activity of the mimic enzyme
The Co-HAp nanocomposite demonstrated improved peroxidase-like catalytic activity. Using the peroxidase substrate TMB and H2O2, the peroxidase-like catalytic activity of the Co-HAp nanocomposite was investigated. The shift in absorbance of the oxidized TMB (TMBoxi) at 652 nm was monitored to observe the progress of the reaction. It is clear from Figure 2 that there is no oxidation when the TMB and Co-HAp are present only in the system. There is a very little oxidation of TMB when H2O2 is present. However, the combination of H2O2 and Co-HAp, significant TMB oxidation of takes place (). It is clearly evident from this that H2O2 and Co-HAp are both necessary for the oxidation of TMB. This suggests that the catalyst accelerates the oxidation of TMB in the presence of H2O2 by exhibiting peroxidase-like activity.
FIGURE 2
3.3 Colorimetric sensing of dopamine
The fabricated sensing platform, i. e., Co-HAp nanocomposite (5 mg), was used for dopamine colorimetric sensing, with TMB serving as a chromogenic substrate. In a typical experiment, 100 µL of hydrogen peroxide (9 mM) was combined with 100 µL of TMB (12 mM) in 500 µL of PBS solution. The color changed from transparent to blue-green, with a visible colorimetric change (A). After the addition of 100 µL of dopamine (35 µM), the blue-green color changed to transparent (B) due to the reduction of oxidized TMB, as confirmed by the UV-Vis spectrophotometer. Inset Figure 3 shows both the colorimetric change and the UV-Vis spectra.
FIGURE 3
3.4 Sensing mechanism of dopamine via Co-HAp nanocomposite
The mimic enzyme (Co-HAp nanocomposite) can work as an excellent platform for the sensing of dopamine. In this process, the oxidizing potential of hydrogen peroxide assisted the mimic enzyme in the oxidation of TMB. A visible colorimetric change to a blue-green color occurs, indicating the oxidation of TMB. Upon the addition of dopamine, the reaction complex changes from blue-green to transparent. This colorimetric change was confirmed through a UV-visible spectrophotometer. The catalytic action was based on a remarkable color change from colorless. The oxidation of TMB to a blue-green color is mediated by a hydroxyl radical that is generated as a result of hydrogen peroxide breakdown assisted by the mimic enzyme. The generated hydroxyl free radical removes the electron from the amino group of the TMB and oxidizes it. Here, the OH free radical acts as an oxidizing agent, and the resulting oxidized TMB gives a blue-green color to the reaction mixture. In reverse, the addition of dopamine to the reaction mixture reduces the oxidized TMB to its original colorless form and itself oxidizes to dopamine quinone (). A detailed mechanism is shown in Scheme 2.
SCHEME 2
3.5 Optimization of various parameters
3.5.1 Effect of Co-HAp nanocomposite amount
In order to assess the effect of Co-HAp, different amounts in the range of 2–8 mg of the proposed platform were evaluated. As the amount of Co-HAp increased, the color of the solution mixture started to fade. The solution color completely vanished at 5 mg of the Co-HAp. With the increase in the concentration of Co-Hap, the color of the reaction mixture starts to intensify to blue-green. For these experiments, 100 µL of TMB solution (12 mM), 500 µL of phosphate-buffer saline, 100 µL of H2O2, and 100 µL of a 35 µM dopamine solution were taken. Under the prevailing conditions, the reaction took only 2 min. Ivanova et al. reported 7 mg of mimic enzyme as optimal in their work (). Figure 4i illustrates the correlation between different Co-HAp nanocomposite concentrations, at given amounts of TMB, H2O2, and dopamine.
FIGURE 4
3.5.2 Impact of pH on the fabricated sensor
The fabricated sensing platform was tested in the pH range 3–10, as shown in Figure 4ii. As the pH increases from three to five, the color of the chromogenic substrate gradually vanishes until it completely disappears at pH 5. As the pH increased further, the color of the reaction mixture appeared again and intensified untill it reached pH 10. In these experiments, 5 mg doped Co-HAp nanocomposite, 100 μL TMB solution (12 mM), incubation time 2 min, 100 μL H2O2, and 100 μL dopamine solution (35 µM) were used. As a result, a pH of five was determined to be the ideal pH for the suggested probe. pH four was proposed as the optimal pH for the work reported in an earlier published work ().
3.5.3 Effect of TMB concentration
The optimization results for TMB concentration for the sensing of dopamine are shown in Figure 4iii. The TMB concentration was varied in the range of 3–21 mM in the optimization experiments. It is clear from the inset Figure that at 12 mM of TMB concentration we get the best response. A TMB concentration, lower or higher than the mentioned amount does not produce any desirable results. In these experiments, 100 µL of TMB (3–21 mM), 100 µL of H2O2 (9 mM), and 5 mg of doped Co-HAp nanocomposite were used. Wu et al. reported 0.5 mM TMB as optimal in their work (). In the subsequent experiments, 12 mM of TMB concentration was used.
3.5.4 Effect of H2O2 concentration
In order to obtain the optimal H2O2 concentration, the sensing experiments were performed at different concentrations of H2O2, ranging from 2 to 14 mM, as shown in Figure 4iv. Results indicate that the best response was achieved at 8 mM of H2O2. These experiments were performed under the following conditions: 5 mg of Co-HAp nanocomposite; 100 µL of TMB (12 mM); and 500 µL of PBS. Yang et al. reported 65 mM to be the optimal concentration of H2O2 in their work ().
3.5.5 Time optimization
Figure 4v depicts the optimization of time for the proposed sensing platform. The maximal efficiency of the Co-HAp nanocomposite was observed after 2 minutes. Under optimal conditions, the proposed sensor detects dopamine in 2 min. Further increases in time show no change in color, indicating the significance of the fabricated platform. An earlier study reported that 7 min are required for the detection of the analyte ().
3.6 Analytical merits of the method
An easy and quick colorimetric detection method was used to detect dopamine under the ideal experimental conditions. Based on the catalytic activity of the synthesized Co-HAp nanocomposite, the sensor’s sensitivity to dopamine detection was examined. Various dopamine concentrations were used during the evaluation of the fabricated platform for its analytical merits. As seen, with the increasing concentration of dopamine, results the UV-Vis peak at 652 nm diminishes. Different concentrations of dopamine were taken in the range of 0.9–35 μM, as shown in Figures 5i, ii. In the absence of dopamine, it shows a peak at 652 nm in the UV spectrum and decreases linearly as dopamine concentration rises. Dopamine detection was performed in a linear range of 0.9–35 µM with an LOD of 0.51 µM and an LOQ of 1.7 µM with regression coefficient (R2) value of 0.993.
FIGURE 5
3.7 Comparing the suggested sensor with different methods
As indicated in Table 2, the efficacy of the suggested sensor was evaluated by contrasting the findings with those of previous investigations. The comparison shows the excellent performance of the proposed sensor in terms of lower LOD and wide linear range.
TABLE 2
| S.No | Analytical method | Linear range (µM) | LOD (µM) | References |
|---|---|---|---|---|
| 1 | Pt/CoFe2O4 | 20–80 | 0.42 | |
| 2 | CoFe2O4/CoS | 0–50 | 0.58 | |
| 3 | Au NP-PET | 0.5–500 | 0.5 | |
| 4 | G-ZIF-8 | 3–1000 | 1.0 | |
| 5 | (NiO) NPs | 2–100 | 1.038 | |
| 6 | TGA-CdTe QDs | 3–100 | 1.3 | |
| 7 | (CuS-BSA-Cu3(PO4)2) | 0.05–100 | 0.13 | |
| 8 | CuS-rGO | 2–100 | 0.48 | |
| 9 | Co−Fe3O4/graphene | 0.5–50 | 0.08 | |
| 10 | Co3O4@NiO | 1–1000 | 1.21 | |
| 11 | Pt/CoSn(OH)6 | 5.0 to 60 | 4.42 | |
| 12 | Co-HAp | 0.9–35 | 0.51 | This work |
A brief comparison of our synthesized platform with the reported sensors for the colorimetric detection of dopamine.
3.8 Interference studies
Under optimized conditions, the fabricated platform was tested for the selective sensing of dopamine. For this purpose, glucose, K+, Mg2+, human serum albumin (HSA), uric acid, nitrite and ascorbic acid, were examined as potential interfering species, as shown in Figure 6. The findings demonstrate that dopamine has a relatively low absorption value as compared to the other species.
FIGURE 6
3.9 Application of the fabricated sensor in physiological solution
In order to examine the use of the suggested platform, we applied the technique for dopamine detection in physiological solutions. For this purpose, a physiological solution was used to analyze dopamine. Physiological solutions of three different concentrations of dopamine were prepared for sensing through the fabricated platform. As the dopamine concentration increases, the intensity of the absorption peak at 652 nm decreases linearly. The colorimetric change was observed in a short time of only 2 min. As shown in Figure 7, the sensor is very efficient and exceptionally sensitive for detecting dopamine in biological samples.
FIGURE 7
4 Conclusion
In conclusion, we have successfully fabricated a new Co-HAp sensing platform for the colorimetric sensing of dopamine. All the characterizations confirmed the successful synthesis of HAp and Co-HAp. The synthesized mimic enzyme, with the synergistic effect of hydrogen peroxide, oxidized the TMB with a visible colorimetric change that was subsequently confirmed with a UV-Vis spectrophotometer. The addition of dopamine to the reaction mixture resulted in the reduction of the oxidized TMB to TMBred and the disappearance of the blue-green color. The fabricated platform (Co-HAp) was highly sensitive, quick, and selective for the sensing of dopamine as compared to the previously reported methods. The fabricated platform was used for the sensing of dopamine in physiological solutions. The proposed sensor has the potential to be used as a laboratory tool for the diagnosis, management, and monitoring of various neurological disorders at low cost and easy operation.
Statements
Data availability statement
The original contributions presented in the study are included in the article/Supplementary material, further inquiries can be directed to the corresponding authors.
Ethics statement
The work received ethical approval from the concerned forum of Kohat University of Science and Technology, KUST, Kohat via No. KUST/Ethical Committee/1023.
Author contributions
UN: Conceptualization, Formal Analysis, Investigation, Methodology, Project administration, Supervision, Writing–review and editing. NJ: Formal Analysis, Investigation, Methodology, Validation, Writing–original draft. AB: Formal Analysis, Investigation, Methodology, Supervision, Writing–review and editing. NM: Conceptualization, Data curation, Visualization, Writing–review and editing. MS: Investigation, Methodology, Software, Writing–review and editing. IU: Formal Analysis, Investigation, Methodology, Visualization, Writing–original draft. SA: Data curation, Software, Writing–review and editing. JI: Data curation, Formal Analysis, Investigation, Methodology, Software, Writing–review and editing. MA: Data curation, Investigation, Methodology, Software, Validation, Writing–original draft. RU: Formal Analysis, Funding acquisition, Project administration, Resources, Validation, Writing–review and editing. SA: Formal Analysis, Funding acquisition, Project administration, Resources, Software, Writing–review and editing. SO: Formal Analysis, Funding acquisition, Methodology, Project administration, Resources, Validation, Visualization, Writing–review and editing.
Funding
The author(s) declare that financial support was received for the research, authorship, and/or publication of this article. This research work is supported by the Doctoral Research Fund, China, awarded to SCO. The authors wish to thank Researchers Supporting Project Number (RSP2024R45) at King Saud University, Riyadh, Saudi Arabia for financial support.
Conflict of interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Publisher’s note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article, or claim that may be made by its manufacturer, is not guaranteed or endorsed by the publisher.
References
1
AnjumN. A.SharmaP.GillS. S.HasanuzzamanM.KhanE. A.KachhapK.et al (2016). Catalase and ascorbate peroxidase—representative H 2 O 2-detoxifying heme enzymes in plants. Environ. Sci. Pollut. Res.23, 19002–19029. 10.1007/s11356-016-7309-6
2
BaruaE.DebP.Das LalaS.DeoghareA. B. (2019). Extraction of hydroxyapatite from bovine bone for sustainable development. Biomaterials Orthop. Bone Regen. Des. Synthesis, 147–158.
3
CarreraV.SabaterE.VilanovaE.SogorbM. A. (2007). A simple and rapid HPLC–MS method for the simultaneous determination of epinephrine, norepinephrine, dopamine and 5-hydroxytryptamine: application to the secretion of bovine chromaffin cell cultures. J. Chromatogr. B847, 88–94. 10.1016/j.jchromb.2006.09.032
4
DhanasekaranT.PadmanabanA.GnanamoorthyG.ManigandanR.KumarS. P.StephenA.et al (2018). Recent advances in polymer supporting layered double hydroxides nanocomposite for electrochemical biosensors. Mater. Res. Express5, 014011. 10.1088/2053-1591/aaa538
5
DuttaS.RayC.MallickS.SarkarS.SahooR.NegishiY.et al (2015). A gel-based approach to design hierarchical CuS decorated reduced graphene oxide nanosheets for enhanced peroxidase-like activity leading to colorimetric detection of dopamine. J. Phys. Chem. C119, 23790–23800. 10.1021/acs.jpcc.5b08421
6
FangX.-Q.LiuY.-C.WangG.-W.KeY.-P. (2006). A novel coenzyme NADH model 1-benzyl-1, 4-dihydronicotinamide-mediated reaction: a single intermediate serves two mechanisms. Res. Chem. Intermed.32, 603–611. 10.1163/156856706778400316
7
FihriA.LenC.VarmaR. S.SolhyA. (2017). Hydroxyapatite: a review of syntheses, structure and applications in heterogeneous catalysis. Coord. Chem. Rev.347, 48–76. 10.1016/j.ccr.2017.06.009
8
GergelyG.WéberF.LukácsI.TóthA. L.HorváthZ. E.MihályJ.et al (2010). Preparation and characterization of hydroxyapatite from eggshell. Ceram. Int.36, 803–806. 10.1016/j.ceramint.2009.09.020
9
HanL.LiC.ZhangT.LangQ.LiuA. (2015). Au@ Ag heterogeneous nanorods as nanozyme interfaces with peroxidase-like activity and their application for one-pot analysis of glucose at nearly neutral pH. ACS Appl. Mater. interfaces7, 14463–14470. 10.1021/acsami.5b03591
10
HeF.LiW.ZhaoF.ZhuX.LiuQ.LiuZ.et al (2020). Pt deposited on magnetic CoFe2O4 nanoparticles: double enzyme-like activity, catalytic mechanism and fast colorimetric sensing of dopamine. Microchem. J.158, 105264. 10.1016/j.microc.2020.105264
11
HosseiniM.AghazadehM.GanjaliM. R. (2017). A facile one-pot synthesis of cobalt-doped magnetite/graphene nanocomposite as peroxidase mimetics in dopamine detection. New J. Chem.41, 12678–12684. 10.1039/c7nj02082a
12
HowesO. D.McCutcheonR.OwenM. J.MurrayR. M. (2017). The role of genes, stress, and dopamine in the development of schizophrenia. Biol. psychiatry81, 9–20. 10.1016/j.biopsych.2016.07.014
13
IrfanM.IrfanM. (2020). Overview of hydroxyapatite; composition, structure, synthesis methods and its biomedical uses. Biomed. Lett.6, 17–22.
14
IvanovaM. N.GrayferE. D.PlotnikovaE. E.KibisL. S.DarabdharaG.BoruahP. K.et al (2019). Pt-decorated boron nitride nanosheets as artificial nanozyme for detection of dopamine. ACS Appl. Mater. interfaces11, 22102–22112. 10.1021/acsami.9b04144
15
JiangD.NiD.RosenkransZ. T.HuangP.YanX.CaiW. (2019). Nanozyme: new horizons for responsive biomedical applications. Chem. Soc. Rev.48, 3683–3704. 10.1039/c8cs00718g
16
KhaliqA.NazirR.KhanM.RahimA.AsadM.ShahM.et al (2023). Co-doped CeO2/activated C nanocomposite functionalized with ionic liquid for colorimetric biosensing of H2O2 via peroxidase mimicking. Molecules28, 3325. 10.3390/molecules28083325
17
KhawarA.AslamZ.ZahirA.AkbarI.AbbasA. (2019). Synthesis of Femur extracted hydroxyapatite reinforced nanocomposite and its application for Pb (II) ions abatement from aqueous phase. Int. J. Biol. Macromol.122, 667–676. 10.1016/j.ijbiomac.2018.10.223
18
KienastT.HeinzA. (2006). Dopamine and the diseased brain. CNS Neurological Disorders-Drug Targets Formerly Curr. Drug Targets-CNS Neurological Disord.5, 109–131. 10.2174/187152706784111560
19
LiuH.DingY.-N.BianB.LiL.LiR.ZhangX.et al (2019). Rapid colorimetric determination of dopamine based on the inhibition of the peroxidase mimicking activity of platinum loaded CoSn (OH) 6 nanocubes. Microchim. Acta186, 755–759. 10.1007/s00604-019-3940-5
20
LuB.KeX.ZhangZ.HaoJ.ZhangB.TangJ. (2013). Amine-assisted solvothermal approach for the in situ synthesis of metal telluride/reduced graphene oxide. Carbon63, 157–164. 10.1016/j.carbon.2013.06.067
21
LuongJ.MulchandaniA.GuilbaultG. (1988). Developments and applications of biosensors. Trends Biotechnol.6, 310–316. 10.1016/0167-7799(88)90026-1
22
MauryaM. R.ChaudharyN.AvecillaF.CorreiaI. (2015). Mimicking peroxidase activity by a polymer-supported oxidovanadium (IV) Schiff base complex derived from salicylaldehyde and 1, 3-diamino-2-hydroxypropane. J. Inorg. Biochem.147, 181–192. 10.1016/j.jinorgbio.2015.01.012
23
MuhammadN.GaoY.IqbalF.AhmadP.GeR.NishanU.et al (2016). Extraction of biocompatible hydroxyapatite from fish scales using novel approach of ionic liquid pretreatment. Sep. Purif. Technol.161, 129–135. 10.1016/j.seppur.2016.01.047
24
NachitW.TouhtouhS.RamziZ.ZbairM.EddiaiA.RguitiM.et al (2016). Synthesis of nanosized TiO2 powder by sol gel method at low temperature. Mol. Cryst. Liq. Cryst.627, 170–175. 10.1080/15421406.2015.1137135
25
NanaL.RuiyiL.QinshengW.YongqiangY.XiulanS.GuangliW.et al (2021). Colorimetric detection of chlorpyrifos in peach based on cobalt-graphene nanohybrid with excellent oxidase-like activity and reusability. J. Hazard. Mater.415, 125752. 10.1016/j.jhazmat.2021.125752
26
NejadM. A. F.Hormozi-NezhadM. R. (2017). Design of a ratiometric fluorescent probe for naked eye detection of dopamine. Anal. Methods9, 3505–3512. 10.1039/c7ay00755h
27
NishanU.GulR.MuhammadN.AsadM.RahimA.ShahM.et al (2020). Colorimetric based sensing of dopamine using ionic liquid functionalized drug mediated silver nanostructures. Microchem. J.159, 105382. 10.1016/j.microc.2020.105382
28
NishanU.SabbaU.RahimA.AsadM.ShahM.IqbalA.et al (2021). Ionic liquid tuned titanium dioxide nanostructures as an efficient colorimetric sensing platform for dopamine detection. Mater. Chem. Phys.262, 124289. 10.1016/j.matchemphys.2021.124289
29
OueslatiK.PromeyratA.GatellierP.DaudinJ.-D.KondjoyanA. (2018). Stoichio-kinetic modeling of fenton chemistry in a meat-mimetic aqueous-phase medium. J. Agric. food Chem.66, 5892–5900. 10.1021/acs.jafc.7b06007
30
PalierseE.MasseS.LaurentG.Le GrielP.MosserG.CoradinT.et al (2022). Synthesis of hybrid polyphenol/hydroxyapatite nanomaterials with anti-radical properties. Nanomaterials12, 3588. 10.3390/nano12203588
31
PountosI.GiannoudisP. V. (2016). Is there a role of coral bone substitutes in bone repair?Injury47, 2606–2613. 10.1016/j.injury.2016.10.025
32
RathaI.DattaP.BallaV. K.NandiS. K.KunduB. (2021). Effect of doping in hydroxyapatite as coating material on biomedical implants by plasma spraying method: a review. Ceram. Int.47, 4426–4445. 10.1016/j.ceramint.2020.10.112
33
RoopalakshmiS.RavishankarR.BelaldavarS.PrasadR. V.PhaniA. (2017). Investigation of structural and morphological characteristic of hydroxyapatite synthesized by sol-gel process. Mater. Today Proc.4, 12026–12031. 10.1016/j.matpr.2017.09.126
34
RostamiA.HadjizadehA.MahshidS. (2020). Colorimetric determination of dopamine using an electrospun nanofibrous membrane decorated with gold nanoparticles. J. Mater. Sci.55, 7969–7980. 10.1007/s10853-020-04547-0
35
RoychoudhuryA.BasuS.JhaS. K. (2016). Dopamine biosensor based on surface functionalized nanostructured nickel oxide platform. Biosens. Bioelectron.84, 72–81. 10.1016/j.bios.2015.11.061
36
SahanaH.KhajuriaD. K.RazdanR.MahapatraD. R.BhatM.SureshS.et al (2013). Improvement in bone properties by using risedronate adsorbed hydroxyapatite novel nanoparticle based formulation in a rat model of osteoporosis. J. Biomed. Nanotechnol.9, 193–201. 10.1166/jbn.2013.1482
37
ShiD.SunY.LinL.ShiC.WangG.ZhangX. (2016). Naked-eye sensitive detection of alkaline phosphatase (ALP) and pyrophosphate (PPi) based on a horseradish peroxidase catalytic colorimetric system with Cu (ii). Analyst141, 5549–5554. 10.1039/c6an01124a
38
SwaidanA.BarrasA.AddadA.TahonJ.-F.ToufailyJ.HamiehT.et al (2021). Colorimetric sensing of dopamine in beef meat using copper sulfide encapsulated within bovine serum albumin functionalized with copper phosphate (CuS-BSA-Cu3 (PO4) 2) nanoparticles. J. Colloid Interface Sci.582, 732–740. 10.1016/j.jcis.2020.08.057
39
WangH.-B.ZhangH.-D.ChenY.LiuY.-M. (2015). A fluorescent biosensor for protein detection based on poly (thymine)-templated copper nanoparticles and terminal protection of small molecule-linked DNA. Biosens. Bioelectron.74, 581–586. 10.1016/j.bios.2015.07.021
40
WangJ.DuR.LiuW.YaoL.DingF.ZouP.et al (2019). Colorimetric and fluorometric dual-signal determination of dopamine by the use of Cu-Mn-O microcrystals and C-dots. Sensors Actuators B Chem.290, 125–132. 10.1016/j.snb.2019.03.107
41
WangY.HamidS.ZhangX.AkhtarN.ZhangX.HeT. (2017). An electrochemiluminescent biosensor for dopamine detection using a poly (luminol–benzidine sulfate) electrode modified by tyramine oxidase. New J. Chem.41, 1591–1597. 10.1039/c6nj03338e
42
WuD.HuN.LiuJ.FanG.LiX.SunJ.et al (2018). Ultrasensitive colorimetric sensing strategy based on ascorbic acid triggered remarkable photoactive-nanoperoxidase for signal amplification and its application to α-glucosidase activity detection. Talanta190, 103–109. 10.1016/j.talanta.2018.07.073
43
XuH.XiaoJ.YanL.ZhuL.LiuB. (2016). An electrochemical sensor for selective detection of dopamine based on nickel tetrasulfonated phthalocyanine functionalized nitrogen-doped graphene nanocomposites. J. Electroanal. Chem.779, 92–98. 10.1016/j.jelechem.2016.04.032
44
XuX.ShiH.MaL.KangW.LiS. (2011). Determination of trace amounts of dopamine by flow‐injection analysis coupled with luminol–Ag (III) complex chemiluminescence detection. Luminescence26, 93–100. 10.1002/bio.1189
45
YangZ.ZhuY.ChiM.WangC.WeiY.LuX. (2018). Fabrication of cobalt ferrite/cobalt sulfide hybrid nanotubes with enhanced peroxidase-like activity for colorimetric detection of dopamine. J. colloid interface Sci.511, 383–391. 10.1016/j.jcis.2017.09.097
46
YazdaniN.JavadpourJ.EftekhariY.HamrangM. (2019). Hydrothermal synthesis of cobalt-doped hydroxyapatite nanoparticles: structure, magnetic behaviour, bioactivity and antibacterial activity. Iran. J. Mater. Sci. Eng.16, 39–48.
47
ZhengX.LianQ.ZhouL.JiangY.GaoJ. (2021). Peroxidase mimicking of binary polyacrylonitrile-CuO nanoflowers and the application in colorimetric detection of H2O2 and ascorbic acid. ACS Sustain. Chem. Eng.9, 7030–7043. 10.1021/acssuschemeng.1c00723
48
ZhengY.WangY.YangX. (2011). Aptamer-based colorimetric biosensing of dopamine using unmodified gold nanoparticles. Sensors Actuators B Chem.156, 95–99. 10.1016/j.snb.2011.03.077
49
ZhengY.-Y.LiC.-X.DingX.-T.YangQ.QiY.-M.ZhangH.-M.et al (2017). Detection of dopamine at graphene-ZIF-8 nanocomposite modified electrode. Chin. Chem. Lett.28, 1473–1478. 10.1016/j.cclet.2017.03.014
50
ZhuX.MaoX.WangZ.FengC.ChenG.LiG. (2017). Fabrication of nanozyme@ DNA hydrogel and its application in biomedical analysis. Nano Res.10, 959–970. 10.1007/s12274-016-1354-9
51
ZhuY.YangZ.ChiM.LiM.WangC.LuX. (2018). Synthesis of hierarchical Co3O4@ NiO core-shell nanotubes with a synergistic catalytic activity for peroxidase mimicking and colorimetric detection of dopamine. Talanta181, 431–439. 10.1016/j.talanta.2018.01.019
Summary
Keywords
cobalt-doped hydroxyapatite, hydrogen peroxide, peroxidase mimic, dopamine, colorimetric sensor
Citation
Nishan U, Jabeen N, Badshah A, Muhammad N, Shah M, Ullah I, Afridi S, Iqbal J, Asad M, Ullah R, Ali EA, Ahmed S and Ojha SC (2024) Nanozyme-based sensing of dopamine using cobalt-doped hydroxyapatite nanocomposite from waste bones. Front. Bioeng. Biotechnol. 12:1364700. doi: 10.3389/fbioe.2024.1364700
Received
02 January 2024
Accepted
04 April 2024
Published
17 April 2024
Volume
12 - 2024
Edited by
Sharmili Roy, Stanford University, United States
Reviewed by
Jiangjiexing Wu, Tianjin University, China
Yen-Ling Chen, National Chung Cheng University, Taiwan
Updates
Copyright
© 2024 Nishan, Jabeen, Badshah, Muhammad, Shah, Ullah, Afridi, Iqbal, Asad, Ullah, Ali, Ahmed and Ojha.
This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Umar Nishan, umarnishan85@gmail.com; Suvash Chandra Ojha, suvash_ojha@swmu.edu.cn
Disclaimer
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.