- 1Key Laboratory of Colloid, Interface and Chemical Thermodynamics, Institute of Chemistry, Chinese Academy of Sciences, Beijing, China
- 2School of Chemistry and Chemical Engineering, University of Chinese Academy of Sciences, Beijing, China
- 3Center for Molecular Imaging and Nuclear Medicine, School for Radiological and Interdisciplinary Sciences (RAD-X), Collaborative Innovation Center of Radiation Medicine of Jiangsu Higher Education Institutions, and State Key Laboratory of Radiation Medicine and Protection, Soochow University, Suzhou, China
The rare-earth nanocrystals containing Er3+ emitters offer very promising tools for imaging applications, as they can not only exhibit up-conversion luminescence but also down-conversion luminescence in the second near-infrared window (NIR II). Doping non-lanthanide cations into host matrix was demonstrated to be an effective measure for improving the luminescence efficiency of Er3+ ions, while still awaiting in-depth investigations on the effects of dopants especially those with high valence states on the optical properties of lanthanide nanocrystals. To address this issue, tetravalent Zr4+ doped hexagonal NaGdF4:Yb,Er nanocrystals were prepared, and the enhancement effects of the Zr4+ doping level on both up-conversion luminescence in the visible window and down-conversion luminescence in NIR II window were investigated, with steady-state and transient luminescence spectroscopies. The key role of the local crystal field distortions around Er3+ emitters was elucidated in combination with the results based on both of Zr4+ and its lower valence counterparts, e.g., Sc3+, Mg2+, Mn2+. Univalent ions such as Li+ was utilized to substitute Na+ ion rather than Gd3+, and the synergistic effects of Zr4+ and Li+ ions by co-doping them into NaGdF4:Yb,Er nanocrystals were investigated toward optimal enhancement. Upon optimization, the up-conversion emission of co-doped NaGdF4:Yb,Er nanocrystals was enhanced by more than one order of magnitude compared with undoped nanocrystals. The current studies thus demonstrate that the local crystal field surrounding emitters is an effective parameter for manipulating the luminescence of lanthanide emitters.
Introduction
Rare-earth (RE) nanocrystals are promising light-emitting materials as they are able to convert near infrared (NIR) photons into ultraviolet, visible, and NIR lights through either an up-conversion path or a down-conversion path (Chen et al., 2013; Dong et al., 2015). Compared with conventional down-conversion luminescent materials such as organic dyes and semiconductor quantum dots (Antaris et al., 2016; Chen B.K. et al., 2017; Stroyuk et al., 2018; Lu et al., 2020), rare-earth nanocrystals offer remarkable optical advantages, such as narrow “atomic-line” emission from the internal f-f transitions of lanthanide ions, large stokes or anti-stokes shifts, long luminescence lifetime, and high photochemical stability, and thus are potentially useful for diverse imaging applications (Zhou et al., 2012; Liu et al., 2014; Fan et al., 2018; Ai et al., 2019). Especially, emitting lanthanide Er3+ ions based rare-earth nanocrystals have aroused intense interests because Er3+ ions present a longer down-conversion emission wavelength at 1,525 nm in the second NIR window (NIR II, 1,000–1,700 nm), which enables a virtual zero auto-fluorescence interference of tissues in bio-imaging, apart from the up-conversion emission at 541 nm and 656 nm in the visible and NIR I region (NIR I, 650–950 nm), respectively (Shen et al., 2013; Xu et al., 2019). However, due to the low absorption cross-section (~10−20 cm2) of lanthanide ions caused by the parity-forbidden transition of 4f electrons (Tu et al., 2015), and non-radiative relaxation between multi-energy levels, their up- and down-conversion luminescence efficiencies are generally low, which obviously hinders their applications. In principle, Yb3+ ions are suitable for sensitizing the up-conversion luminescence of Er3+ ions, benefiting from the large absorption cross-section of Yb3+ ions. Increasing the concentration of sensitizer or emitter have been adopted to improve the luminescence upon 980 nm excitation (Chen Q.S. et al., 2017; Ma et al., 2017), but overincreasing the concentration of Yb3+ is unfavorable owing to the participation of Yb3+ ions on the particle surface in dissipating the absorbed energy (Johnson et al., 2017).
Apart from sensitizing ion doping, significant progresses have also been made for improving the up-conversion luminescence of Er3+ ions in rare-earth nanocrystals through surface passivation by forming core-shell structures (Yi and Chow, 2007; Fan et al., 2019), surface plasmon coupling by conjugating to noble metal particles (Sun et al., 2014; Clarke et al., 2018), and host-lattice manipulation by non-lanthanide (Ln) ions doping (Dong et al., 2013). The epitaxial growth of a shell on preformed emitting core, e.g., growing NaGdF4 shell on NaGdF4:Yb,Er core (Vetrone et al., 2009; Li et al., 2013), can suppress the energy transfer from the emitting core to surrounding environment, thus favorable for boosting the luminescence efficiency, apart from giving rise to stable and controllable core/shell structures (Wang et al., 2010). However, this approach will require at least two successive steps of preparations (He et al., 2017). Modifying rare-earth nanocrystals with plasmonic noble metal can efficiently improve the luminescence by changing the surface electronic field, but also leads to relatively large and less stable structures that may be disassociated under certain conditions. Different from these two approaches, doping non-Ln ions to enhance the luminescence through modulating the local chemical environment of the emitting centers doesn't necessarily increase the particle size apart from forming more stable structures (Huang et al., 2019). Because of the interplay between the 4f electrons of Er3+ and the crystal field of the host doped with non-Ln ions, the probability of radiative transitions within Er3+ can hopefully be enhanced by relaxing the selection rules (Fischer et al., 2019). For example, metal ions such as Li+, Ca2+, Mn2+, and Fe3+, were adopted as non-Ln dopants to enhance the up-conversion luminescence (Cheng et al., 2012; Zeng et al., 2014; Tang et al., 2020b; Verma et al., 2020). Doping of Li+ ions was demonstrated to increase the up-conversion luminescence of Y2O3:Yb,Er nanocrystals by factors of 8-25 (Chen et al., 2008). Doping of alkaline-earth ions such as Ca2+ was also found to improve the uniformity of the resulting NaGdF4:Yb,Er nanocrystals, apart from enhancing the up-conversion luminescence (Lei et al., 2013). Doping Fe3+ into a NaYF4:Yb,Er nanocrystals selectively enhanced the red up-conversion luminescence of Er3+ ions by 7 times (Tang et al., 2015). Nevertheless, doping of 3d transition metal ions such as Mn2+ or Fe3+ into host will introduce new energy levels associated with partially filled 3d orbitals of the dopant, particularly when the doping level is high enough. In consequence, additional electronic transition pathways may be created to alter the up-conversion emission position or decrease the up-conversion luminescence intensity. However, the effect of dopant ions on the down-conversion luminescence of Er3+ remains rarely addressed. Besides, the dopants are mainly chosen from low valence state ions. Therefore, it is fundamentally interesting to study the high valence dopants particularly those free of d-d transitions for improving the up- and down-conversion luminescence of Er3+ based RE luminescent nanocrystals. But there is a clear lack of a systematic study in this respect.
Following our previous investigations on the synthesis and optical properties of RE nanocrystals (Liu et al., 2013; Huang et al., 2015; Li et al., 2019), herein we report hexagonal NaGdF4:Yb,Er nanocrystals doped with tetravalent Zr4+ ions that possess d0 configuration, and studied the Zr4+ doping level-dependent luminescence properties of Er3+ through both steady-state and transient luminescence spectroscopies. The resulting Zr4+-doped NaGdF4:Yb,Er nanocrystals exhibited enhanced emissions for both up-conversion luminescence and down-conversion emission peaking at 1,525 nm. The role of Zr4+ dopants in altering the local crystal field of the emitters was discussed in combination with Judd-Ofelt theory. To disclose the underlying mechanisms, the effects of the valence state of the dopant ions on the luminescence properties were investigated by doping NaGdF4:Yb,Er nanocrystals with Sc3+, Mg2+, Mn2+, respectively, for comparing with the Zr4+-doped counterpart. Different from above dopants, univalent ion such as Li+ was doped into NaGdF4:Yb,Er nanocrystals by substituting Na+ rather than Gd3+, and the synergistic effects of Zr4+ and Li+ ions by co-doping them into NaGdF4:Yb,Er nanocrystals were investigated toward optimal enhancement.
Results and Discussion
Synthesis of Zr4+-Doped NaGdF4:Yb,Er Nanocrystals
Zr4+-doped NaGdF4:Yb,Er nanocrystals were synthesized via a high temperature approach using oleic acid (OA) as the particle surface capping ligand. As displayed in Figure 1a, the as-prepared NaGdF4:Yb,Er nanocrystals are quasi-spherical. After doped with Zr4+ ions, as shown in Figures 1b–e, the nanocrystals slightly increase in particle size from 9.7 ± 1.1 nm to 13.3 ± 0.7 nm, depending on the initial feeding molar ratio of Zr4+ to the total cations. Meanwhile, the relative standard deviation (RSD) of the particle size was reduced from 11.3 to 5.3%. Further ICP-AES results demonstrated that the Zr4+ ions were successfully doped into the NaGdF4:Yb,Er nanocrystals and the actual doping level of Zr4+ in the final particles goes linearly from 2.4 to 9.9% against the initial feeding molar ratio of Zr4+ from 3.0 to 15.0%, as shown in Figure 1f.
Figure 1. (a–e) Typical TEM images of NaGdF4:Yb,Er nanocrystals doped with different feeding ratios of Zr4+ ions, i.e., (a) 0, (b) 3.0%, (c) 5.0%, (d) 10.0%, and (e) 15.0%, together with their corresponding size distributions, respectively. (f) The actual doping levels of Zr4+ in the final nanocrystals. (g) The XRD patterns of NaGdF4:Yb,Er nanocrystals before and after Zr4+ doping. The vertical line pattern in the bottom frame is the standard XRD data for hexagonal NaGdF4 according to JCPDS card.
It's worth noting that the size of the doped nanocrystals is positively correlated with the doping level of Zr4+ ions. In the current reaction system, OA acts as a coordinating solvent. It forms metal oleate with the metal precursors prior to the formation of the target nanocrystals. In this context, OA is expected to show higher binding affinity to Zr4+ ion than to Gd3+ ion due to the smaller radius and higher valence of Zr4+. The energy barrier for decomposing Zr oleate is expected to be higher than that for Gd oleate, which can find supports from the difference in the bond dissociation energies, i.e., 766.1 kJ/mol for Zr-O and 715 kJ/mol for Gd-O. Consequently, the supersaturation level as well as the number of nuclei is decreased in the reaction system as a function of Zr4+ precursor concentration, which explains the dependency of particle size on the Zr4+ feeding ratio (Buonsanti and Milliron, 2013).
The crystal structure of all aforementioned samples was analyzed by powder XRD. As shown in Figure 1g, both undoped and Zr4+-doped NaGdF4:Yb,Er nanocrystals display a hexagonal phase structure. Although the doped samples exhibit similar diffraction patterns, the diffraction peak of (201) crystal plane gradually shifts to higher angles along with the increase of Zr4+ dopant concentration, indicating an effective incorporation of Zr4+ ions into the host lattice. It can then be deduced that the Zr4+ ions substitute Gd3+ ions rather than staying at the interstitial sites, because substituting the Gd3+ cations with smaller Zr4+ ions will cause the host lattice to shrink according to Bragg's Law (2dsinθ = nλ), while occupying the interstitial sites will cause the host lattice to expand. According to the ICP-AES results given in Table S1 in supplementary material the concentration of Gd3+ in the nanocrystals was decreased with the increase of Zr4+ doping level, which strongly supports the above structural analysis. While the gradually narrowed full width at half maximum (FWHM) of the main diffraction peaks, as shown in Figure S1, suggested that Zr4+ doping didn't decrease the crystalline degree, which is the most important prerequisite for improving the luminescence properties of the doped nanocrystals through the manipulation of the crystal field around the emitting ions.
Up- and Down-Conversion Luminescence of Zr4+-Doped NaGdF4:Yb,Er Nanocrystals
As demonstrated by the results given in Figure 1 that the particle size and size distribution are dependent on the doping level of Zr4+, it is interesting to learn the dependency of optical properties of the resulting nanocrystals on the doping level of Zr4+ as well. In the absence of Zr4+ dopant, the NaGdF4:Yb,Er nanocrystals exhibit multiple emissions upon 980 nm excitation e.g., up-conversion emissions peaking at 541 and 656 nm, down-conversion emission peaking at 1,525 nm, respectively, as shown in Figure 2a. In the presence of Zr4+ dopants, the luminescence intensity of the up-conversion emission at 541 nm is dramatically increased against the Zr4+ content and gets enhanced by a factor of 6.7 when the Zr4+ content reaches 7.1%, and then becomes decreased upon further increase of the Zr4+ content. Meanwhile, the luminescence intensity of the down-conversion emission presents a similar tendency and gets enhanced by a factor of 1.8 when the Zr4+ content is around 7.1%.
Figure 2. (a) Up- and down-conversion luminescence spectra of Zr4+-doped NaGdF4:Yb,Er nanocrystals at varying doping ratios of Zr4+ ions under 980 nm laser excitation and the up- and down-conversion emission intensities as a function of Zr4+ doping level, respectively. (b) Simplified energy level diagrams depicting the energy transfer between Yb3+ and Er3+ ions. (c,d) Transient emissions observed at 541, 656, and 1,525 nm of NaGdF4:Yb,Er nanocrystals at varying doping ratios of Zr4+ ions.
To rule out the possible size effects on the optical properties, the undoped NaGdF4:Yb,Er nanocrystals of 13.2 nm were prepared, as shown in Figure S2a, for comparing with the Zr4+-doped NaGdF4:Yb,Er with Zr4+ level of 9.9%. The enhancement factors for up-conversion emission at 541 nm and down-conversion emission at 1,525 nm were determined to be 1.2 and 1.1, respectively, as shown in Figure S2b, remarkably smaller than that obtained upon Zr4+ doping. Therefore, it is reasonable to deduce that the enhancement effects on both up- and down-conversion luminescence may come from the alternation of crystal field symmetry surrounding Er3+ ions, induced by the Zr4+ dopants. Regarding the difference in the enhancement effects of Zr4+ ions on up- and down-conversion emissions, it can reasonably be attributed to the difference between the transitions involved in these two types emissions, as shown in Figure 2b. The up-conversion luminescence of Er3+ is a multiphoton process and requires the participation of multiple energy levels, while the down-conversion emission of Er3+ involves less energy levels. Therefore, it can be expected that the up-conversion luminescence is more readily disturbed by the crystal field.
To provide more evidence on the variation of the crystal field induced by Zr4+ ions, time-resolved luminescence measurements were carried out to determine the variations in the lifetimes of up- and down-conversion luminescence upon Zr4+ doping. The luminescence decay curves measured at different emission positions, i.e., 541 nm (4S3/2-4I15/2), 656 nm (4F9/2-4I15/2), and 1,525 nm (4I13/2-4I15/2) of the Zr4+-doped NaGdF4:Yb,Er nanocrystals with different Zr4+ doping levels are shown in Figures 2c,d. All decay curves were well-fitted with a two-exponential function and the detailed fitting results are given in Table S2. In brief, Zr4+ doping increased the average lifetime of 541 nm emission from 82.1 μs for the undoped ones to 114.1 μs for doped ones with Zr4+ content of 7.1%, while the average lifetime of 1,525 nm emission was prolonged from 855.0 μs to 1247.2 μs accordingly. The measured lifetime of the excited states of Er3+ is the reciprocal of the total transition rate including radiative and non-radiative transition rates. The non-radiative transition rate of Er3+ can be affected by the phonon energy of NaGdF4 lattice, the energy transfer process from adsorbed photoenergy to surroundings, the cross-relaxation between energy levels, and so forth. While the radiative transition part strongly depends on the crystal structure and the symmetry of local crystal field of the emitters owing to a decrease of the forbidden nature of the transition in asymmetric sites (Boyer et al., 2004; Tu et al., 2013). In general, the lifetime of the intermediate states of activator experiences a prolongation with the distortion of its local asymmetry (Kar and Patra, 2012; Dong et al., 2015). Therefore, the prolongation of the lifetimes of both up- and down-conversion luminescence suggests that long-lived intermediate excited states 4I11/2 and the population of 4S3/2 and 4I13/2 (Er3+) become more favorable upon the introduction of Zr4+ dopants, which as a result increases the f-f transition probability of Er3+ to induce efficient up- and down-conversion luminescence.
Trivalent lanthanide ions generally suffer from low luminescence efficiency as the electric-dipole transition within the 4f electrons is forbidden by Laporte rule. The non-Ln ions doping may disturb the local crystal field of the emitters and thus change the transition probability (Chen et al., 2014; Han et al., 2014). In order to further understand the underlying mechanism of the Zr4+ dopants governing the luminescence, the electric-dipole transition theory was discussed below.
The f-f transition intensity can be estimated from Judd-Ofelt theory as given by Equations (1) and (2) (Werts et al., 2002; Du et al., 2018),
where A is the spontaneous emission probability of transition from the initial J manifold |[S, L]J〉 to final J′ manifold |[S′, L′]J′〉 and e, h, n, and λ refer to the elementary charge, Plank constant, refraction index, and average wavelength of the transition, respectively. 2J+1 is the degeneracy of the initial state, and Sed and Smd are the electric dipole and magnetic dipole line strengths, respectively. The electric dipole transition strength Sed is very sensitive to the chemical surrounding of the lanthanide emitting ions, whereas the magnetic dipole transition strength Smd is not. In Equation (2), Sed can be calculated by three transition intensity parameters Ωt (t = 2, 4, 6). Ω2 is the spectral intensity parameter of electric-dipole transition for 4fn electron configuration, strongly depending on the crystal field environment and reflecting that the asymmetry of the crystal field surrounding lanthanide emitting ions (Zhang et al., 2018). In principle, the enhanced lattice distortion leads to lower local crystal field symmetry, thereby giving rise to larger value of Ω2 (Walsh et al., 1998; Liu et al., 2008). With relatively smaller cationic radius and higher valence state of Zr4+ compared with those of Gd3+, the bond length of Zr-F (1.90 Å) is shorter than that of Gd-F (1.99 Å), whilst the bond energy of Zr-F (627.2 kJ/mol) is higher than that of Gd-F (590 kJ/mol), indicating that Zr4+ ions have stronger electron cloud distortion ability than Gd3+ ions. This can be further evidenced by a stronger electronic polarizability of Zr4+ (3.56 × 10−24 cm3) than that of Gd3+ (3.39 × 10−24 cm3) (Shannon and Fischer, 2016). Therefore, the distortion of electron clouds of Er3+ ions becomes favorable upon substitution of Gd3+ with Zr4+ dopants, which is intensified against the Zr4+ doping level. The decreased local crystal field symmetry is expected to give rise to a higher Ω2, which consequently encourages the electronic coupling between 4f energy levels and increases the probability of the intra f-f transition, leading to more effective enhancement in up-conversion emission.
NaGdF4:Yb,Er Nanocrytals Doped With Cations of Various Valance States
To further show the effects of the valence state of cationic dopants on the emission of Er3+ ions via the modulation of the local crystal field, non-Ln cations with various valance states, e.g., Sc3+, Mg2+, Mn2+, were also chosen to dope the NaGdF4:Yb,Er nanocrystals by feeding molar ratio of 10%, according to that optimized for Zr4+.
Although Sc3+ ion has the same valence as Gd3+ ion, it was selected to dope NaGdF4:Yb,Er by substituting Gd3+ ion. As it possesses no electron in d orbital, the substitution won't introduce new energetic levels into the nanocrystals. As shown in Figure 3a, the particle size of the resulting Sc3+-doped nanocrystals is 12.6 ± 0.8 nm. The XRD pattern shown in Figure 3b reveals the nanocrystals are in hexagonal phase. According to the luminescence spectra given in Figure 3c, Sc3+ doping only slightly increases the up-conversion luminescence by a factor of 1.8 and shows almost no impact on the down-conversion luminescence. As shown in Figures 3d,e and Table S3, Sc3+ doping gives rise to a slight increase in the average lifetimes of 541 nm and 656 nm emissions, i.e., from 82.1 μs to 85.9 μs and from 98.7 μs to 118.1 μs, respectively. The average lifetime of down-conversion emission at 1,525 nm was increased from 855.0 μs to 1035.9 μs, but still lower than that for Zr4+-doped counterparts. This can be understood by the fact that Sc3+ has very similar properties to Gd3+ as seen by very comparable binding energies between Sc-F (599 kJ/mol) and Gd-F (590 kJ/mol) bonds, thus it won't introduce strong distortion effects on the crystal field surrounding Er3+ as Zr4+ does.
Figure 3. (a) TEM image and (b) corresponding XRD pattern of Sc3+-doped NaGdF4:Yb,Er nanocrystals. (c) The up- and down-conversion luminescence spectra and intensities at 541, 656, and 1,525 nm of Sc3+-doped NaGdF4:Yb,Er nanocrystals under 980 nm laser excitation. (d,e) Transient emissions observed at 541, 656, and 1,525 nm of Sc3+-doped NaGdF4:Yb,Er nanocrystal.
Both Mg2+ and Mn2+ were selected to dope NaGdF4:Yb,Er nanocrystals, because the former is free of d orbital electrons contrasting to the latter that has d5 electron configuration. Therefore, it is expected to show the impacts of electronic configuration of the dopants on the optical properties of the resulting nanocrystals. As shown in Figures 4a,b, the particle sizes of the resulting Mg2+-doped and Mn2+-doped nanocrystals are of 12.4 ± 1.0 nm and 7.2 ± 1.0 nm, respectively. The XRD results shown in Figure 4c reveal that Mg2+-doped nanocrystals display a hexagonal phase structure, while Mn2+-doped nanocrystals exhibit a distinct cubic phase structure. The results in Figure 4d further reveal that Mg2+ doping slightly decreases the emission at 541 nm and the emission at 1,525 nm, while the emission intensity at 656 nm remains nearly unchanged. This can be explained by the fact that Mg2+ ions have much weaker electron cloud distortion ability than Gd3+ due to low electric polarizability (0.6 × 10−24 cm3), and thereby Mg2+-doped nanocrystals display even weakened luminescence in comparison with the undoped NaGdF4:Yb,Er nanocrystals. As shown in Figures 4e,f and Table S3, Mg2+ dopants give rise to a slightly increased average lifetimes for 541 nm and 656 nm emissions, i.e., from 82.1 μs to 87.4 μs and 98.7 μs to 115.4 μs in comparison with the undoped one. The average lifetime of down-conversion emission at 1,525 nm was increased from 855.0 μs to 962.8 μs, even shorter than that of Sc3+-doped nanocrystals let alone the lifetime of Zr4+-doped ones. Therefore, it can be concluded that Mg2+ ions can hardly distort the crystal filed surrounding Er3+ ions. Moreover, the substitution of Ln3+ ions with bivalent Mg2+ ions in the NaGdF4:Yb,Er nanocrystals will generate F− vacancies to balance the charge of the whole nanocrystal, which is even deleterious to the luminescence as the increase of the concentration of defects around the emitters (Tang et al., 2020a).
Figure 4. TEM images of NaGdF4:Yb,Er nanocrystals doped with (a) Mg2+ and (b) Mn2+. (c) Corresponding XRD patterns of NaGdF4:Yb,Er nanocrystals doped with Mg2+ and Mn2+. The vertical line pattern in the bottom frame is the standard XRD data for hexagonal (red line) and cubic (black line) NaGdF4 according to JCPDS card. (d) The up- and down-conversion luminescence spectra and intensities at 541, 656, and 1,525 nm of NaGdF4:Yb,Er nanocrystals doped with Mg2+ and Mn2+ under 980 nm laser excitation. (e,f) Transient emissions observed at 541, 656, and 1,525 nm of Mg2+-doped NaGdF4:Yb,Er nanocrystal.
When it comes to Mn2+ dopants, the intensity of 541 nm emission is dramatically decreased by a factor of 7.5, while the intensity of 656 nm emission is increased by a factor of 2.1, in comparison with those recorded from undoped counterparts. Consequently, the ratio of red emission to green emission is dramatically increased as shown in Figure 4d, arising from the involvement of d electron-associated energy levels of Mn2+ ions. It has been reported that using KMnF3 as matrix, a single-band red emission was obtained upon Mn-doping (Wang et al., 2011). Although the intensity of 1,525 nm emission is nearly unchanged in comparison with that of undoped nanocrystals, the down-conversion emission profile of Er3+ ions is also varied upon Mn2+ doping.
NaGdF4:Yb,Er Nanocrystals Doped With Univalent Ions
Different from the above-mentioned mechanism for enhancing the luminescence of Er3+ emitters through the distortion of local crystal field, univalent ions such as Li+ and K+ were also used to dope NaGdF4:Yb,Er nanocrystals by substituting Na+ rather than Gd3+. The TEM results shown in Figures 5a,b reveal that the average size of Li+-doped nanocrystals is of 14.3 ± 1.2 nm, while that of K+-doped nanocrystals becomes greatly decreased to 6.8 ± 1.0 nm. The XRD results in Figure 5c reveal that Li+-doped nanocrystals are in hexagonal phase, but K+-doped nanocrystals are in cubic phase. As the diffraction peak of (201) crystal plane of Li+-doped NaGdF4:Yb,Er shifts higher angles, it can be deduced that Li+ ions take the positions of Na+ ions rather than occupy the interstitial sites. According to luminescence spectra of the Li+- and K+-doped NaGdF4:Yb,Er nanocrystals shown in Figure 5d, Li+ doping increases the intensities of 541 nm emission and 1,525 nm emission by factors of 6.8 and 2.5, respectively. In huge contrast, the up- and down-conversion luminescence of K+-doped nanocrystals are dramatically decreased, due to the remarkably decreased particle size and higher crystal field symmetry of cubic phase. As shown in Figures 5e,f and Table S4, Li+ doping significantly prolongs the average lifetimes of emissions at 541 and 656 nm, i.e., from 82.1 μs to 107.5 μs, and from 98.7 μs to 151.1 μs, respectively. Meanwhile, Li+ doping also profoundly prolongs the average lifetime of the emission at 1,525 nm, i.e., from 855.0 μs to 1297.5 μs, which is comparable with 1247.2 μs for Zr4+-doped ones. In fact, owing to the much smaller radius of Li+ (0.76 Å) than that of Na+ (1.02 Å), the substitution of Na+ with Li+ in NaGdF4 nanocrystals can thus effectively modulate the crystal field, which is also supported by the higher binding energy of Li-F bond (577 kJ/mol) than that of Na-F bond (477 kJ/mol). Therefore, doping Li+ into NaGdF4:Yb,Er is favorable for enhancing both up- and down-conversion luminescence, similar to Zr4+ dopants.
Figure 5. TEM images of NaGdF4:Yb,Er nanocrystals doped with (a) Li+ and (b) K+. (c) Corresponding XRD patterns of NaGdF4:Yb,Er nanocrystals doped with Li+ and K+. (d) The up- and down-conversion luminescence spectra and intensities at 541, 656, and 1,525 nm of NaGdF4:Yb,Er nanocrystals doped with Li+ and K+ under 980 nm laser excitation, respectively. (e,f) Transient emissions observed at 541, 656, and 1,525 nm of Li+-doped NaGdF4:Yb,Er nanocrystal.
The Synergistic Crystal Field Modulation via Co-doping of Zr4+ and Li+
Considering Zr4+ and Li+ ions occupy the different lattice sites, it's therefore very interesting to synergistically combine the effects of both Zr4+ and Li+ ions for further improving the optical properties of the NaGdF4:Yb,Er nanocrystals. The co-doped nanocrystals were then prepared. The TEM image and selected area electron diffraction pattern of the resulting nanocrystals shown in Figure 6a reveal that the average size is 15.8 ± 1.2 nm and the nanocrystals are in hexagonal phase. As shown in Figure 6b, upon co-doping of Zr4+ and Li+ ions, the luminescence intensity of up-conversion emission at 541 nm is enhanced by factors of 15.0, 2.2, and 2.2, if compared with those recorded from undoped, Li+-doped, and Zr4+-doped nanocrystals, respectively, while the down-conversion emission intensity of co-doped samples is enhanced by factors of 2.7, 1.1, and 1.5, respectively. As shown in Figures 6c,d and Table S5, the transient optical behaviors of the co-doped nanocrystals also confirm the synergistic effects of Zr4+ and Li+, evidenced by the prolonged average decay lifetimes for different emissions. For example, the decay lifetime of 541 nm emission is of 123.3 μs, higher than 82.1 μs for the undoped, 107.5 μs for Li+-doped, and 114.1 μs for Zr4+-doped ones.
Figure 6. (a) TEM image and selected area electron diffraction pattern of NaGdF4:Yb,Er nanocrystals co-doped with Li+ and Zr4+. (b) The emission intensities at 541, 656, and 1,525 nm of NaGdF4:Yb,Er nanocrystals co-doped with Li+ and Zr4+ under 980 nm laser excitation. (c,d) Transient emissions observed at 541, 656, and 1,525 nm of NaGdF4:Yb,Er nanocrystals co-doped with Li+ and Zr4+ under 980 nm laser excitation.
Conclusion
In summary, tetravalent Zr4+-doped NaGdF4:Yb,Er nanocrystals were prepared. The steady-state and transient luminescence spectroscopies studies demonstrated that the Zr4+ dopants could simultaneously enhance both up- and down-conversion luminescence of Er3+ ions. Combining the experimental results with Judd-Ofelt theoretical analysis, it was revealed that Zr4+ dopants take effects by varying the crystal field surrounding Er3+ emitters. Compared with host Gd3+ ion, Zr4+ ion exhibits increased electron cloud distortion ability due to its stronger electric polarizability and higher bond energy with F−, which accounts for the increased distortion of crystal field surrounding Er3+, thus efficiently enhancing both up- and down- conversion luminescence. In addition, the effects of non-Ln dopants (Sc3+, Mg2+, Mn2+) on the up- and down-conversion emission were also investigated, and no stronger effects than Zr4+ ion were observed. Apart from the substituting Gd3+ ion, strong luminescence enhancement effects were also found when Li+ ion was used to substitute Na+ via similar mechanism, which offers an opportunity to show the synergistic effects of Zr4+ and Li+ ions by co-doping the NaGdF4:Yb,Er nanocrystals with them. Upon optimization, the up-conversion emissions were enhanced by more than one order of magnitude compared with undoped nanocrystals. The current studies thus demonstrate that the local crystal field surrounding emitters is an effective parameter for manipulating the up- and down-conversion luminescence of lanthanide emitters.
Materials and Methods
Materials
GdCl3·6H2O (450855), YbCl3·6H2O (337927), ErCl3·6H2O (259256), ScCl3·6H2O (451274), oleic acid (OA, 364525), 1-octadecene (ODE, O806), oleylamine (OM, O7805), ammonium fluoride (NH4F, 216011) and potassium fluoride (KF, 402931) were all purchased from Sigma-Aldrich. LiOH·H2O (80074718), MgCl2·6H2O (10012817) and Mn(ac)2·4H2O (A22100702) were purchased from Sinopharm Chemical Reagent Beijing, Co., Ltd. Zr(acac)4 (Z107220) was purchased from Aladdin Chemistry Co., Ltd. Other analytical grade chemicals, such as cyclohexane, ethanol and sodium hydroxide, were purchased from Sinopharm Chemical Reagent Beijing, Co., Ltd.
Synthesis of NaGdF4:Yb,Er Nanocrystals
The NaGdF4:Yb,Er nanocrystals were synthesized through the coprecipitation reaction at high temperature according to our previous works with slight modification (Liu et al., 2016). Typically, GdCl3·6H2O (0.48 mmol), YbCl3·6H2O (0.108 mmol), and ErCl3·6H2O (0.012 mmol) were mixed with 4 mL of OA as the coordinating ligand and 16 mL of ODE as the non-coordinating solvent in a 100 mL 3-necked flask. The mixture was heated to 150°C under a vacuum and then kept at this temperature approximately for 60 min for forming a homogeneous solution. 10 mL of methanol solution containing NaOH (1.8 mmol) and NH4F (1.8 mmol) was added dropwise after the solution was cooled down to 50°C. Then the reaction system was stirred at 50°C for another 30 min. After that, the methanol was removed under a vacuum and the solution was kept at 110°C for 10 min until there were no bubbles in the reaction system. Subsequently, the reaction temperature was improved to 300°C with the rate of 20°C/min, under a gentle flow of nitrogen protection. And the reaction was held for 1 h at 300°C. Finally, the reaction system was cooled to room temperature. The nanocrystals were precipated by ethanol, collected by centrifugation for several times and then re-dispersed in cyclohexane for further use.
Synthesis of Non-ln Ions Doped NaGdF4:Yb,Er Nanocrystals
The rare-earth nanocrystals doped with different non-Ln metal ions were synthesized following a similar process of the preparation of NaGdF4:Yb,Er nanocrystals. In the case of Zr4+-doped NaGdF4:Yb,Er nanocrystals, different feeding ratios of Zr4+ ions (defined as the molar ratios of Zr4+ precursor to the amount of total cation precursors) were used, namely: 3.0, 5.0, 10.0, 15.0%. In detail, Zr(acac)4 (x mmol, x = 0.018, 0.03, 0.06, 0.09), GdCl3·6H2O (0.48-x mmol), YbCl3·6H2O (0.108 mmol), and ErCl3·6H2O (0.012 mmol) were mixed with 4 mL of OA and 16 mL of ODE in a 100 mL 3-necked flask. While the Sc3+, Mg2+ or Mn2+-doped NaGdF4:Yb,Er nanocrystals were synthesized similar to the Zr4+-doped nanocrystals (Zr4+ precursor:10.0%) by replacing Zr(acac)4 with ScCl3·6H2O, MgCl2·6H2O or Mn(ac)2·4H2O, respectively. In addition, for the Mn2+-doped NaGdF4:Yb,Er nanoparticles, the precursors were mixed with 3.8 mL of OA and 0.2 mL OM as the coordinating ligand. The growth of the nanocrystals and the following purification procedures were the same as those for the NaGdF4:Yb,Er nanocrystals.
In the case of Li+-doped NaGdF4:Yb,Er nanocrystals, after forming a homogeneous solution of rare-earth chloride at 50°C, 10 ml of methanol solution containing of NaOH (1.62 mmol), LiOH·H2O (0.18 mmol) and NH4F (1.8 mmol) was added in the reaction system for preparing Li+-doped NaGdF4:Yb,Er nanocrystals. Other experimental steps were the same to the synthesis of above-mentioned nanocrystals. While in the case of NaGdF4:Yb,Er nanoparticles doped with K+, the methanol solution was consisted of NaOH (1.62 mmol), KF (0.18 mmol) and NH4F (1.62 mmol). Other experimental steps were the same to the synthesis of above-mentioned nanoparticles.
Synthesis of Li+ and Zr4+ Co-doped NaGdF4:Yb,Er Nanocrystals
GdCl3·6H2O (0.42 mmol), Zr(acac)4 (0.06 mmol), YbCl3·6H2O (0.108 mmol), and ErCl3·6H2O (0.012 mmol) were mixed with 4 mL of OA and 16 mL of ODE. After forming a homogeneous solution of rare-earth chloride at 50°C, 10 ml of methanol solution containing of NaOH (1.62 mmol), LiOH·H2O (0.18 mmol) and NH4F (1.8 mmol) was added in the reaction system for preparing Li+ and Zr4+ co-doped NaGdF4:Yb,Er nanocrystals. Other experimental steps were the same to the synthesis of above-mentioned nanocrystals.
Structural and Optical Characterization of Nanocrystals
Transmission electron microscopy (TEM) measurements were carried out with JEM-100CXII at 100 KV and Hitachi HT7700 at 120 KV for characterizing the particle shape and size, and selected area electron diffractions (SAED) were taken for the characterization of crystalline structure. The particle size was determined with ImageJ by counting more than 300 nanoparticles per sample. In addition, X-ray diffraction (XRD) measurements were carried out on a Regaku D/Max-2500 diffractometer under Cu Kα1 radiation (λ = 1.54056 Å) for further characterizing the phase structure of the resultant nanocrystals. The concentrations of metal ions in different systems was determined by using an inductively coupled plasma atomic emission spectrometer (ICP-AES 6300DV) after the particles were eroded with certain concentrated mixture of concentrated nitric acid and hydrogen peroxide. The up- and down-conversion luminescence spectra were measured by a Cary Eclipse fluorescence spectrophotometer and Edinburgh Instruments FLS 920 equipped with 980 nm CW laser diodes (MDL-III-980 nm) as the excitation sources, respectively. The luminescence spectra of different samples are normalized according to the concentration of Er3+ serving as the emissive centers, and the excitation power (2 W/cm2) remain unchanged for comparing the luminescence intensities of different samples dispersed in cyclohexane. The transient up- and down-conversion luminescence of different samples dispersed in cyclohexane was recorded on FLS 920 equipped with 980 nm pulsed laser diodes (the excitation power: 2 W/cm2, pulse frequency: 100 Hz, pulse width: 3 μs), with the former detected by HAMAMATSU PMT (R928-P) detector and the latter detected by HAMAMATSU NIRPMT (R5509) detector.
Data Availability Statement
All datasets generated for this study are included in the article/Supplementary Material.
Author Contributions
MG, CL, LJ, and YL were responsible for designing experiments, put forward the innovation of this work, and wrote the paper. YL carried out the experiments and analyzed the data with the support from MG, LJ, and CL. All the authors contributed to the discussion of results and the design of figures.
Funding
This work was financially supported by the National Key Research and Development Program of China (2018YFA0208800), National Natural Science Foundation of China (NSFC) (81771902, 81720108024, 81530057, 81671755, and 81671754), the Youth Innovation Promotion Association CAS (2018042), CAS-VPST Silk Road Science Fund 2019 (GJHZ201963), and State Key Laboratory of Luminescence and Applications (SKLA-2019-01).
Conflict of Interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
Supplementary Material
The Supplementary Material for this article can be found online at: https://www.frontiersin.org/articles/10.3389/fchem.2020.00832/full#supplementary-material
References
Ai, X., Wang, Z., Cheong, H., Wang, Y., Zhang, R., Lin, J., et al. (2019). Multispectral optoacoustic imaging of dynamic redox correlation and pathophysiological progression utilizing upconversion nanoprobes. Nat. Commun. 10:1087. doi: 10.1038/s41467-019-09001-7
Antaris, A. L., Chen, H., Cheng, K., Sun, Y., Hong, G., Qu, C., et al. (2016). A small-molecule dye for NIR-II imaging. Nat. Mater. 15, 235–242. doi: 10.1038/nmat4476
Boyer, J. C., Vetrone, F., Capobianco, J. A., Speghini, A., and Bettinelli, M. (2004). Variation of fluorescence lifetimes and judd-ofelt parameters between Eu3+doped bulk and nanocrystalline cubic Lu2O3. J. Phys. Chem. B 108, 20137–20143. doi: 10.1021/jp0480504
Buonsanti, R., and Milliron, D. J. (2013). Chemistry of doped colloidal nanocrystals. Chem. Mater. 25, 1305–1317. doi: 10.1021/cm304104m
Chen, B. K., Susha, A. S., Reckmeier, C. J., Kershaw, S. V., Wang, Y. T., Zou, B. S., et al. (2017). Mesoporous aluminum hydroxide synthesized by a single-source precursor-decomposition approach as a high-quantum-yield blue phosphor for UV-pumped white-light-emitting diodes. Adv. Mater. 29:8. doi: 10.1002/adma.201604284
Chen, G., Liu, H., Liang, H., Somesfalean, G., and Zhang, Z. (2008). Upconversion emission enhancement in Yb3+/Er3+-Codoped Y2O3 nanocrystals by tridoping with Li+ Ions. J. Phys. Chem. C 112, 12030–12036. doi: 10.1021/jp804064g
Chen, G., Qiu, H., Prasad, P. N., and Chen, X. (2014). Upconversion nanoparticles: design, nanochemistry, and applications in theranostics. Chem. Rev. 114, 5161–5214. doi: 10.1021/cr400425h
Chen, G., Yang, C., and Prasad, P. N. (2013). Nanophotonics and nanochemistry: controlling the excitation dynamics for frequency up- and down-conversion in lanthanide-doped nanoparticles. Acc. Chem. Res. 46, 1474–1486. doi: 10.1021/ar300270y
Chen, Q. S., Xie, X. J., Huang, B. L., Liang, L. L., Han, S. Y., Yi, Z. G., et al. (2017). Confining excitation energy in Er3+-sensitized upconversion nanocrystals through Tm3+-mediated transient energy trapping. Angew. Chem., Int. Ed. 56, 7605–7609. doi: 10.1002/anie.201703012
Cheng, Q., Sui, J., and Cai, W. (2012). Enhanced upconversion emission in Yb3+ and Er3+ codoped NaGdF4 nanocrystals by introducing Li+ ions. Nanoscale 4, 779–784. doi: 10.1039/c1nr11365h
Clarke, C., Liu, D., Wang, F., Liu, Y., Chen, C., Ton-That, C., et al. (2018). Large-scale dewetting assembly of gold nanoparticles for plasmonic enhanced upconversion nanoparticles. Nanoscale 10, 6270–6276. doi: 10.1039/C7NR08979A
Dong, H., Sun, L. D., and Yan, C. H. (2013). Basic understanding of the lanthanide related upconversion emissions. Nanoscale 5, 5703–5714. doi: 10.1039/c3nr34069d
Dong, H., Sun, L. D., and Yan, C. H. (2015). Energy transfer in lanthanide upconversion studies for extended optical applications. Chem. Soc. Rev. 44, 1608–1634. doi: 10.1039/c4cs00188e
Du, P., Kim, E.-J., and Yu, J. S. (2018). Local symmetry distortion-induced enhancement of upconversion luminescence in Gd2O3:Ho3+/Yb3+ /Zn 2+ nanoparticles for solid-state lighting and bioimaging. Curr. Appl. Phys. 18, 310–316. doi: 10.1016/j.cap.2018.01.004
Fan, Y., Liu, L., and Zhang, F. (2019). Exploiting lanthanide-doped upconversion nanoparticles with core/shell structures. Nano Today 25, 68–94. doi: 10.1016/j.nantod.2019.02.009
Fan, Y., Wang, P., Lu, Y., Wang, R., Zhou, L., Zheng, X., et al. (2018). Lifetime-engineered NIR-II nanoparticles unlock multiplexed in vivo imaging. Nat. Nanotechnol. 13, 941–946. doi: 10.1038/s41565-018-0221-0
Fischer, S., Mehlenbacher, R. D., Lay, A., Siefe, C., Alivisatos, A. P., and Dionne, J. A. (2019). Small alkaline-earth-based core/shell nanoparticles for efficient upconversion. Nano Lett. 19, 3878–3885. doi: 10.1021/acs.nanolett.9b01057
Han, S., Deng, R., Xie, X., and Liu, X. (2014). Enhancing luminescence in lanthanide-doped upconversion nanoparticles. Angew. Chem. Int. Ed. Engl. 53, 11702–11715. doi: 10.1002/anie.201403408
He, S., Johnson, N. J. J., Nguyen Huu, V. A., Cory, E., Huang, Y., Sah, R. L., et al. (2017). Simultaneous enhancement of photoluminescence, MRI relaxivity, and CT contrast by tuning the interfacial layer of lanthanide heteroepitaxial nanoparticles. Nano Lett. 17, 4873–4880. doi: 10.1021/acs.nanolett.7b01753
Huang, J., Hou, Y., Liu, C., Jing, L., Ma, T., Sun, X., et al. (2015). Chemical spacer design for engineering the relaxometric properties of core–shell structured rare earth nanoparticles. Chem. Mater. 27, 7918–7925. doi: 10.1021/acs.chemmater.5b02875
Huang, P., Zheng, W., Gong, Z., You, W., Wei, J., and Chen, X. (2019). Rare earth ion– and transition metal ion–doped inorganic luminescent nanocrystals: from fundamentals to biodetection. Materials Today Nano 5:100031. doi: 10.1016/j.mtnano.2019.100031
Johnson, N. J., He, S., Diao, S., Chan, E. M., Dai, H., and Almutairi, A. (2017). Direct evidence for coupled surface and concentration quenching dynamics in lanthanide-doped nanocrystals. J. Am. Chem. Soc. 139, 3275–3282. doi: 10.1021/jacs.7b00223
Kar, A., and Patra, A. (2012). Impacts of core-shell structures on properties of lanthanide-based nanocrystals: crystal phase, lattice strain, downconversion, upconversion and energy transfer. Nanoscale 4, 3608–3619. doi: 10.1039/c2nr30389b
Lei, L., Chen, D., Huang, P., Xu, J., Zhang, R., and Wang, Y. (2013). Modifying the size and uniformity of upconversion Yb/Er:NaGdF4 nanocrystals through alkaline-earth doping. Nanoscale 5, 11298. doi: 10.1039/c3nr03497f
Li, X., Shen, D., Yang, J., Yao, C., Che, R., Zhang, F., et al. (2013). Successive layer-by-layer strategy for multi-shell epitaxial growth: shell thickness and doping position dependence in upconverting optical properties. Chem. Mater. 25, 106–112. doi: 10.1021/cm3033498
Li, Y., Zhang, P., Ning, H., Zeng, J., Hou, Y., Jing, L., et al. (2019). Emitting/sensitizing ions spatially separated lanthanide nanocrystals for visualizing tumors simultaneously through up- and down-conversion near-infrared II luminescence in vivo. Small 15:e1905344. doi: 10.1002/smll.201905344
Liu, C., Gao, Z., Zeng, J., Hou, Y., Fang, F., Li, Y., et al. (2013). Magnetic/upconversion fluorescent NaGdF4:Yb,Er nanoparticle-based dual-modal molecular probes for imaging tiny tumors in vivo. ACS Nano 7, 7227–7240. doi: 10.1021/nn4030898
Liu, C., Hou, Y., and Gao, M. (2014). Are rare-earth nanoparticles suitable for in vivo applications? Adv. Mater. 26, 6922–6932. doi: 10.1002/adma.201305535
Liu, C., Qi, Y., Qiao, R., Hou, Y., Chan, K., Li, Z., et al. (2016). Detection of early primary colorectal cancer with upconversion luminescent NP-based molecular probes. Nanoscale 8, 12579–12587. doi: 10.1039/c5nr07858j
Liu, Y., Luo, W., Li, R., Liu, G., Antonio, M. R., and Chen, X. (2008). Optical Spectroscopy of Eu3+Doped ZnO Nanocrystals. J. Phys. Chem. C 112, 686–694. doi: 10.1021/jp077001z
Lu, M., Guo, J., Sun, S., Lu, P., Wu, J., Wang, Y., et al. (2020). Bright CsPbI3 perovskite quantum dot light-emitting diodes with top-emitting structure and a low efficiency roll-off realized by applying zirconium acetylacetonate surface modification. Nano Lett. 20, 2829–2836. doi: 10.1021/acs.nanolett.0c00545
Ma, C., Xu, X., Wang, F., Zhou, Z., Liu, D., Zhao, J., et al. (2017). Optimal sensitizer concentration in single upconversion nanocrystals. Nano Lett. 17, 2858–2864. doi: 10.1021/acs.nanolett.6b05331
Shannon, R. D., and Fischer, R. X. (2016). Empirical electronic polarizabilities of ions for the prediction and interpretation of refractive indices: oxides and oxysalts. Am. Mineral. 101, 2288–2300. doi: 10.2138/am-2016-5730
Shen, J., Zhao, L., and Han, G. (2013). Lanthanide-doped upconverting luminescent nanoparticle platforms for optical imaging-guided drug delivery and therapy. Adv. Drug Deliver. Rev 65, 744–755. doi: 10.1016/j.addr.2012.05.007
Stroyuk, O., Raevskaya, A., and Gaponik, N. (2018). Solar light harvesting with multinary metal chalcogenide nanocrystals. Chem. Soc. Rev. 47, 5354–5422. doi: 10.1039/c8cs00029h
Sun, Q. C., Mundoor, H., Ribot, J. C., Singh, V., Smalyukh, I. I., and Nagpal, P. (2014). Plasmon-enhanced energy transfer for improved upconversion of infrared radiation in doped-lanthanide nanocrystals. Nano Lett. 14, 101–106. doi: 10.1021/nl403383w
Tang, H., Xu, Y., and Cheng, X. (2020a). Growth and enhanced upconversion luminescence intensity of Mg2+ and Cr3+ co-doped beta-NaYF4:Yb3+/Er3+ microcrystals. J. Solid State Chem. 285:121229. doi: 10.1016/j.jssc.2020.121229
Tang, H., Zhou, H., and Cheng, X. (2020b). Effects of Ca2+ doping on upconversion luminescence intensity and crystal field asymmetry of beta-NaYF4:Yb3+/Er3+ microcrystals. J. Lumin. 221:117086. doi: 10.1016/j.jlumin.2020.117086
Tang, J., Chen, L., Li, J., Wang, Z., Zhang, J., Zhang, L., et al. (2015). Selectively enhanced red upconversion luminescence and phase/size manipulation via Fe3+ doping in NaYF4:Yb,Er nanocrystals. Nanoscale 7, 14752–14759. doi: 10.1039/c5nr04125b
Tu, D., Liu, Y., Zhu, H., Li, R., Liu, L., and Chen, X. (2013). Breakdown of crystallographic site symmetry in lanthanide-doped NaYF4 crystals. Angew. Chem. Int. Ed. Engl. 52, 1128–1133. doi: 10.1002/anie.201208218
Tu, L., Liu, X., Wu, F., and Zhang, H. (2015). Excitation energy migration dynamics in upconversion nanomaterials. Chem. Soc. Rev. 44, 1331–1345. doi: 10.1039/c4cs00168k
Verma, P., Sarkar, D., Rajput, P., Singh, M. N., Sharma, R., and Giri, S. (2020). Synchrotron-based X-ray analysis: relating compressive lattice strain with the photoluminescence intensity of Li+-doped beta-NaYF4:Yb3+/Ln3+ (Ln3+ = Ho3+/Er3+/Tm3+) Upconversion Crystals. Crystal Growth Design 20, 468–478. doi: 10.1021/acs.cgd.9b01426
Vetrone, F., Naccache, R., Mahalingam, V., Morgan, C. G., and Capobianco, J. A. (2009). The active-core/active-shell approach: a strategy to enhance the upconversion luminescence in lanthanide-doped nanoparticles. Adv. Funct. Mater. 19, 2924–2929. doi: 10.1002/adfm.200900234
Walsh, B. M., Barnes, N. P., and Di Bartolo, B. (1998). Branching ratios, cross sections, and radiative lifetimes of rare earth ions in solids: application to Tm3+ and Ho3+ ions in LiYF4. J. Appl. Phys. 83, 2772–2787. doi: 10.1063/1.367037
Wang, F., Wang, J., and Liu, X. (2010). Direct evidence of a surface quenching effect on size-dependent luminescence of upconversion nanoparticles. Angew. Chem. Int. Ed. Engl. 49, 7456–7460. doi: 10.1002/anie.201003959
Wang, J., Wang, F., Wang, C., Liu, Z., and Liu, X. (2011). Single-band upconversion emission in lanthanide-doped KMnF3 nanocrystals. Angew. Chem. Int. Ed. 50, 10369–10372. doi: 10.1002/anie.201104192
Werts, M. H. V., Jukes, R. T. F., and Verhoeven, J. W. (2002). The emission spectrum and the radiative lifetime of Eu3+ in luminescent lanthanide complexes. Phys. Chem. Chem. Phys. 4, 1542–1548. doi: 10.1039/b107770h
Xu, J., Gulzar, A., Yang, P., Bi, H., Yang, D., Gai, S., et al. (2019). Recent advances in near-infrared emitting lanthanide-doped nanoconstructs: mechanism, design and application for bioimaging. Coordin. Chem. Rev. 381, 104–134. doi: 10.1016/j.ccr.2018.11.014
Yi, G. S., and Chow, G. M. (2007). Water-soluble NaYF4:Yb,Er(Tm)/NaYF4/polymer core/shell/shell nanoparticles with significant enhancement of upconversion fluorescence. Chem. Mater. 19, 341–343. doi: 10.1021/cm062447y
Zeng, S., Yi, Z., Lu, W., Qian, C., Wang, H., Rao, L., et al. (2014). Simultaneous realization of phase/size manipulation, upconversion luminescence enhancement, and blood vessel imaging in multifunctional nanoprobes through transition metal Mn2+ doping. Adv. Funct. Mater. 24, 4051–4059. doi: 10.1002/adfm.201304270
Zhang, Y., Chen, B., Xu, S., Li, X., Zhang, J., Sun, J., et al. (2018). A universal approach for calculating the Judd-Ofelt parameters of RE3+ in powdered phosphors and its application for the beta-NaYF4:Er3+/Yb3+ phosphor derived from auto-combustion-assisted fluoridation. Phys. Chem. Chem. Phys. 20, 15876–15883. doi: 10.1039/c8cp02317d
Keywords: non-lanthanide doping, up- and down-conversion luminescence, crystal field, valence state effects, rare-earth nanocrystals, lanthanide emitters
Citation: Li Y, Liu C, Zhang P, Huang J, Ning H, Xiao P, Hou Y, Jing L and Gao M (2020) Doping Lanthanide Nanocrystals With Non-lanthanide Ions to Simultaneously Enhance Up- and Down-Conversion Luminescence. Front. Chem. 8:832. doi: 10.3389/fchem.2020.00832
Received: 31 May 2020; Accepted: 07 August 2020;
Published: 23 September 2020.
Edited by:
Qin Li, Griffith University, AustraliaReviewed by:
Baojiu Chen, Dalian Maritime University, ChinaYiqing Lu, Macquarie University, Australia
Copyright © 2020 Li, Liu, Zhang, Huang, Ning, Xiao, Hou, Jing and Gao. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Chunyan Liu, bGl1Y2h5JiN4MDAwNDA7aWNjYXMuYWMuY24=; Lihong Jing, amluZ2xoJiN4MDAwNDA7aWNjYXMuYWMuY24=; Mingyuan Gao, Z2FvbXkmI3gwMDA0MDtpY2Nhcy5hYy5jbg==