Abstract
The fast consumption of fossil energy accompanied by the ever-worsening environment urge the development of a clean and novel energy storage system. As one of the most promising candidates, the supercapacitor owns unique advantages, and numerous electrodes materials have been exploited. Hence, biomass-derived porous carbon materials (BDPCs), at low cost, abundant and sustainable, with adjustable dimension, superb electrical conductivity, satisfactory specific surface area (SSA) and superior electrochemical stability have been attracting intense attention and highly trusted to be a capable candidate for supercapacitors. This review will highlight the recent lab-scale methods for preparing BDPCs, and analyze their effects on BDPCs' microstructure, electrical conductivity, chemical composition and electrochemical properties. Future research trends in this field also will be provided.
Introduction
The ever-growing population, crisis of energy shortage, and environmental pollution caused by burning fossil fuels have brought about different kinds of problems, and they stimulate the process of developing clean and sustainable energy, such as solar energy, wind power etc. (Dunn et al., 2011; Chu and Majumdar, 2012; Dubal et al., 2015; Kamat, 2015; Kazmerski, 2016; Peng et al., 2017). All these closely relate to the development of the advanced energy storage system. Until now, for electrochemical energy storage systems, for example, various rechargeable batteries and supercapacitorsare identified as the most promising energy storage devices (Chmiola et al., 2006; Miller and Simon, 2008; Kim et al., 2010; Cheng et al., 2011; Xu et al., 2014; Gogotsi, 2015). Although batteries have a relatively longer life cycle, (< 1,000 cycles), high-energy density and satisfactory rate performance, distinct from rechargeable batteries, supercapacitors possess the following characteristics: high-power energy, extremely long cycle life (>100,000 cycles) without losing capacitance and safety, it is quite essential to bridge the gap between conventional electrochemical capacitors and rechargeable batteries, and meet the demand of electric vehicles which require high power (Liu et al., 2018a; Xu et al., 2018).
Basically, supercapacitors can be classified under two categories according to their charge storage mechanism, which further affects the power density of supercapacitors. The electrical double layer (EDL) capacitance and pseudo-capacitance are quite different. For the former, charges are stored through ions' adsorption by electro-static interaction at the near-surface of active materials, where EDL forms; while the energy storage/release mechanism for pseudo-capacitance is by means of redox reaction, ions insertion/extrusion and under-potential depositions (Augustyn et al., 2014; Mccloskey, 2015). Both the aforementioned supercapacitors require chemical and structure stability, outstanding electrical conductivity, and high SSA. Hence, to satisfy the requirement of high capacity and superior rate performance for supercapacitors, the exploitation of advanced electrode materials with low cost, adjustable composition, and microstructure (especially pore structure) turns increasingly important.
In the past decades, thanks to the excellent conductivity property, high SSA, variable pore structure and porosity, carbon materials, such as commercial activated carbons (Chan et al., 2004; Jänes et al., 2007; Zhang and Zhao, 2009; Lv et al., 2011; Wang et al., 2014), graphene (Wang et al., 2009; Liu et al., 2010; Zhang et al., 2010; Cao et al., 2011), graphene oxide (GO) (Li et al., 2013; Li and Yang, 2014; Down et al., 2018), carbon nanotubes (CNTs) (An et al., 2001; Futaba et al., 2006; Pushparaj et al., 2007), porous carbon (PC) (Lee et al., 2000; Vix-Guterl et al., 2005; Hou et al., 2015) and their composites (Salunkhe et al., 2015) have achieved various kinds of essential accomplishments on their volumetric performance. However, their high production cost, complicated and unsustainable preparation process greatly limited their wide application. Besides, the gravimetric capacitance for CAs is keeping at a relatively low level for several decades, that should be ascribed to the rich micro-pores, which are hard accessible for ions, especially at high-current density condition (Li et al., 2014). Therefore, enlarging the ion-accessible area through creating a suitable hierarchical porous structure is a key factor for achieving high specific capacitance (Cs) and rate performance (Zhao et al., 2016). Biomass materials abundantly present across our surroundings, and their low cost, accessible, environmentally friendly, and recyclable properties ensure they are ideal candidates for resources of carbon materials. At the same time, their naturally hierarchical porous structure and various elements (N, S) facilitate electrolyte penetration and extra active sites' generation, respectively (Chen et al., 2016).
In this review, we provide a summary of the recent and significant advances in hierarchical porous carbon (HPC) derived from biomass materials, emphasizing on the relationship between interconnectivity of the pore structure and electrochemical efficiency, and synthetic strategies for preparing HPC as supercapacitors. Finally, the current challenges and future directions are briefly discussed.
Relation Between Pore Features and Capacities
In general, the capacitance of PC materials relies on the pore size distribution, connectivity and hydrophilicity; these factors will be further influencing the ion diffusion process and energy density of active materials. According to the findings by Dubinin (1960) and the classification by the International Union of Pure and Applied Chemistry (IUPAC) in 1985 (Sing, 1985), pores with different widths can be divided among three categories: macropores (>50 nm), mesopores (2–50 nm) and micropores (< 2 nm). With the development of porous materials, three new pore types have been classified since 2015, they are nanopores (< 100 nm), supermicropores (0.7–2 nm) and ultramicropores (< 0.7 nm).
Pore Size Distribution
Although intense efforts are focused on improving the surface area and redox active sites of PC materials, optimization of pore size distribution is also an effective mode to enhance capacitance, especially for EDL capacitors. Generally, nanoporous carbons consist of pores ranging from micropores to mesopores, and most of them cannot maintain long-range ordering, or be accessible to ions from the electrolyte, though we know the electrochemical performance of PC is dependent on the interface of carbon and electrolyte. The macropore, mesopore and micropore have different functions in the electrochemical charge/discharge process. Macropores serve as ion-buffing reservoirs for meso- and micropores; mesopores provide abundant transport channels for ions' diffusion; in spite of some regions of micropores are inaccessible to adsorb ions, it still affects the charge status through controlling the diffusion of ions and molecular sieve effects, and then changing the capacitance of PC materials (Liu et al., 2018c); in addition, as the size of pores decreases toward <1 nm, an anomalous capacitance increase occurred in the organic electrolyte due to ion dissolution. Chmiola and co-workers reported that PC could achieve the highest capacitance as its average pore size matched the size of desolvated ions (Chmiola et al., 2006). Kondrat (Kondrat et al., 2012) found that different carbon materials with the same average pore size will display very different capacitive properties, because of the difference in pore size distribution; besides, for the monodisperse porous electrode, its energy density and pore size do not fit a non-monotonic function (Figure 1). Moreover, Cheng (Wang et al., 2008) believed that high micropore volume and the micropore-to-total-pore ratio are crucial for gaining a high-rate electrochemical performance of PC.
Figure 1
Pore Connectivity
interconnected pores at different size dimensions are qualified as a hierarchical porous structure, which facilitates electrolyte infiltration and ion diffusion through a different pore canal (Borchardt et al., 2013). Until now, it is still a big challenge to construct carbon materials with 3D-interconnected, long-range order macroporous and mesoporous structures. These structures, combined with decent SSA and proper pore size distribution, allow efficient diffusion of any substance, such as electrolytes, ions etc., to the interior space of all channels. The strategies for fabrication HPC mainly includes templating (hard/soft) (Yuan et al., 2016; Xiong et al., 2017; Zhu et al., 2017) and non-templating ways (Lv et al., 2012), while these methods are time-consuming and highly costly. As a promising renewable resource, Biomass always possess a naturally interconnected, multichannel and porous structure, hence, they are the excellent candidates for preparing HPC. Wang and co-workers used pomelo peel as the carbon sources, in virtue of its foamy fibrous layer and abundant oxygen-containing functional groups, HPC was obtained after KOH activation, it gained a capacitance of 222.6 F/g at relatively low discharge current density (0.5 A/g), at the same time, it maintained a good rate of performance and a suitable cycling stability (Li et al., 2017a).
Pores' Hydrophilicity
Until recently, the charging mechanism for supercapacitors is derived from ions into the PC network by applied potential driving. Hence, the pore wettability, also named as surface hydrophobic/hydrophilic balance, closely relates to pores' surface functional groups, and has a great impact on the penetration of guest species into the pore systems and transfer of electrons (Xiao et al., 2016). Therefore, the functionalization of PC materials through surface modification gradually becomes an important issue to achieve appropriate wettability (Figure 2). The modification techniques always involve post-treatment of PC materials in oxidizing media, or doping carbons with oxygen, nitrogen and other elements (Lin et al., 2015; Chen et al., 2017b). Generally, N- and O-doping, introduced by grafting different functional groups, facilitate adsorption of ions and further improve the hydrophilicity of the carbon matrix. Therefore, moderate oxidation accompanied by heteroatom doping provide faradic pseudocapacitance, and then increase the capacitance value of electrode materials. However, overoxidation results in collapse of pore structure and large interface resistance (Wei et al., 2016). Moreover, most natural biomass contains nitrogen, boron, sulfur and other trace elements, which would be doped into the carbon framework as heteroatoms, and that will generate a more active site, and decrease the hydrophobicity of PC. Li utilized corncob as a precursor, and obtained nitrogen-doped activated carbons with N content up to 4 wt%, the corresponding hybrid-type supercapacitor achieved high-energy density and rate performance (Li et al., 2015a).
Figure 2
Brief Overview of Fabrication Strategies for PC
Up to now, various synthetic methods have been developed for preparing biomass-derived PC. The carbonization methods, such as pyrolysis (Dubal et al., 2016) and hydrothermal carbonization (Enterría et al., 2016), are used earliest to obtain PC. The pyrolysis is a dry-carbonization reaction, which usually takes place in an inert atmosphere or low oxygen environment at an elevated temperature condition (300–900°C), the main components of biomass are gradually transferred into biochar through a series of reaction, such as cross-linking depolymerization, fragmentation reactions etc. The performance of biochar depends on the reaction temperature, time and catalyst (Li et al., 2016b); For the hydrothermal carbonization, it is carried out in aqueous environment at elevated temperature (< 300°C) and autogenous high pressure, it is a chemical process for conversion of biomass to carbonaceous materials, whose properties are determined by reaction temperature, time, pressure, and water/biomass ratio. Furthermore, Compared with the pyrolysis reaction, hydrothermal carbonization results in higher biochar yield. However, biochars obtained through the aforementioned methods have low SSA and porosity. Hence, as the most common strategies for increasing SSA of carbon materials, activation, including physical and chemical activation, have been wildly used.
Physical activation is carried out at a high temperature (>700°C) in the presence of gases like CO2, H2O, air and ozone (Abioye and Ani, 2015; Chang et al., 2016; Lota et al., 2016). The process of physical activation has two steps: firstly, carbonization happens at a low temperature in an inert atmosphere, and during this process, volatile matters are eliminated and biochar is formed. Subsequently, gasification reaction leads to the formation of abundant open pores because of the introduction of oxidizing gas at a high temperature. It should be noteworthy that increasing reaction temperature and prolonging treating time are helpful to improve the porosity of carbon materials, while the pore size distribution will be broadened.
Prior to carbonization, biochar is pre-mixed with certain chemicals, such as an acid (Sun et al., 2015), strong base (Qu et al., 2015), or a salt (Sevilla and Fuertes, 2016), then the mixture is carbonized at relatively low temperatures (450–900°C). Although there are drawbacks for chemical activation, for example, high cost, apparatus corrosion, and non-recoverable chemicals, it is still preferred over physical activation owing to its lower reaction temperature, shorter reaction time and larger SSA. Among various kinds of activating reagents, KOH (Lv et al., 2011) is the most wildly used chemical. The activation mechanism of KOH activation (Figure 3) can be summarized and shown as the following reaction equations.
Figure 3
Cellulose-Derived PC
As the most abundant and sustainable natural polymer, cellulose is the main component of green plants' primary cell wall and consists of a linear chain of D-glucose. Cellulose fibers exhibit high surface area and aspect ratios, excellent mechanics and flexibility, broad chemical-modification capacity, so it has attracted intense attention in the past several years for supercapacitor (Yang et al., 2015; Yu et al., 2016). Generally, according to the origin of cellulose, it can be classified in two ways: commercial cellulose and isolated cellulose from lignocellulose for PC precursor. After carbonization and activation through a physical or chemical process at elevated temperature, then PC was gained. Although they have extremely high SSA, compared with HPC, it exhibited limited Cs because of low wettability, slow ions' diffusion rate and relatively small amount of the effective active site. Hence, recently, many efforts have been focusing on the fabrication of HPC derived from cellulose.
The unique structure of carbon aerogels provides high SSA, hierarchical porous structure, interconnected macro-/meso-/micropores, efficient ions diffusion rate, and abundant active sites. Nanocellulose microcrystalline would be gelling at the base condition, after freeze-drying and CO2 activation process, carbon aerogel with interconnected 3D nanostructure could be prepared. The final products showed high SSA (1,873 m2/g) and high pore volume (2.65 cm3/g); besides, the Cs reached 302 F/g and 205 F/g at 0.5 A/g and 20 A/g, respectively (Zu et al., 2016). “leavening” strategy (Figure 4) is applicable to various biomass and their derivatives, the corresponding electrode materials exhibited a Cs of 253 F/g with superior cycling stability (Deng et al., 2015). Zhuo et al. synthesized HPC through a dissolving-gelling process, after carbonization process, carbon aerogel with abundant macropores, mesopores and micropores was obtained, and gained high Cs of 328 F/g at 0.5 A/g with 96% of the capacitance retention after 5,000 cycles (Zhuo et al., 2016). Sodium carboxymethyl cellulose aerogels derived PC could be obtained through sol-gel and KOH activation, its relative low Cs (152 F/g at 0.5 A/g) might be attributed to the limited SSA (<500 m2/g) (Yu et al., 2016). What's more, Long et al. cellulose nanofibrils and short cellulose nanofibrils were assembled into macro/micro/mesoporous structure by Li and co-workers, who found the hierarchical structure maintained high surface area (1,244 cm2/g), good Cs (170 F/g) at high current densities (Li et al., 2017b). Waste paper is also a promising candidate for preparing PC. Kraft pulp was mixed with KOH solution and freeze-dried, then the mixture was calcined at an elevated temperature under an inert atmosphere. Dense graphene-like HPC was fabricated, and its gravimetric and volumetric Cs is 309 F/g and 309 F/cm3 at 1 A/g, respectively (Mo et al., 2018).
Figure 4
It is believed that increasing surface functional groups into the carbon framework contribute to the enhancement of the capacitance of supercapacitors. Hence, introducing of N, B, P, and O, which act as electron donor or electron acceptor, have the following effects: improving wettability between PC and electrolyte; facilitate the binding between carbon materials and ions; enhancing the active sites in the carbon framework (Chen et al., 2013, 2017d; Wu et al., 2015; An et al., 2017). Contrary to oxygenic functional groups, N-containing functional groups own basic characters, which leads to donor-acceptor properties, and improves the final electrochemical properties of electrode materials (Wang et al., 2008). As the carbon sources and as a template, cellulose nanocrystals were used to control the growth of melamine-formaldehyde, then rod-like porous N-doped carbon particles were fabricated; they achieved 352 F/g at 5 A/g and maintained over 95% Cs retention after 2000 cycles (Wu et al., 2015). Through pyrolysis and activation procedure, PC nanosheets (PCN) were doped by N and S, the co-doped PCN had a Cs of 298 and 233 F/g at charge/discharge current density of 0.5 and 50 A/g. Besides, only 2% capacitance lost after 10,000 cycles (Li et al., 2016b). Phosphorus (P) doped HPC possessed outstanding rate capability, and it showed a Cs of 133 F/g (146 mF/cm2) at 10 A/g with ~98% capacitance retention after 10,000 cycles (Yi et al., 2017).
Lignin-Derived PC
As the most abundant natural aromatic polymer and the second raw material from plants, lignin, with a production ~ 50 million tons per year, is known as one of the most promising candidates for carbon sources considering environmental and economic aspects (Suhas and Carrott, 2007). Recently, the lignin-based PC nanocomposite gradually has attracted much attention because of its excellent electrochemical performance (Kai et al., 2016; Ma et al., 2016; Wang et al., 2016a). Generally, it is quite difficult to isolate the lignin because of the potential oxidation and condensation reaction during the isolation process; besides, the mass production and purity of lignin, isolated through hydrolysis or solubilization of plants, also limit the wide application of lignin-based PC for supercapacitor. However, series of works have been published and some progress has been made. Physical and chemical activations are the most common strategy to prepare lignin-based HPC. Zhang (Zhang et al., 2015a) utilized KOH as the template and activating agent and successfully prepared lignin-derived HPC with an interconnected 3D network. Its abundant oxygen-containing group ensures a relatively good pseudocapacitance performance (165 F/g in 1 M H2SO4 at 50 mA/g). Increasing SSA of carbon materials is a good choice for promoting the Cs of electrode materials; hence, a higher HPC derived from lignin was obtained by KOH activation, the corresponding products provided a Cs of 286.7 F/g at 0.2 A/g (Zhang et al., 2015b). In addition, a hard template, such as zeolite, was used to control the assembly of lignin, and then control the pore structure of the final products, this lignin-based templated PC showed a high Cs (250 F/g at 50 mA/g) (Ruiz-Rosas et al., 2014). One dimension of PC fibers derived from lignin not only contributed to faster electron conduction, but also facilitated the electrolyte infiltration by providing abundant pore structure, Hu et al. reported that porous fiber activated by KOH achieved a total capacitance of 1 F at 10 mg loading (Hu et al., 2014). Besides, lignin-based HPC film was developed by Chang and co-workers, as shown in Figure 5, a flexible film consists of lignin, PVP and Mg (NO3)2 was synthesized through electrospinning, then the precursor was carbonized and pickling to remove the MgO, the final PC film exhibited Cs of 248 F/g and outstanding rate and cyclic performance (Ma et al., 2018).
Figure 5
To enhance the performance of lignin-derived PC, surfactant, organic solvent and silica were added into the mixture of lignin, after carbonization and activation by 2 M NaOH, the carbon film (~310 μm) was used as an electrode, because of its hierarchical pore structure and superb electrical conductivity, this novel carbon electrode achieved an ultrahigh areal capacitance of 3 F/cm2 and a high volumetric capacitance of 97.1 F/cm3, high mass loading and excellent electrochemical performance ensure it is a promising candidate for supercapacitor (Li et al., 2016a). Furthermore, lignin-derived byproducts were used as carbon resources by hydrothermal treatment and activation, the as-prepared N-doped PC with hierarchical bowl-like pore structure exhibited a high conductivity (4.8 S/cm), favorable Cs (312 F/g at 1 A/g in 6 M KOH) and excellent rate capability (81% retention at 80 A/g) (Wang et al., 2017). Moreover, Wang reported that N-doped PC derived by KOH activated urea-modified lignin could be obtained; it possessed a well-developed porous structure and extremely high SSA (3,130 m2/g). The corresponding supercapacitors achieved Cs of 273 and 306 F/g in 6 M KOH and KOH-PVA solid electrolytes, respectively (Wang et al., 2016b).
Alginate-Derived PC
Except for cellulose, other kinds of natural polysaccharides obtained by artificial extracting have been wildly used as PC precursor because of their low cost, accessibility and component stability.
Alginate is a polysaccharide composed by covalently linked mannuronate and guluronate, and widely distributed to the cell walls of brown algae. Furthermore, the chelation between metal ions and alginate results in gelling and forming an “egg-box” structure (Davis et al., 2003), which further being calcinated at 800°C, three-dimensional macro-meso-microporous HPC aerogels were prepared. The final products showed an excellent rate performance (65% capacity retention at 100 A/g) and decent capacity (188 F/g at 1 A/g) (Wang et al., 2018a). Li and co-workers synthesized alginate gels with interconnected macropore structure utilizing freeze-drying process, then after activation by KOH and removal of Ca, interconnected HPC was obtained; it showed a high-rate capability with 222 F/g and long cycling life at 10 A/g (Li et al., 2015c). On account of the limited Cs of an EDLC capacitor, O- and N- enriched PC was prepared by calcining kelp in NH3 atmosphere, the products acquired high volumetric Cs (>360 F/cm3) and superb cycling performance (Li et al., 2015b). In addition, Nitrogen-doped PC fibers derived from cobalt alginate with egg-box structure, which led into the formation of abundant large mesopores, and the product presented an excellent capacitive behavior of 197 F/g at 1 A/g and superb cycling ability (Tang et al., 2018). Geng (Geng et al., 2016) reported a facile method to synthesis HPC derived from sodium alginate by pre-carbonization and NaOH activation, and it exhibited a capacity of 451 F/g in 2 M KOH solution; while its rate performance, which greatly depends on the electrical conductivity of the electrode materials, was not satisfied.
Starch-Derived PC
As the most common carbohydrate in the human diet, starch, a polymeric carbohydrate consisting of glucose units jointed by glycosidic bonds, is a promising candidate for supercapacitors as its low cost, accessibility (Lei et al., 2016; Figure 6). Direct carbonization of starch with the aid of activated agents is easy and commonly used by researchers for preparing PC. Guo (Guo et al., 2018) synthesized starch-derived PC through one-pot carbonization, the as-prepared PC achieved a Cs of 385 F/g at 1 A/g. Zhang (Zhang et al., 2015b) proposed a simple strategy to fabricate hierarchical hollow porous spherical carbon using starch as raw materials and KHCO3 as the activation agent. The relatively large SSA and rich porous structure endowed the electrode materials with a high capacitance (265.4 F/g at 1 A/g) and excellent rate capacitance (137 F/g at 100 A/g). Hence, carbon derived by different botanical origin would influence the electrochemical performance of the products, and this was verified by Bakierska (Bakierska et al., 2017). In addition, hydrothermal treatment of starch is useful for improving the hydrophilic of carbon materials by introducing the oxygen-containing functional group. Therefore, before carbonization and activation at elevated temperature, hydrothermal carbonization was performed, the potato-derived PC spheres displayed a high Cs (245 F/g) and good rate performance (61% capacitance retention at 10 A/g) (Qiang et al., 2015); similar processing procedure was used by Hong with sweet potato starch as the carbon source, a Cs of 208 F/g at 1 A/g was gained (Hong et al., 2018).
Figure 6
The foaming process (Wang et al., 2016b) through physical or chemical blowing with the aid of carbonate of urea leads to the formation of abundant macropores. For this reason, inspired by bread leavening, Deng (Deng et al., 2015) proposed a non-casting and template-free method to fabricate HPC by mixing the starch with KHCO3 followed by carbonization at a high-temperature condition. The as-prepared samples owned a Cs of 253 F/g and with no distict capacitance loss after 10,000 cycles. At the same time, Chang (Chang et al., 2017) employed a chemical blowing strategy to synthesis N-doping sheet-like PC by graphitization and chemical activation. The samples gained extremely high surface area (2,129 m2/g), large pore volume (0.97 cm3/g), good Cs (337 F/g at 0.5 A/g) and reasonable cycle stability. Similar preparation strategies were employed to treat starch by other researchers to investigate the electrochemical properties of the PC (Pang et al., 2016a; Yang et al., 2016; Du et al., 2017). Calcium acetate was used as the hard template and mixed with starch before carbonization, the PC with tunable pore size by adjusting the ratio of starch/calcium acetate was prepared. When the current density increased from 0.1 A/g to 10 A/g, the Cs of the electrode materials transformed from 277 F/g to 182 F/g, and the cycling results indicated that the PC owned an extremely outstanding cycle stability even after 20,000 cycles (Zhang et al., 2016b). Compared with other kinds of biomass, corn starch is a relatively pure resource as its high-yield character. PC derived corn starch by hydrothermal carbonization, and activation acquired high SSA (1,239 cm2/g), good capacitance (144 F/g) and energy density (19.9 Wh/kg), that were performed slightly better than commercial PC (Pang et al., 2016b). The rate performance of the electrode can be improved by combining PC and carbon cloth together. Zhong (Zhong et al., 2018) synthesized a binder-free activated carbon electrode via sol-gel and KOH activation; the corresponding electrodes achieved 272 F/g (1 A/g) and Cs retention of 75.9% at 50 A/g.
Chitin-Derived PC
As one of the most abundant natural polymers, chitins, with stiff chain conformation and considerable nitrogen concentration (~6.9 wt%), can be completely dissolved into the mixture solution of NaOH and urea. Generally, the addition of PETF hampers the electron transport and restrains the rate capacity of electrode materials. Zhang (Zhang et al., 2016a) employed a one-step synthesis strategy for preparing a binder-free PC electrode by sol-gel method. After KOH activation, the electrode achieved gravimetric Cs of 272 F/g and 75.9% Cs retention at 50 A/g. By means of emulsification and carbonization at high temperature, N-doped microsphere with ample interconnected porous structure, high SSA, unique elasticity and outstanding rate performance were obtained (Suhas and Carrott, 2007). Gao employed prawn shells as a carbon precursor, the obtained N-doped activated carbon exhibited very fine Cs of 357 F/g (6 M KOH) and 695 F/g (1 M H2SO4) (Zhang et al., 2015b). The fungus was also used as PC sources, Long (Ruiz-Rosas et al., 2014) found the corresponding graphene-like carbon possessed high specific surface are (1,103 m2/g), outstanding volumetric (360 F/cm3) and cycle stability (99% capacitance retention after 10,000 cycles). At the same time, N-doped PC derived from shrimp shells with high surface area (1,271 m2/g) by KOH activation also got a high Cs (239 F/g at 0.5 A/g). Moreover, as a renewable biomass mainly composed of chitin, cicada slough derived PC was obtained through carbonization in air and KOH etching in inert atmosphere, results showed that the products exhibited fairly high oxygen content (~30%), moderate nitrogen content (~4%) and high Cs (266 F/g at 0.5 A/g) (Hu et al., 2014).
Gelatin-Derived PC
As a renewable biomass resource, gelatin owns abundant rich –NH3 groups, which ensure a good wettability after carbonization, and facilitates nitrogen atoms doped during the activation process. Hence, it is believed to be a promising candidate for the raw material of PC for supercapacitor. Recently, it is still a big challenge for preparing bio-sources derived carbon materials with 2D planar architectures, which promote ions transportation and electrons conduction, and further affecting the capacitance and rate performance of the electrode materials. Therefore, utilizing gelatin and dopamine as carbon and N sources, respectively, Fan and colleagues (Fan et al., 2015) developed a general strategy for synthesizing 2D PC nanosheets through a series of treatment, including intercalation, thermal treatment and chemical etching; meanwhile, layered montmorillonite was added to control the microstructure of gelatin, and brought about the formation of two-dimensional nanosheet-like PC. The final products exhibited an enhanced rate capability and a high Cs of 246 F/g; besides, the decent capacitance retention (81% at 100 A/g) indicates the electrode material is a good candidate of electrode material for supercapacitor. Furthermore, a free-standing N-doped PC film derived from gelatin/copper hydroxide nanostrands composite films were synthesized by Hu et al. (2016); the binder-free mesoporous N-doped carbon film possessed promoted specific energy (28.1 Wh/kg) and high specific capacity (316 F/g at 0.5 A/g), while its rate performance was not satisfied. Doping with multi-elements is another strategy to improve the electrochemical performance of PC because of the synergistic effect. Therefore, a facile yet sustainable approach was used to produce B/N co-doped PC. Boric acid was added into the gelatin solution, and it acted as hard templates after crystallization during the evaporation of aqueous solution at an elevated temperature. The plate-like shaped boric acid regulating the assembly of gelatin, after carbonization and activation, 2D plate-like PC formed. As the voltage windows is 0.8 and 1.0 V, the Cs of the PC is 240 and 230 F/g, respectively. It also showed improved capacitance retention (Zheng et al., 2016b). Except for boric acid, graphene oxide was applied as a regulator to modify the pore structure, composition, and microstructure of PC derived from gelatin, and results showed that the carbon nanosheets with thickness range from 10 to 30 nm, owned high Cs, decent rate capability and high capacitance retention (76% at 20 A/g). At the same time, Zhang applied a similar approach to preparing layer-like PC with the thickness ~100 nm, which delivered a high discharge Cs (366 F/g at 1 A/g), good rate capability (221 F/g at 30 A/g) and suitable cycling performance (Zhang et al., 2015c).
Plant-Tissue-Derived PC
It is well-known that a thick electrode with high areal active materials loading is urgent in supercapacitor designs as it is closely related to the energy density of supercapacitor devices, and it is useful to reduce the cost of manufacturing through maximizing the packing density of electrode materials and decreasing the layers of inactive materials. What is noteworthy is that the transportation rates of the ion and electron are inversely proportional to the thickness of the electrode in the real-world application. However, natural wood possesses a unique anisotropic structure and plenty of open channel along the growth direction, which facilitates alleviating the electrode materials' tortuosity, promoting the ions transfer, and further increasing the rate capacity of the electrode materials (Figure 7). Hence, a surface modified porous wood carbon derived from poplar wood was prepared by Liu (Liu et al., 2012), and the products achieved a maximum gravimetric and volumetric capacitance of 234 F/g and 36 F/cm3, respectively. Basswood was carbonized by multistep thermal treatment and CO2 activation; the obtained HPC with extremely high mass loading of MnO2 gained high-energy density (1.6 mWh/cm2) and power density (24 W/cm2) (Chen et al., 2017a). In addition, highly anisotropic, multichannel wood carbon doped by N and S were also exhibited well electrochemical properties, the PC showed a Cs of 704 F/g at 0.2 A/g, and still maintained a competitive Cs of 349 F/g at 4 A/g (Tang et al., 2018). Pinecone tree activated carbon was prepared by KOH activation at 800°C, and the products showed a Cs and energy density of 69 F/g at 0.5 A/g and 24.6 Wh/kg, respectively, besides, it exhibited excellent voltage stability after holding 110 h (Barzegar et al., 2017).
Figure 7
Similar to the wood's microstructure, bamboo-derived carbon was obtained by carbonization with the aid of KOH under N2 atmosphere. After being doped by boron and nitrogen, the corresponding HPC exhibited a Cs of 281 F/g (1 M, KOH) and energy density (37.8 Wh/kg) (Chen et al., 2015). As N-enrich biomass, the bamboo shoot was carbonized by Chen (Chen et al., 2017c) to prepare N-doped PC materials, which was endowed with high SSA, highly interconnected pores and uniform nitrogen dopant distribution. Its outstanding Cs and rate performance ensured it is a promising candidate for supercapacitors. Wei employed broussonetia papyrifera as a biomass source, after hydrothermal treatment in KOH solution, then pyrolysis and activated at high temperature in Ar atmosphere, N-doped HPC with high SSA (1,212 m2/g) and outstanding Cs (320 F/g at 0.5 A/g) were fabricated (Wei et al., 2015). Thubsuang reported that rubberwood waste treated with H3PO4 or NaOH led into the formation of carbon monoliths, which exhibited a maximum gravimetric capacitance, volumetric capacitance and energy density of 129 F/g, 104 F/cm3, and 14.2 Wh/kg, respectively (Thubsuang et al., 2017). What's more, wood waste was used as raw material, and the N-doped PC-PANI composite possessed a decent Cs (347 F/g at 2 A/g) and high energy density (44.4 Wh/kg) (Yu et al., 2015). Compared with conventional KOH activation, impregnate-activation method resulted in PC derived from pine tree sawdust with higher surface area and richer interconnected pores, and achieved good Cs in the organic electrolyte (146 F/g) and IL electrolyte (224 F/g) (Wang et al., 2017). Except for these woody materials aforementioned, other woody wastes, such as spruce bark (Sun et al., 2018), Java Kapok tree (Kumar et al., 2018), plane tree (Yao et al., 2017), Melia azedarach (Morenocastilla et al., 2017), auriculiformis tree bark (Momodu et al., 2017), ginkgo leaves (Hao et al., 2017) (Figure 8) were developed as carbon for fabricating PC, whose Cs was all better than commercial activated carbon. Musa basjoo, which appears like a tree and have three layers of structure involves nano-/micro-/millimeter level, that endowed the PC with abundant interconnected pores after KOH activation. The products displayed high Cs and good cycling performance (Zheng et al., 2016a).
Figure 8
In addition to wood, plants with a similar structure like shrimp shell, which preserve its layered structure after carbonization and washing with an acid solution, should be a kind of promising candidate for HPC. The microstructure of these plants, such as the flower petals andtree leaves, could be kept by shape fixing via a salt recrystallization strategy, which involves the addition of salt crystals with a high melting point (Ding et al., 2015). Hence, the salt sealing strategy was utilized to fabricate graphene-like PC nanosheets (GPCN) derived from salvia splendens' flower petals. The obtained PC consisted of 10.26% O and 2.3% N through elemental analysis, and it owns high SSA (~1,051 m2/g). Thanks to these characteristics, the GPCN-based carbon materials exhibited ~220 F/g at 20 A/g, and showed a high-rate capability (86.3% capacity retention from 1 to 100 A/g in 6 M KOH solution) (Liu et al., 2018b). In addition, PC derived from paulownia flower by pyrolysis carbonization and chemical activation also showed high SSA, suitable size distribution, superb wettability and partial graphitization phase, which endowed the electrode with a Cs of 297 F/g at 1 A/g in 1 M H2SO4 solution, and the corresponding electrode material exhibited high-energy densities of ~22 Wh/kg as the power output is 3,781 W/kg (Chang et al., 2015). Moreover, other kinds of flower-derived carbon have been prepared by carbonization and activation process, such as camellia and pine cone flower (Nagaraju et al., 2016; Ma et al., 2017), Borassus flabellifer flower (Sivachidambaram et al., 2017), Osmanthu's flower (Zou et al., 2018), cornstalk (Wang et al., 2018b), rice husk (Dong et al., 2018), grape seeds (Guardia et al., 2019), rice straw (Liu et al., 2018d), walnut shell (Wang et al., 2019), wood sawdust (Sevilla et al., 2019) all of these PC electrode materials delivered a relative high Cs and good rate capacity owing to their fine microstructure and abundant N, O elements.
What's more, leaves with a delicate hierarchical structure, which promote the diffusion of electrolytes in living organisms, are also a good choice for transferring it into HPC materials. Li proposed a facile strategy to fabricate a free-standing bio-carbon supercapacitor derived from sisal leaves by being carbonized at 1,000°C for two times and by chemical activation afterwards, was removed and freeze-dried; the developed free-standing electrode exhibited a high Cs of 204 F/g at 1 A/g and good rate capacity; at the same time, it also delivered a relative steady capacity in an organic electrolyte (Wang et al., 2016c). It is worth noting that the combination of the physical and chemical activation method might bring about unexpected results. Li (Li et al., 2015d) proposed a novel strategy to treat the fallen leaves by the activations of mixed KOH and KHCO3. The combination of KOH and KHCO3 led to the enlargement of pore size, which benefited the diffusion of ions and is helpful to enhance the specific capacity and rate performance of carbon materials, the electrochemical characterizations' results revealed that this novel strategy endows the PC with a capacity of 242 F/g at 0.3 A/g in 6 M KOH solution, and it also showed a relative good cyclic performance. Although the activation process is a common method to fabricate biomass-derived PC materials, while the physical or chemical activates, reaction always accompanied with the collapse of the fine microstructure of the biomass, and further affecting the ion/electron diffusion during energy storage. Hence, a possible way should be developed to replace the activation process while endows the PC with high SSA and abundant pore structure. Huang (Huang et al., 2017) proposed a facile technique, which involves indicalamus leaves and polytetrafluoroethylene as carbon precursor and silica-in-situ-remover, respectively, the obtained PC owns a SSA of ~1,800 m2/g, and exhibited high capacitance (326 F/g in 1 V supercapacitor), high-energy density (23.7 Wh/kg at power density of 224.5 W/kg). Furthermore, hydrothermal treatment is a benefit to introducing rich oxygen-group into the framework of carbon, and dual-doped by N, S can promote the electron conduction and increase the active sites of PC materials. Hao and colleagues reported that HPC derived from gingko leaves by hydrothermal treatment in H2SO4 and then activated by KOH at elevated temperature in inert atmosphere, the final products contained small amount of N and S according to the EDS analysis; and the PC maintained a high Cs of 364 F/g at 0.5 A/g and excellent cycling capability (98% capacity retention after 30,000 cycles) (Hao et al., 2016). In addition the leaves aforementioned, other leaves, such as tea (Inal et al., 2015; Ma et al., 2017), euonymus japonicas (Zhu et al., 2015), corn (Yang et al., 2017), cabbage (Wang et al., 2016c), have been used as carbon precursors for synthesizing PC materials for supercapacitor electrodes.
Conclusion and Prospective
In the new era of energy storage, compared with traditional activated carbon materials, biomass-derived HPC has achieved superior performance because of their natural fine structure and rich race elements in the organic tissue. However, it is worth noting that their rate capability performance is not satisfied especially at a high charge/discharge electric current condition. That should be contributed to the high concentration of oxygen groups in carbon framework, which is helpful for enhancing the hydrophilic of carbon materials, and further facilitating the infiltration of electrolyte, while these oxygen groups hamper the electric conductivity of PC. Hence, it is urgent to develop an efficient strategy to balance the wettability and electric conductivity of the carbon matrix, and that calls for the joint from theoretical and experimental researches.
Till now, the chemical activation process through KOH, NaOH etc. is a common tool for preparing porous carbon with a rich porous structure, especially for micropores. It should be noteworthy that a large amount of volatile-gases will be formed because of the reaction between KOH and carbon matrix at elevated temperature, these volatile gases, including metal K, CO, CO2, H2, and H2O, not only lead to the formation of abundant micropores, they also threaten the safety of the instrument because of the strong corrosiveness of metal K. Therefore, other activation strategies should be developed to meet the demand of industrialization.
Ion diffusion is a key issue in supercapacitor systems. Although molecular simulation provides different viewpoints for us to design electrode materials with high efficiency; recently, it mainly focuses on the ion-diffusion within ultra-small pores, and it is still a big challenge for us to investigate the diffusion process of ions in hierarchical pore structure, which is extremely important to enhance the electrochemical performance of PC. Moreover, from the perspective of the environment, security and cost, aqueous electrolyte, but not ionic liquids, should be a better choice for the wide application of supercapacitors in energy storage. However, most of the previous studies have been focused on simulating ion behavior in ionic liquids, which is quite different from the aqueous electrolytes, including ion size, solvation shell and diffusion coefficient. Hence, it is necessary to carry out related studies, and investigate the ion diffusion behavior in aqueous electrolytes, then push the development of supercapacitor.
The impact of carbon doping is still unclear, although doped PC materials provide great opportunities to meet the energy density gap between supercapacitor and battery. As we know, introducing nitrogen into the framework of carbon is always accompanied with the enhancement of electrical conductivity and increasing of electrochemically-active sites compared with commercial carbon, which further results in huge improvement of Cs because of an additional faradaic contribution, while the enhancement is quite limited in an aqueous electrolyte. Meanwhile, although the promising prospect of aqueous electrolyte, till now, ions liquids offer better capacitive performance, while it still needs to investigate numerous cations, anions and solvent molecules to achieve more excellent performance to meet the requirement of the industry. Therefore, high-throughput techniques, already applied in battery materials and electrolytes, is a powerful tool for the exploitation of promising systems among thousands of candidates for supercapacitors, and the systems-screening process is closely related to the results of in-situ experiments and simulation in molecular level.
Unveiling the ion adsorption and charge storage in PC materials for supercapacitor is essential for its applications; in the meantime, it also promotes the development of other energy storage system, for example, redox flow batteries, biofuel cells, flow capacitors. Hence, it is of central importance to combine the experimental and theoretical tools gained from supercapacitors to promote the development of other current/future technologies.
At last, it is noteworthy that previously reported electrode materials with high gravimetric/areal/volumetric capacitance is meaningless if we ignore the corresponding mass loading/working area/ total volume of the electrode. Hence, effective metrics are required to evaluate the performance of numerous materials for supercapacitors, including biomass-derived PC. As for gravimetric capacitance, ultra-small mass loading means the storage of a limited amount of charges. So, the mass loading of electrodes is a key parameter in comparing the capacitance variation, and it is still urgent to improve electrochemical performance of supercapacitor at high mass loading, but not the Cs of the electrode with small loading active materials.
Statements
Author contributions
SY and JZ were responsible for literature searching and drafting. All authors contributed equally to the final writing of the paper.
Funding
This research was supported by National Nature Science Foundation of China (51702139) and Youth Science Foundation (20151BAB216007, GJJ150637, 20161BAB216122).
Conflict of interest
The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
References
1
AbioyeA. M.AniF. N. (2015). Recent development in the production of activated carbon electrodes from agricultural waste biomass for supercapacitors: a review. Renew. Sustain. Energy Rev.52, 1282–1293. 10.1016/j.rser.2015.07.129
2
AnK. H.KimW. S.ParkY. S.MoonJ. M.BaeD. J.LimS. C.et al. (2001). Electrochemical properties of high-power supercapacitors using single-walled carbon nanotube electrodes. Adv. Funct. Mater.11, 387–392. 10.1002/1616-3028(200110)11:5<;387::AID-ADFM387>3.0.CO;2-G
3
AnY.YangY.HuZ.GuoB.WangX.YangX.et al. (2017). High-performance symmetric supercapacitors based on carbon nanosheets framework with graphene hydrogel architecture derived from cellulose acetate. J. Power Sources337, 45–53. 10.1016/j.jpowsour.2016.10.112
4
AugustynV.SimonP.DunnB. (2014). Pseudocapacitive oxide materials for high-rate electrochemical energy storage. Energy Environ. Sci.7, 1597–1614. 10.1039/c3ee44164d
5
BakierskaM.ChojnackaA.MS.NatkanskiP.GajewskaM.RutkowskaM.et al. (2017). Multifunctional carbon aerogels derived by sol–gel process of natural polysaccharides of different botanical origin. Materials.10:1336. 10.3390/ma10111336
6
BarzegarF.BelloA.DangbegnonJ. K.ManyalaN.XiaX. (2017). Asymmetric supercapacitor based on activated expanded graphite and pinecone tree activated carbon with excellent stability. Appl. Energy207, 417–426. 10.1016/j.apenergy.2017.05.110
7
BorchardtL.OschatzM.KaskelS. (2013). Tailoring porosity in carbon materials for supercapacitor applications. Mater. Horizons1, 157–168. 10.1039/C3MH00112A
8
CaoX.ShiY.ShiW.LuG.HuangX.YanQ.et al. (2011). Preparation of novel 3D graphene networks for supercapacitor applications. Small7, 3163–3168. 10.1002/smll.201100990
9
ChanK.ChoiY. O.LeeW. J.YangK. S. (2004). Supercapacitor performances of activated carbon fiber webs prepared by electrospinning of PMDA-ODA poly(amic acid) solutions. Electrochim. Acta50, 883–887. 10.1016/j.electacta.2004.02.072
10
ChangB.YinH.ZhangX.ZhangS.YangB. (2017). Chemical blowing strategy synthesis of nitrogen-rich porous graphitized carbon nanosheets: morphology, pore structure and supercapacitor application. Chem. Eng. J.312, 191–203. 10.1016/j.cej.2016.11.129
11
ChangH. K.WeeJ. H.KimY. A.YangK. S.YangC. M. (2016). Tailoring pore structure of carbon nanofiber for achieving ultrahigh-energy-density supercapacitors using ionic liquid as electrolyte. J. Mater. Chem. A4, 4763–4770. 10.1039/C5TA10500E
12
ChangJ.GaoZ.WangX.WuD.XuF.WangX.et al. (2015). Activated porous carbon prepared from paulownia flower for high performance supercapacitor electrodes. Electrochim. Acta157, 290–298. 10.1016/j.electacta.2014.12.169
13
ChenC.ZhangY.LiY.DaiJ.SongJ.YaoY.et al. (2017a). All-wood, low tortuosity, aqueous, biodegradable supercapacitors with ultra-high capacitance. Energy Environ. Sci.10, 538–545. 10.1039/C6EE03716J
14
ChenH.LiuD.ShenZ.BaoB.ZhaoS.WuL. (2015). Functional biomass carbons with hierarchical porous structure for supercapacitor electrode materials. Electrochim. Acta180, 241–251. 10.1016/j.electacta.2015.08.133
15
ChenL.JiT.MuL.ZhuJ. (2016). Cotton fabric derived hierarchically porous carbon and nitrogen doping for sustainable capacitor electrode. Carbon111, 839–848. 10.1016/j.carbon.2016.10.054
16
ChenL. F.HuangZ. H.LiangH. W.YaoW. T.YuZ. Y.YuS. H. (2013). Flexible all-solid-state high-power supercapacitor fabricated with nitrogen-doped carbon nanofiber electrode material derived from bacterial cellulose. Energy Environ. Sci.6, 3331–3338. 10.1039/c3ee42366b
17
ChenL. F.LuY.YuL.LouX. W. (2017b). Designed formation of hollow particle-based nitrogen-doped carbon nanofibers for high-performance supercapacitors. Energy Environ. Sci.10, 1777–1783. 10.1039/C7EE00488E
18
ChenX.ZhangJ.ZhangB. (2017c). A novel hierarchical porous nitrogen-doped carbon derived from bamboo shoot for high performance supercapacitor. Sci. Rep.7:7362. 10.1038/s41598-017-06730-x
19
ChenZ.PengX.ZhangX.JingS.ZhongL.SunR. (2017d). Facile synthesis of cellulose-based carbon with tunable N content for potential supercapacitor application. Carbohydr. Polym.170, 107–116. 10.1016/j.carbpol.2017.04.063
20
ChengF.LiangJ.TaoZ.ChenJ. (2011). Functional materials for rechargeable batteries. Adv. Mater.23, 1695–1715. 10.1002/adma.201003587
21
ChmiolaJ.YushinG.GogotsiY.PortetC.SimonP.TabernaP. L. (2006). Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer. Science313, 1760–1763. 10.1126/science.1132195
22
ChuS.MajumdarA. (2012). Opportunities and challenges for a sustainable energy future. Nature488:294. 10.1038/nature11475
23
DavisT. A.VoleskyB.MucciA. (2003). A review of the biochemistry of heavy metal biosorption by brown algae. Water Res.37, 4311–4330. 10.1016/S0043-1354(03)00293-8
24
DengJ.XiongT.XuF.LiM.HanC.GongY.et al. (2015). Inspired by bread leavening: one-pot synthesis of hierarchically porous carbon for supercapacitors. Green Chem.17, 4053–4060. 10.1039/C5GC00523J
25
DingW.LiL.XiongK.WangY.LiW.NieY.et al. (2015). Shape fixing via salt recrystallization: a morphology-controlled approach to convert nanostructured polymer to carbon nanomaterial as a highly active catalyst for oxygen reduction reaction. J. Am. Chem. Soc.137:5414. 10.1021/jacs.5b00292
26
DongS. A.HeX. J.ZhangH. F.XieX. Y.YuM. X.YuC.et al. (2018). Surface modification of biomass-derived hard carbon by grafting porous carbon nanosheets for high-performance supercapacitors. J. Mater. Chem. A33, 15954–15960. 10.1039/C8TA04080J
27
DownM. P.RowleynealeS. J.SmithG. C.BanksC. E. (2018). Fabrication of graphene oxide supercapacitor devices. ACS Appl. Energy Mater.1, 707–714. 10.1021/acsaem.7b00164
28
DuG.BianQ.ZhangJ.YangX. (2017). Facile fabrication of hierarchical porous carbon for a high-performance electrochemical capacitor. RSC Adv.7, 46329–46335. 10.1039/C7RA08402A
29
DubalD. P.AyyadO.RuizV.GómezromeroP. (2015). Hybrid energy storage: the merging of battery and supercapacitor chemistries. Cheminform44, 1777–1790. 10.1039/c4cs00266k
30
DubalD. P.ChodankarN. R.Caban-HuertasZ.WolfartF.VidottiM.HolzeR.et al. (2016). Synthetic approach from polypyrrole nanotubes to nitrogen doped pyrolyzed carbon nanotubes for asymmetric supercapacitors. J. Power Sources308, 158–165. 10.1016/j.jpowsour.2016.01.074
31
DubininM. M. (1960). The potential theory of adsorption of gases and vapors for adsorbents with energetically nonuniform surfaces. Chem. Rev.60, 235–241. 10.1021/cr60204a006
32
DunnB.KamathH.TarasconJ. M. (2011). Electrical energy storage for the grid: a battery of choices. Science334, 928–935. 10.1126/science.1212741
33
EnterríaM.Martín-JimenoF. J.Suárez-GarcíaF.ParedesJ. I.PereiraM. F. R.MartinsJ. I.et al. (2016). Effect of nanostructure on the supercapacitor performance of activated carbon xerogels obtained from hydrothermally carbonized glucose-graphene oxide hybrids. Carbon105, 474–483. 10.1016/j.carbon.2016.04.071
34
FanX.YuC.YangJ.LingZ.HuC.ZhangM.et al. (2015). A layered-nanospace-confinement strategy for the synthesis of two-dimensional porous carbon nanosheets for high-rate performance supercapacitors. Adv. Energy Mater.5:1401761. 10.1002/aenm.201401761
35
FutabaD. N.HataK.YamadaT.HiraokaT.HayamizuY.KakudateY.et al. (2006). Shape-engineerable and highly densely packed single-walled carbon nanotubes and their application as super-capacitor electrodes. Nat. Mater.5, 987–994. 10.1038/nmat1782
36
GengZ.WangH.WangR.ZhangP.LangJ.WangC. (2016). Facile synthesis of hierarchical porous carbon for supercapacitor with enhanced electrochemical performance. Mater. Lett.182, 1–5. 10.1016/j.matlet.2016.06.046
37
GogotsiY. (2015). Materials for electrochemical capacitors. Nat Mater.7, 845–854. 10.1038/nmat2297
38
GuardiaL.SuarezL.QuerejetaN.VretenarV.KotruszP.SkakalovaV.et al. (2019). Biomass waste-carbon/reduced graphene oxide composite electrodes for enhanced supercapacitors. Electrochimica Acta298, 910–917. 10.1016/j.electacta.2018.12.160
39
GuoJ.GuoH.ZhangL.YangB.CuiJ. (2018). Hierarchically porous carbon as a high-rate and long-life electrode material for high-performance supercapacitors. Chemelectrochem5, 770–777. 10.1002/celc.201701286
40
HaoE.LiuW.LiuS.ZhangY.WangH.ChenS.et al. (2016). Rich sulfur doped porous carbon materials derived from ginkgo leaves for multiple electrochemical energy storage devices. J. Mater. Chem. A5, 2204–2214. 10.1039/C6TA08169Jt
41
HaoE.LiuW.LiuS.ZhangY.WangH.ChenS.et al. (2017). Rich sulfur doped porous carbon materials derived from ginkgo leaves for multiple electrochemical energy storage devices. J. Mater. Chem. A5, 2204–2214. 10.1039/C6TA08169J
42
HongW.WangL.LiuK.HanX.ZhouY.GaoP.et al. (2018). Asymmetric supercapacitor constructed by self-assembled camellia-like BiOCl and activated carbon microspheres derived from sweet potato starch. J. Alloys Comp.746, 292–300. 10.1016/j.jallcom.2018.02.231
43
HouJ.CaoC.IdreesF.MaX. (2015). Hierarchical porous nitrogen-doped carbon nanosheets derived from silk for ultrahigh-capacity battery anodes and supercapacitors. ACS Nano9:2556. 10.1021/nn506394r
44
HuP.MengD.RenG.YanR.PengX. (2016). Nitrogen-doped mesoporous carbon thin film for binder-free supercapacitor. Appl. Mater. Today5, 1–8. 10.1016/j.apmt.2016.08.001
45
HuS.ZhangS.PanN.HsiehY. L. (2014). High energy density supercapacitors from lignin derived submicron activated carbon fibers in aqueous electrolytes. J. Power Sources270, 106–112. 10.1016/j.jpowsour.2014.07.063
46
HuangJ.ChenL.DongH.ZengY.HuH.ZhengM.et al. (2017). Hierarchical porous carbon with network morphology derived from natural leaf for superior aqueous symmetrical supercapacitors. Electrochim. Acta258, 504–511. 10.1016/j.electacta.2017.11.092
47
InalI. I. G.HolmesS. M.BanfordA.AktasZ. (2015). The performance of supercapacitor electrodes developed from chemically activated carbon produced from waste tea. Appl. Surf. Sci.357, 696–703. 10.1016/j.apsusc.2015.09.067
48
JänesA.KurigH.LustE. (2007). Characterisation of activated nanoporous carbon for supercapacitor electrode materials. Carbon45, 1226–1233. 10.1016/j.carbon.2007.01.024
49
KaiD.TanM. J.PeiL. C.YunK. C.YongL. Y.XianJ. L. (2016). Towards lignin-based functional materials in a sustainable world. Green Chem.18, 1175–1200. 10.1039/C5GC02616D
50
KamatP. V. (2015). Meeting the clean energy demand: nanostructure architectures for solar energy conversion. J. Phys. Chem. C111, 2834–2860. 10.1021/jp066952u
51
KazmerskiL. (2016). Renewable and sustainable energy reviews. Renew. Sustain. Energy Rev.38, 834–847.
52
KimH.SeoM.ParkM. H.ChoJ. (2010). A critical size of silicon nano-anodes for lithium rechargeable batteries. Angewandte Chemie Int. Edition122, 2192–2195. 10.1002/ange.200906287
53
KondratS.PresserV.GogotsiY.KornyshevA. A. (2012). Effect of pore size and its dispersity on the energy storage in nanoporous supercapacitors. Energy Environ. Sci.5, 6474–6479. 10.1039/c2ee03092f
54
KumarK. T.SundariG. S.KumarE. S.AshwiniA.RamyaM.VarshaP.et al. (2018). Synthesis of nanoporous carbon with new activating agent for high-performance supercapacitor. Mater. Lett.218, 181–184. 10.1016/j.matlet.2018.02.017
55
LeeJ.YoonS.OhS. M.ShinC. H.HyeonT. (2000). Development of a new mesoporous carbon using an HMS aluminosilicate template. Adv. Mater.12, 359–362. 10.1002/(SICI)1521-4095(200003)12:5<;359::AID-ADMA359>3.0.CO;2-1
56
LeiH.ChenD.HuoJ. (2016). Blowing and in-situ activation of carbonaceous “lather” from starch: preparation and potential application. Mater. Des.92, 362–370. 10.1016/j.matdes.2015.12.063
57
LiB.DaiF.XiaoQ.YangL.ShenJ.ZhangC.et al. (2015a). Nitrogen-doped activated carbon for high energy hybrid supercapacitor. Energy Environ. Sci.9, 102–106. 10.1039/C5EE03149D
58
LiH.YuanD.TangC.WangS.SunJ.LiZ.et al. (2016a). Lignin-derived interconnected hierarchical porous carbon monolith with large areal/volumetric capacitances for supercapacitor. Carbon100, 151–157. 10.1016/j.carbon.2015.12.075
59
LiJ.LiuK.GaoX.YaoB.HuoK.ChengY.et al. (2015b). Oxygen and nitrogen enriched 3D porous carbon for supercapacitors of high volumetric capacity. ACS Appl. Mater. Interfaces7, 24622–24628. 10.1021/acsami.5b06698
60
LiJ.LiuW.XiaoD.WangX. (2017a). Oxygen-rich hierarchical porous carbon made from pomelo peel fiber as electrode material for supercapacitor. Appl. Surf. Sci.416, 918–924. 10.1016/j.apsusc.2017.04.162
61
LiJ.XieH.LiY. (2013). Fabrication of graphene oxide/polypyrrole nanowire composite for high performance supercapacitor electrodes. J. Power Sources241, 388–395. 10.1016/j.jpowsour.2013.04.144
62
LiW.YangY. J. (2014). The reduction of graphene oxide by elemental copper and its application in the fabrication of graphene supercapacitor. J. Solid State Electrochem.18, 1621–1626. 10.1007/s10008-014-2391-5
63
LiY.LiuQ.KangD.GuJ.ZhangW.ZhangD. (2015c). Freeze-drying assisted synthesis of hierarchical porous carbons for high-performance supercapacitors. J. Mater. Chem. A3, 21016–21022. 10.1039/C5TA04233J
64
LiY.RoyS.BenT.XuS.QiuS. (2014). Micropore engineering of carbonized porous aromatic framework (PAF-1) for supercapacitors application. Phys. Chem. Chem. Phys.16, 12909–12917. 10.1039/c4cp00550c
65
LiY.WangG.WeiT.FanZ.YanP. (2016b). Nitrogen and sulfur co-doped porous carbon nanosheets derived from willow catkin for supercapacitors. Nano Energy19, 165–175. 10.1016/j.nanoen.2015.10.038
66
LiY. T.PiY. T.LuL. M.XuS. H.RenT. Z. (2015d). Hierarchical porous active carbon from fallen leaves by synergy of K 2 CO 3 and their supercapacitor performance. J. Power Sources299, 519–528. 10.1016/j.jpowsour.2015.09.039
67
LiZ.AhadiK.JiangK.AhvaziB.LiP.AnyiaA. O.et al. (2017b). Freestanding hierarchical porous carbon film derived from hybrid nanocellulose for high-power supercapacitors. Nano Res.10, 1847–1860. 10.1007/s12274-017-1573-8
68
LinT.ChenI. W.LiuF.YangC.BiH.XuF.et al. (2015). Nitrogen-doped mesoporous carbon of extraordinary capacitance for electrochemical energy storage. Science350, 1508–1513. 10.1126/science.aab3798
69
LiuB.YangM.ChenH.LiuY.YangD.LiH. (2018b). Graphene-like porous carbon nanosheets derived from salvia splendens for high-rate performance supercapacitors. J. Power Sources397, 1–10. 10.1016/j.jpowsour.2018.06.100
70
LiuC.YanX.HuF.GaoG.WuG.YangX. (2018c). Toward superior capacitive energy storage: recent advances in pore engineering for dense electrodes. Adv. Mater.30:1705713. 10.1002/adma.201705713
71
LiuC.YuZ.NeffD.ZhamuA.JangB. Z. (2010). Graphene-based supercapacitor with an ultrahigh energy density. Nano Lett.10, 4863–4868. 10.1021/nl102661q
72
LiuJ.WangJ.XuC.JiangH.LiC.ZhangL. L.et al. (2018a). Advanced energy storage devices: basic principles, analytical methods, and rational materials design. Adv. Sci.5:1700322. 10.1002/advs.201700322
73
LiuM. C.KongL. B.ZhangP.LuoY. C.KangL. (2012). Porous wood carbon monolith for high-performance supercapacitors. Electrochim. Acta60, 443–448. 10.1016/j.electacta.2011.11.100
74
LiuS. B.YangZ.ZhangB. H.XiaH.ZhouJ. F.XieW. K.et al. (2018d). Nano-micro carbon spheres anchored on porous carbon derived from dual-biomass as high rate performance supercapacitor electrodes. J. Power Sources381, 116–126. 10.1016/j.jpowsour.2018.02.014
75
LotaG.KrawczykP.LotaK.SierczynskaA.KolanowskiŁ.BaraniakM.et al. (2016). The application of activated carbon modified by ozone treatment for energy storage. J. Solid State Electrochem.20:2857. 10.1007/s10008-016-3293-5
76
LvY.GanL.LiuM.XiongW.XuZ.ZhuD.et al. (2012). A self-template synthesis of hierarchical porous carbon foams based on banana peel for supercapacitor electrodes. J. Power Sources209, 152–157. 10.1016/j.jpowsour.2012.02.089
77
LvY.ZhangF.DouY.ZhaiY.WangJ.LiuH.et al. (2011). A comprehensive study on KOH activation of ordered mesoporous carbons and their supercapacitor application. J. Mater. Chem.22, 93–99. 10.1039/C1JM12742J
78
MaC.LiZ.LiJ.FanQ.WuL.ShiJ.et al. (2018). Lignin-based hierarchical porous carbon nanofiber films with superior performance in supercapacitors. Appl. Surf. Sci.456, 568–576. 10.1016/j.apsusc.2018.06.189
79
MaG.LiJ.SunK.PengH.FengE.LeiZ. (2017). Tea-leaves based nitrogen-doped porous carbons for high-performance supercapacitors electrode. J. Solid State Electrochem.21, 1–11. 10.1007/s10008-016-3389-y
80
MaX.KollaP.ZhaoY.SmirnovaA. L.HaoF. (2016). Electrospun lignin-derived carbon nanofiber mats surface-decorated with MnO 2 nanowhiskers as binder-free supercapacitor electrodes with high performance. J. Power Sources325, 541–548. 10.1016/j.jpowsour.2016.06.073
81
MccloskeyB. D. (2015). Expanding the ragone plot: pushing the limits of energy storage. J. Phys. Chem. Lett.6:3592. 10.1021/acs.jpclett.5b01813
82
MillerJ. R.SimonP. (2008). Materials science. electrochemical capacitors for energy management. Science321, 651–652. 10.1126/science.1158736
83
MoR.-J.ZhaoY.ZhaoM.-M.WuM.WangC.LiJ.-P.et al. (2018). Graphene-like porous carbon from sheet cellulose as electrodes for supercapacitors. Chem. Eng. J.346, 104–112. 10.1016/j.cej.2018.04.010
84
MomoduD.MaditoM.BarzegarF.BelloA.KhaleedA.OlaniyanO.et al. (2017). Activated carbon derived from tree bark biomass with promising material properties for supercapacitors. J. Solid State Electrochem.21, 859–872. 10.1007/s10008-016-3432-z
85
MorenocastillaC.GarcíaroseroH.CarrascomarínF. (2017). Symmetric supercapacitor electrodes from KOH activation of pristine, carbonized, and hydrothermally treated melia azedarach stones. Materials.10:747. 10.3390/ma10070747
86
NagarajuG.LimJ. H.ChaS. M.YuJ. S. (2016). Three-dimensional activated porous carbon with meso/macropore structures derived from fallen pine cone flowers: A low-cost counter electrode material in dye-sensitized solar cells. J. Alloys Comp.693, 1297–1304. 10.1016/j.jallcom.2016.10.015
87
PangL.ZouB.HanX.CaoL.WangW.GuoY. (2016a). One-step synthesis of high-performance porous carbon from corn starch for supercapacitor. Mater. Lett.184, 88–91. 10.1016/j.matlet.2016.07.147
88
PangL.ZouB.ZouY.HanX.CaoL.WangW.et al. (2016b). A new route for the fabrication of corn starch-based porous carbon as electrochemical supercapacitor electrode material. Colloids Surfaces A Physicochem. Eng. Aspects504, 26–33. 10.1016/j.colsurfa.2016.05.049
89
PengH. J.HuangJ. Q.ChengX. B.ZhangQ. (2017). Review on high-loading and high-energy lithium–sulfur batteries. Adv. Energy Mater.7:1700260. 10.1002/aenm.201700260
90
PushparajV. L.ShaijumonM. M.KumarA.MurugesanS.CiL.VajtaiR.et al. (2007). Flexible energy storage devices based on nanocomposite paper. Proc. Natl. Acad. Sci. USA.104, 13574–13577. 10.1073/pnas.0706508104
91
QiangR.HuZ.YangY.LiZ.AnN.RenX.et al. (2015). Monodisperse carbon microspheres derived from potato starch for asymmetric supercapacitors. Electrochim. Acta167, 303–310. 10.1016/j.electacta.2015.03.190
92
QuW.-H.XuY.-Y.LuA.-H.ZhangX.-Q.LiW.-C. (2015). Converting biowaste corncob residue into high value added porous carbon for supercapacitor electrodes. Bioresour. Technol.189, 285–291. 10.1016/j.biortech.2015.04.005
93
Ruiz-RosasR.Valero-RomeroM. J.Salinas-TorresD.Rodríguez-MirasolJ.CorderoT.MorallónE.et al. (2014). Electrochemical performance of hierarchical porous carbon materials obtained from the infiltration of lignin into zeolite templates. ChemSusChem7, 1458–1467. 10.1002/cssc.201301408
94
SalunkheR. R.LinJ.MalgrasV.DouS. X.KimJ. H.YamauchiY. (2015). Large-scale synthesis of coaxial carbon nanotube/Ni(OH) 2 composites for asymmetric supercapacitor application. Nano Energy11, 211–218. 10.1016/j.nanoen.2014.09.030
95
SevillaM.DiezN.FerreroG. A.FuertesA. B. (2019). Sustainable supercapacitor electrodes produced by the activation of biomass with sodium thiosulfate. Energy Storage Mater. 18, 356–365. 10.1016/j.ensm.2019.01.023
96
SevillaM.FuertesA. B. (2016). A green approach to high-performance supercapacitor electrodes: the chemical activation of hydrochar with potassium bicarbonate. ChemSusChem9, 1880–1888. 10.1002/cssc.201600426
97
SingK. S. W. (1985). Reporting physisorption data for gas/solid systems-with special reference to the determination of surface area and porosity. Pure Appl. Chem.57, 603–619. 10.1351/pac198557040603
98
SivachidambaramM.VijayaJ. J.KennedyL. J.JothiramalingamR.AllohedanH. S. A.MunusamyM. A.et al. (2017). Preparation and characterization of activated carbon derived from the borassus flabellifer flower as an electrode material for supercapacitor applications. N. J. Chem.41, 3939–3949. 10.1039/C6NJ03867K
99
Suhas CarrottP. J. M.CarrottM. M. L. R. (2007). Lignin – from natural adsorbent to activated carbon: a review. Bioresour. Technol.98:2301. 10.1016/j.biortech.2006.08.008
100
SunX.ChengP.WangH.XuH.DangL.LiuZ.et al. (2015). Activation of graphene aerogel with phosphoric acid for enhanced electrocapacitive performance. Carbon.92, 1–10. 10.1016/j.carbon.2015.02.052
101
SunZ.ZhengM.HuH.DongH.LiangY.XiaoY.et al. (2018). From biomass wastes to vertically aligned graphene nanosheet arrays: a catalyst-free synthetic strategy towards high-quality graphene for electrochemical energy storage. Chem. Eng. J.336, 550–561. 10.1016/j.cej.2017.12.019
102
TangZ.PeiZ.WangZ.LiH.ZengJ.RuanZ.et al. (2018). Highly anisotropic, multichannel wood carbon with optimized heteroatom doping for supercapacitor and oxygen reduction reaction. Carbon.130, 532–543. 10.1016/j.carbon.2018.01.055
103
ThubsuangU.LaebangS.ManmuanpomN.WongkasemjitS.ChaisuwanT. (2017). Tuning pore characteristics of porous carbon monoliths prepared from rubber wood waste treated with H 3 PO 4 or NaOH and their potential as supercapacitor electrode materials. J. Mater. Sci.52, 6837–6855. 10.1007/s10853-017-0922-z
104
Vix-GuterlC.FrackowiakE.JurewiczK.FriebeM.ParmentierJ.BéguinF. (2005). Electrochemical energy storage in ordered porous carbon materials. Carbon43, 1293–1302. 10.1016/j.carbon.2004.12.028
105
WangB.LiD.TangM.MaH.GuiY.TianX.et al. (2018a). Alginate-based hierarchical porous carbon aerogel for high-performance supercapacitors. J. Alloys Compd.749, 517–522. 10.1016/j.jallcom.2018.03.223
106
WangC. J.WuD. P.WangH. J.GaoZ. Y.XuF.JiangK. (2018b). A green and scalable route to yield porous carbon sheets from biomass for supercapacitors with high capacity. J. Mater. Chem. A6, 1244–1254. 10.1039/C7TA07579K
107
WangD. W.LiF.LiuM.LuG. Q.ChengH. M. (2008). 3D aperiodic hierarchical porous graphitic carbon material for high-rate electrochemical capacitive energy storage. Angewandte Chemie120, 379–382. 10.1002/ange.200702721
108
WangG.WangH.LuX.LingY.YuM.ZhaiT.et al. (2014). Solid-state supercapacitor based on activated carbon cloths exhibits excellent rate capability. Adv. Mater.26, 2676–2682. 10.1002/adma.201304756
109
WangJ.KaskelS. (2012). KOH activation of carbon-based materials for energy storage. J. Mater. Chem.22, 23710–23725. 10.1039/c2jm34066f
110
WangK.CaoY.WangX.CastroM. A.LuoB.GuZ.et al. (2016a). Rod-shape porous carbon derived from aniline modified lignin for symmetric supercapacitors. J. Power Sources307, 462–467. 10.1016/j.jpowsour.2016.01.008
111
WangK.XuM.GuY.GuZ.FanQ. H. (2016b). Symmetric supercapacitors using urea-modified lignin derived N-doped porous carbon as electrode materials in liquid and solid electrolytes. J. Power Sources332, 180–186. 10.1016/j.jpowsour.2016.09.115
112
WangP.WangQ.ZhangG.JiaoH.DengX.LiuL. (2016c). Promising activated carbons derived from cabbage leaves and their application in high-performance supercapacitors electrodes. J. Solid State Electrochem.20, 319–325. 10.1007/s10008-015-3042-1
113
WangX.LiY.LouF.BuanM. E. M.SheridanE.ChenD. (2017). Enhancing capacitance of supercapacitor with both organic electrolyte and ionic liquid electrolyte on a biomass-derived carbon. RSC Adv.7:23859–23865. 10.1039/C7RA01630A
114
WangY.ShiZ.HuangY.MaY.WangC.ChenM.et al. (2009). Supercapacitor devices based on graphene materials. J. Phys. Chem. C113, 13103–13107. 10.1021/jp902214f
115
WangY. F.JiangH. H.YeS. W.ZhouJ. M.ChenJ. H.ZengQ. Q.et al. (2019). N-doped porous carbon derived from walnut shells with enhanced electrochemical performance for supercapacitor. Funct. Mater. Lett. 10.1142/S1793604719500425. [Epub ahead of print].
116
WeiT.WeiX.GaoY.LiH. (2015). Large scale production of biomass-derived nitrogen-doped porous carbon materials for supercapacitors. Electrochim. Acta169, 186–194. 10.1016/j.electacta.2015.04.082
117
WeiX.JiangX.WeiJ.GaoS. (2016). Functional groups and pore size distribution do matter to hierarchically porous carbons as high-rate-performance supercapacitors. Chem. Mater.28, 445–458. 10.1021/acs.chemmater.5b02336
118
WuX.ShiZ.TjandraR.CousinsA.SyS.YuA.et al. (2015). Nitrogen-enriched porous carbon nanorods templated by cellulose nanocrystals as high performance supercapacitor electrode. J. Mater. Chem. A3, 23768–23777. 10.1039/C5TA07252B
119
XiaoK.DingL. X.LiuG.ChenH.WangS.WangH. (2016). Freestanding, hydrophilic nitrogen-doped carbon foams for highly compressible all solid-state supercapacitors. Adv. Mater.28, 5997–6002. 10.1002/adma.201601125
120
XiongS.FanJ.WangY.ZhuJ.YuJ.HuZ. (2017). A facile template approach to nitrogen-doped hierarchical porous carbon nanospheres from polydopamine for high-performance supercapacitors. J. Mater. Chem. A5, 18242–18252. 10.1039/C7TA05880B
121
XuK. B.YangJ. M.HuJ. Q. (2018). Synthesis of hollow NiCo2O4 nanospheres with large specific surface area for asymmetric supercapacitors. J. Colloid Interface Sci.511, 456–462. 10.1016/j.jcis.2017.09.113
122
XuW.WangJ.DingF.ChenX.NasybulinE.ZhangY.et al. (2014). Lithium metal anodes for rechargeable batteries. Energy Environ. Sci.7, 513–537. 10.1039/C3EE40795K
123
YangX.DuG.ZhangL.LiuY. (2016). Preparation of hierarchical porous carbon material derived from starch for high-performance electrochemical capacitor. Mater. Lett.183, 52–55. 10.1016/j.matlet.2016.07.069
124
YangX.LiC.ChenY. (2017). Hierarchical porous carbon with ultrahigh surface area from corn leaf for high-performance supercapacitors application. J. Phys. D Appl. Phys.50:055501. 10.1088/1361-6463/50/5/055501
125
YangX.ShiK.ZhitomirskyI.CranstonE. D. (2015). Cellulose nanocrystal aerogels as universal 3D lightweight substrates for supercapacitor materials. Adv. Mater.27, 6104–6109. 10.1002/adma.201502284
126
YaoY.ZhangY.LiL.WangS.DouS. X.LiuX. (2017). Fabrication of hierarchical porous carbon nanoflakes for high-performance supercapacitors. ACS Appl. Mater. Interfaces9:34944. 10.1021/acsami.7b10593
127
YiJ.YanQ.WuC. T.ZengY.WuY.LuX.et al. (2017). Lignocellulose-derived porous phosphorus-doped carbon as advanced electrode for supercapacitors. J. Power Sources351, 130–137. 10.1016/j.jpowsour.2017.03.036
128
YuM.LiJ.WangL. (2016). KOH-activated carbon aerogels derived from sodium carboxymethyl cellulose for high-performance supercapacitors and dye adsorption. Chem. Eng. J.310, 300–306. 10.1016/j.cej.2016.10.121
129
YuS.LiuD.ZhaoS.BaoB.JinC.HuangW.et al. (2015). Synthesis of wood derived nitrogen-doped porous carbon–polyaniline composites for supercapacitor electrode materials. RSC Adv.5:30943–30949. 10.1039/C5RA01949D
130
YuanK.HuT.XuY.GrafR.BrunklausG.ForsterM.et al. (2016). Engineering the morphology of carbon materials: 2D porous carbon nanosheets for high-performance supercapacitors. Chemelectrochem3, 822–828. 10.1002/celc.201500516
131
ZhangL.YouT.TianZ.XiaZ.FengX. (2016a). Interconnected hierarchical porous carbon from lignin-derived byproducts of bioethanol production for ultra-high performance supercapacitors. ACS Appl. Mater. Interfaces8:13918. 10.1021/acsami.6b02774
132
ZhangL. L.ZhaoX. S. (2009). Carbon-based materials as supercapacitor electrodes. Chem. Soc. Rev.38:2520. 10.1039/b813846j
133
ZhangL. L.ZhouR.ZhaoX. S. (2010). Graphene-based materials as supercapacitor electrodes. J. Mater. Chem.20, 5983–5992. 10.1039/c000417k
134
ZhangW.LinH.LinZ.YinJ.LuH.LiuD.et al. (2015a). 3 D hierarchical porous carbon for supercapacitors prepared from lignin through a facile template-free method. ChemSusChem8, 2114–2122. 10.1002/cssc.201403486
135
ZhangW.ZhaoM.LiuR.WangX.LinH. (2015b). Hierarchical porous carbon derived from lignin for high performance supercapacitor. Colloids Surfaces A Physicochem. Eng. Aspects484, 518–527. 10.1016/j.colsurfa.2015.08.030
136
ZhangX.JiaoY.SunL.WangL.WuA.YanH.et al. (2015c). GO-induced assembly of gelatin toward stacked layer-like porous carbon for advanced supercapacitors. Nanoscale8, 2418–2427. 10.1039/C5NR07857A
137
ZhangY.JiaM.YuJ.FanJ.WangL.ZouY.et al. (2016b). A tunable hierarchical porous carbon from starch pretreated by calcium acetate for high performance supercapacitors. J. Solid State Electrochem.20, 733–741. 10.1007/s10008-015-3101-7
138
ZhaoJ.LaiH.LyuZ.JiangY.XieK.WangX.et al. (2015). Hydrophilic hierarchical nitrogen-doped carbon nanocages for ultrahigh supercapacitive performance. Adv. Mater.27, 3541–3545. 10.1002/adma.201500945
139
ZhaoY. Q.LuM.TaoP. Y.ZhangY. J.GongX. T.YangZ.et al. (2016). Hierarchically porous and heteroatom doped carbon derived from tobacco rods for supercapacitors. J. Power Sources307, 391–400. 10.1016/j.jpowsour.2016.01.020
140
ZhengK.FanX.MaoY.LinJ.DaiW.ZhangJ.et al. (2016a). The well-designed hierarchical structure of musa basjoo for supercapacitors. Sci. Rep.6:20306. 10.1038/srep20306
141
ZhengL.ZhiyuW.MengdiZ.ChangY.GangW.YanfengD.et al. (2016b). Sustainable synthesis and assembly of biomass-derived b/n co-doped carbon nanosheets with ultrahigh aspect ratio for high-performance supercapacitors. Adv. Funct. Mater.26, 111–119. 10.1002/adfm.201504004
142
ZhongY.ShiT.HuangY.ChengS.LiaoG.TangZ. (2018). One-step synthesis of porous carbon derived from starch for all-carbon binder-free high-rate supercapacitor. Electrochim. Acta269, 676–685. 10.1016/j.electacta.2018.03.012
143
ZhuD.WangY.LuW.ZhangH.SongZ.LuoD.et al. (2017). A novel synthesis of hierarchical porous carbons from interpenetrating polymer networks for high performance supercapacitor electrodes. Carbon111, 667–674. 10.1016/j.carbon.2016.10.016
144
ZhuL.GaoQ.TanY.TianW.XuJ.YangK.et al. (2015). Nitrogen and oxygen co-doped microporous carbons derived from theleaves of Euonymus japonicas as high performance supercapacitor electrode material. Micropor. Mesopor. Mater.210, 1–9. 10.1016/j.micromeso.2015.02.014
145
ZhuoH.HuY.TongX.ZhongL.PengX.SunR. (2016). Sustainable hierarchical porous carbon aerogel from cellulose for high-performance supercapacitor and CO2 capture. Ind. Crops Prod.87, 229–235. 10.1016/j.indcrop.2016.04.041
146
ZouR.QuanH.WangW.GaoW.DongY.ChenD. (2018). Porous carbon with interpenetrating framework from osmanthus flower as electrode materials for high-performance supercapacitor. J. Environ. Chem. Eng.6, 258–265. 10.1016/j.jece.2017.11.080
147
ZuG.ShenJ.ZouL.WangF.WangX.ZhangY.et al. (2016). Nanocellulose-derived highly porous carbon aerogels for supercapacitors. Carbon99, 203–211. 10.1016/j.carbon.2015.11.079
Summary
Keywords
biomass, porous carbon, supercapacitor, electrochemical performance, energy storage
Citation
Yang H, Ye S, Zhou J and Liang T (2019) Biomass-Derived Porous Carbon Materials for Supercapacitor. Front. Chem. 7:274. doi: 10.3389/fchem.2019.00274
Received
01 March 2019
Accepted
03 April 2019
Published
24 April 2019
Volume
7 - 2019
Edited by
Wenyao Li, Shanghai University of Engineering Sciences, China
Reviewed by
Kaibing Xu, Donghua University, China; Guangjin Wang, Hubei Engineering University, China
Updates
Copyright
© 2019 Yang, Ye, Zhou and Liang.
This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: Hui Yang yanghui_2521@163.comTongxiang Liang liang_tx@126.com
This article was submitted to Electrochemistry, a section of the journal Frontiers in Chemistry
†Co-first authors
Disclaimer
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.