Engineering Nanostructural Routes for Enhancing Thermoelectric Performance: Bulk to Nanoscale

Abstract

Thermoelectricity is a very important phenomenon, especially its significance in heat-electricity conversion. If thermoelectric devices can be effectively applied to the recovery of the renewable energies, such as waste heat and solar energy, the energy shortage, and global warming issues may be greatly relieved. This review focusses recent developments on the thermoelectric performance of a low-dimensional material, bulk nanostructured materials, conventional bulk materials etc. Particular emphasis is given on, how the nanostructure in nanostructured composites, confinement effects in one-dimensional nanowires and doping effects in conventional bulk composites plays an important role in ZT enhancement.

Introduction

Thermoelectric (TE) materials can directly contribute toward a global joint solution because they are capable of converting a thermal gradient into a voltage, and vice-versa, and thus to recover waste heat (Bell, 2008). Many advantages of this technology can be cited with respect to other approaches to refrigeration or power generation: Compactness and quietness, scalability, no moving parts, long, and reliable working life, local cooling or power generation, no need of maintenance and remarkably, the abundance of waste heat sources present in household and industrial processes (Rowe, 2006).

The performance of TE devices is assessed using the dimensionless figure of merit ZT = α²σT/κ, where α, σ, T, and κ are the Seebeck coefficient, the electrical conductivity, the absolute temperature, and the thermal conductivity, respectively. Because α, σ, and the electronic contribution to κ involve band structures (e.g., energy gap E_g, effective mass carrier m^*), and scattering mechanisms, controlling the parameters independently is difficult (Bell, 2008). Therefore, a ZT-value of 1 has long been considered a benchmark for practical TE materials. Based on the above relationship, optimally performing TE materials should possess high electrical conductivity, a large Seebeck coefficient, and low thermal conductivity (Bell, 2008). This review covers the latest advancement in TE technology focusing on the nanostructural approaches, provides comprehensive review on recent developments in nanowires and also highlights some of the most promising thermoelectric material system including Bi-Te alloys, CoSb₃ skutterudites, PbTe, AgSbTe₂ etc.

Research progress on nanostructured TE materials

One-dimensional TE materials: Nanowires

Low-dimensional TE materials such as quantum wells and nanowires are supposed to have excellent thermoelectric properties than their bulk counterparts, because of increase in the density of states (DOS) near Fermi level by quantum confinement which tends to enhance the Seebeck coefficient. And also effectively scatters phonon over a large mean free path (mfp) by high density of interfaces, hence resulting in the lower lattice thermal conductivity. Remarkable enhancement of ZT has been reported in one- dimensional (1D) thermoelectric materials.

Large enhancement of ZT inside quantum wires is predicted through theoretical studies due to its additional electron confinement. Hicks and Dresselhaus (1993) consider that nanowires can deliver higher thermoelectric performance because of stronger quantum confinement and enhanced phonon scattering, in comparison to bulk counterparts. Till now there have been various reports on the ZT enhancement in one-dimensional materials. Dedi et al. (2013) reported PbTe nanowire with diameter of 217 nm synthesized by stress induced method exhibited a maximal thermopower of −342 μVK⁻¹ at 375 K, which is two times larger than that of its bulk counterpart due to increase in the DOS of electrons near the Fermi level in the nanowires. The thermopower and power factor of the nanowires are shown in Figure 1. Measurement techniques for thermal conductivity of nanowires are always difficult and challenging, recently Lee et al. (2013) reported self-heating 3-omega technique that was applied to characterize the thermal conductivity of individual single crystalline Bi_1.75Sb_0.25Te_2.02 nanobelt with thickness 250 nm that was prepared by On-Film Formation method. This platform provides an opportunity to measure the TE properties including structure analysis on single nanowire, which would help improve the reliability of the resulting ZT-value. The measurement platform, power factor and thermal conductivity of the nanowires are shown in Figure 2. Boukai et al. (2008) also reported a large enhancement in ZT at low temperatures (~150 K) due to phonon drag effects (heat current affecting electrical transport). This is the first time it has been claimed that phonon-drag can enhance ZT significantly. The argument is that in rough nanowires, the Seebeck coefficient can be increased by the transport of certain phonon modes which have minimal contribution to thermal conductivity. An interesting study published by Hsiung et al. (2015) reported ZT = 0.36 can be obtained at room temperature for 180 nm diameter topological insulator Bi_1.5Sb_0.5Te_1.7Se_1.3 (BSTS) nanowires synthesized by stress-induced method, representing 10 times higher than compared to its bulk counterpart because of surface-dominated transport and large insulating bulk state in the BSTS nanowires. The thermal conductivity and power factor of the nanowires are shown in Figure 3.

Figure 1

Figure 2

Figure 3

Three-dimensional TE materials: Nanocomposites

Nanostructured materials are among the strongest candidates for thermoelectric applications, as they offer a route to suppressing thermal conductivity without hindering electrical properties. Second phase endotaxial nanostructuring (Ikeda et al., 2007), metal nanoparticle decoration (Lee et al., 2012), and most recently all-length scale phonon scattering (Biswas et al., 2012) have been experimentally proved to be effective routes to improve the ZT through significant reduction of the lattice thermal conductivity, κ_lat.

AgSbTe₂ based chalcogenide

The best studied bulk nanocomposite material is based on p-type Silver Antimony Telluride (AgSbTe₂), one of the traditional thermoelectric materials, which spontaneously forms nanostructures efficiently scatters phonons, without the need for artificial nanostructuring confirmed from neutron scattering and high resolution transmission electron microscope (HRTEM) investigations (Ma et al., 2013). Several studies have reported on effect of natural formation of nanoscale impurities on matrix and its contribution on ZT improvements in bulk nanostructured AgSbTe₂ materials come from very large reduction in κ_lat(Xu et al., 2010; Zhang et al., 2010; Du et al., 2011). The Ternary chalcogenide AgSbTe₂ has already gained attention for both thermoelectric and optical phase-change applications, because of its extremely low thermal conductivity, κ_tot = 0.6 ~ 0.7 W/m/K (Hockings, 1959; Morelli et al., 2008). AgSbTe₂ is widely identified as a rock salt NaCl type (Fm-3m) where Ag and Sb randomly occupying the Na site whereas Te is located at the Cl position shown in Figure 4A. Its lattice component κ_lat, dominates largely on the total thermal conductivity, which is related to the propagation of phonons. The κ_lat in rock salt AgSbTe₂ is about three fold lower than that of PbTe at around room temperature. It has been reported that band gap ~0.35 eV at room temperature were obtained by optical diffuse reflectance measurements, whereas strong degenerate nature reflects the electrical conductivity. Recently, the AgSbTe₂ compound has attracted considerable attention in constructing so-called bulk nanostructured TE materials, such as (AgSbTe₂)_1−x(PbTe)_x (LAST-m) (Hsu et al., 2004), (AgSbTe₂)_1−x(GeTe)_x (TAGS) (Yang et al., 2008), and AgSbTe₂–SnTe (Chen et al., 2012) with excellent TE properties. TAGS based alloys, which have been studied for many years and used in National Aeronautics and Space Administrative (NASA) missions since the early 1970s. The LAST-m system is an interesting bulk-grown material that spontaneously forms nanostructures during cooling from the melt.

Figure 4

Recent studies has been reported that element doping or substitution technique has succeeded in enhancing the thermoelectric performance of AgSbTe₂ materials by tuning its electrical and thermal properties (Jovovic and Heremans, 2009). Moreover, the doping of appropriate semiconductor material is a potential way to enhance the thermoelectric properties of AgSbTe₂ based alloy by reducing its lattice thermal conductivity and adjusting its carrier concentration. Du et al. (2010) investigated AgSbTe₂ compounds by selenium (Se) doping; the electrical conductivity was enhanced greatly with an increase in the Se doping concentration. In 2014, Mohanraman et al. (2014a) reported on AgSbTe₂ compound doped with tin (Sn), the Ag₂Te nanoprecipitates with feature size of 100–500 nm were observed in AgSbTe₂ matrix are effective in scattering the phonons with mid-to-long mean free paths shown in Figures 4B,C and achieved a ZT ~ 1.1 at 600 K representing an enhancement greater than 20% compared with a pristine sample shown in Figure 4D.

Moreover, recent study published by Mohanraman et al. (2013) on doping effect of bismuth (Bi) on AgSbTe₂ material demonstrated that the Bi doping has significantly enhanced phonon scattering process through point defects over the entire temperature range, they possessed lower thermal conductivity and achieved a high ZT-value ~ 1.0 at 570 K shown in Figure 4D. Mohanraman et al. (2014b) reported on influence of indium (In) doping in AgSbTe₂ material, the results showed enhanced power factor over 25–30% because of the increase in Seebeck coefficient related to decreased in carrier concentration and increase of the effective mass caused by In doping whereas lattice thermal conductivities were reduced substantially because of lattice mismatch arise from the dopants and host atoms having different atomic weights and thus resulted in enhanced phonon scattering. The highest ZT = 1.35 is achieved for Ag(Sb_0.97In_0.03)Te₂ sample at 650 K shown in Figure 4D has promising applications in TE power generation in the intermediate temperature range. Furthermore, various studies on AgSbTe₂ based alloys shows that the thermoelectric performances have been greatly improved by suitable types of dopants. Techniques such as doping or substitution have considerably decreased the lattice thermal conductivity, particularly in the high temperature range. All the results show that doping technique for enhancement of thermoelectric performance for AgSbTe₂ based composites is reliable.

Bi₂Te₃—bulk nanocomposites

Bi₂Te₃ based alloys, the excellent TE materials at room temperature, are extensively used for the commercial thermoelectric devices for thermo-cooling application. Significant enhancement in the ZT-value of Bi₂Te₃ based bulk materials has been reported recently (Wood, 1988; Zhao et al., 2005; Cao et al., 2008; Poudel et al., 2008; Xie et al., 2009; Kim et al., 2015) shown in Figure 5. Poudel et al. (2008) reported nanostructure p-type Bi_xSb_2−xTe₃ system fabricated by mechanical milling followed by hot pressing, exhibited ZT ≈ 1.4 at 373 K. In their study reveals that ZT enhancement is partially attribute to reduction of κ_lat due to scattering at the grain boundary and the presence of nanoprecipitates. Melt spinning followed by spark plasma sintering (SPS) method fabricated bulk nanocomposite p-type (Bi,Sb)₂Te₃ ingot with a ZT-value of 1.56 at 300 K published by Xie et al. (2009). The material features nanocrystalline domains embedded in matrix composed of 5–15 nm nanocrystals with coherent grain boundaries are believed to attribute for significant reduction of thermal conductivity without degrading the electrical properties. Cao et al. (2008) obtained a high ZT-value of 1.47 at 438 K for Bi₂Te₃/Sb₂Te₃ bulk nanocomposite with nanoscale laminated structures prepared by a simple route involving hydrothermal synthesis and hot pressing. Kim et al. (2015) reported record ZT-value of 2.01 at 320 K due to generation of dislocation arrays at grain boundaries in Bi_0.5Sb_1.5Te₃ by liquid phase compaction greatly reduce their thermal conduction, leading to an enhancement of their thermoelectric conversion efficiency.

Figure 5

In our point of view, nanocomposites and controlled two-dimensional coated nanostructures are the solution to effectively minimize thermal conductivity and promote figure of merit (ZT). Lan et al. (2012) demonstrated a method to introduce nano-coating structures into surface of bulk material by using a hydrothermal process. A fine crystalline layer of Bi₂Te₃ was coated onto the surfaces of Bi seed micron-sized particles. After that, highly densified pellets were successfully obtained by the subsequent hot-press at around 400 K and a uniaxial pressure of 680 MPa for 30 min. Binary-phase particles composed of micro-sized Bi particles and nanosize Bi₂Te₃ were prepared via the aforementioned process.

The morphology of the samples is studied by SEM. In Figure 6A, the difference between before and after the coating process is shown. The surface of particles after the hydrothermal process is fuzzier and the EDS analysis shows larger amounts of Te on the boundary of the two particles. This indicates that Bi₂Te₃is very small, or a very thin layer of Bi₂Te₃ is coated on the surface of Bi grains. Figure 6B shows that the existence of boundaries in the bulk sample is more obvious after grinding. Figure 6Ba shows that grain boundaries can still be observed by SEM. The EDS mapping analysis (Figure 6Bb) shows larger amounts of Te along the boundary, and that the coating layer is less than few micrometers.

Figure 6

The nano-coating process even slightly decreases electrical resistivity and maintains the values of Seebeck coefficient at the same value shown in Figures 6C,D respectively. Furthermore, when the sizes of Bi seed particles decrease, the total thermal conductivity decrease with the same trend is shown in Figure 6E. All four samples show similar downward tendency. Because the TE property of Bi₂Te₃ near the room temperature is at an advantageous position, the small decrease of electrical resistivity and the values of Seebeck coefficient can be explained by the existence of Bi₂Te₃ thin layer. Furthermore, the thermal conductivity κ was gradually diminished while the grain size was reduced. This also indicates that the quantity of grain boundaries is influenced by the thermoelectric property. The coating process might scatter the phonons but not the electrons. Moreover, the electrical resistivity was also diminished when the Bi₂Te₃ was coated on. This may be because the coating layer is more flexible than the core material making for better contact of particles than with the single phased material. Hence, the nano-coating process can increase the figure of merit (ZT) because the coating layers provide more boundaries and also prohibit the aggregation of particles within the sintering process. Increasing the number of grain boundaries could efficiently reduce the thermal conductivity without the reduction of electrical conductivity. We found that reducing thermal conductivity leads to a dimensionless figure of merit ZT ~ 0.278 at ~300 K shown in Figure 6F, more than an appreciable improvement over commercial Bi powder treated with the same hot-press process. We propose a new route for developing high performance Bi nano-composites by using a hydrothermal nano-coating process, which have even broader prospects for commercial applications. The combination of nano-coating layers and Bi seed particles with subsequent hot-pressed process affect the TE properties of the Bi, leading to a significant enhancement of the figure of merit. The enhancement of ZT was primarily influenced by an appreciable reduction in the thermal conductivity. It was due to presence of nanostructured regions existing within the material as the result of our processing route.

PbTe nanocomposites

PbTe alloys are one of the premiere TE materials for intermediate range temperature (500–800 K) applications and played a key role in radioisotope thermoelectric generator for deep space exploration program as a power source. Recently, Kanatzidis group has published many reports on significant improvements in the thermoelectric properties of PbTe based alloys by nanostucturing and also modification in density of states through band structures (Zhao et al., 2014) shown in Figure 7. A recent study published by Biswas et al. (2012) has reported a high record of ZT-value of 2.2 at 915 K for p type PbTe-SrTe system via grain boundary phonon scattering enabled by nanostructuring to reduce the thermal conductivity.

Figure 7

CoSb₃ nanocomposites

CoSb₃ based skutterudites are highly promising candidate for medium temperature TE power generation applications because both n and p type materials with high performance can be obtained in the same material system. The most remarkable feature of this compound is that the cage like open structure are found and can be filled with foreign atoms acting as phonon rattlers which scatter phonons strongly thus drastically reduces the thermal conductivity. Nanocomposites, as an efficient way to reduce the thermal conductivity via grain boundaries and nanoinclusions, have also been used in CoSb₃ based TE materials. Significant advances have been made in recent years with various kinds of nanoinclusion filling the cages in this compound (Bertini et al., 2003; Zhao et al., 2006; Li et al., 2009; Yang et al., 2009; Xiong et al., 2010; Fu et al., 2015) and shown in Figure 8. Fu et al. (2015) reported formation of core-shell microstructure in compounds doped with 2% of Ni, has enhanced ZT to 1.07 at 723 K. Li et al. (2009) observed in situ formation of InSb nanoislands in the In_0.2Ce_0.5Co₄Sb₁₂ nanocomposite with enhanced ZT up to 1.43 at 800 K by significant reduction in thermal conductivity. Zhao et al. (2006) fabricated Yb_0.25Co₄Sb₁₂ nanocomposite and well distributed Yb₂O₃ particles synthesized by in situ reaction. The Yb₂O₃ nanoinclusions located at the grain boundaries are effective in scattering phonons, there by increases the figure of merit and achieved peak ZT of 1.3 at 850 K. Xiong et al. (2010) has reported formation of GaSb nanoinclusions for the (GaSb)_0.2-Yb_0.26Co₄Sb₁₂ nanocomposite exhibiting peak ZT-value of 1.45 at 850 K.

Figure 8

Conclusions and outlook

This review summarizes the recent progress of nanowires; Ag-Sb based alloys, PbTe, CoSb₃ skutterudites, and Bi₂Te₃ based nanocomposites. Nanostructures such as nanoprecipitates, controlled two-dimensional coated nanostructures, nanoinclusion to atomic defects, and nanoscale inhomogeneities have been found to be potential routes for reducing thermal conductivity to a greater extend without hindering much on electrical conductivity, resulting in an enhanced figure of merit for the bulk nanocomposite material. However, additional approaches such as carrier-energy filtering or quantum confinement effects will likely be key role for enhancing power factor to achieve further significant ZT enhancement. Overall from our practical point of view, bulk nanocomposites shows more exciting than nanowires or nanobelts because the former can reduce the expenses, scale-up, and thermal management issues normally related with the later.

Conflict of interest statement

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

References

• 1

  BellL. E. (2008). Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science321, 1457–1461. 10.1126/science.1158899

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 2

  BertiniL.BilliquistK.ChristensenM.GattiC.HolmgrenL.IversenB.et al. (2003). Thermoelectrics, 2003 Twenty-Second International Conference on ICT (La Grande Motte).

  • Google Scholar

• 3

  BiswasK.HeH.BlumI. D.WuC. I.HoganT. P.SeidmanD. N.et al. (2012). High-performance bulk thermoelectrics with all-scale hierarchical architectures. Nature489, 414–418. 10.1038/nature11439

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 4

  BoukaiA. I.BunimovichY.Tahir-KheliJ.YuJ. K.GoddardW. A.III.HeathJ. R. (2008). Silicon nanowires as efficient thermoelectric materials. Nature451, 168–171. 10.1038/nature06458

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 5

  CaoY. Q.ZhaoX. B.ZhuT. J.ZhangX. B.TuJ. P. (2008). Synthesis and thermoelectric properties of Bi₂Te₃/Sb₂Te₃ bulk nanocomposites with laminated structures. Appl. Phys. Lett. 92, 143106. 10.1063/1.2900960

  • CrossRef
  • Google Scholar

• 6

  ChenY.NielsenM. D.GaoY. B.ZhuT. J.ZhaoX.HeremansJ. P.et al. (2012). SnTe–AgSbTe2 thermoelectric alloys. Adv. Energ. Mater. 2, 58–62. 10.1002/aenm.201100460

  • CrossRef
  • Google Scholar

• 7

  DediLee, P. C.ChienC. H.DongG. P.HuangW. C.ChenC. L.TsengC. M.et al. (2013). Stress-induced growth of single-crystalline lead telluride nanowires and their thermoelectric transport properties. Appl. Phys. Lett. 103, 023115. 10.1063/1.4813606

  • CrossRef
  • Google Scholar

• 8

  DuB.LiH.XuJ.TangX.UherC. (2010). Enhanced figure-of-merit in Se-doped p-Type AgSbTe₂ thermoelectric compound. Chem. Mater. 22, 5521–5527. 10.1021/cm101503y

  • CrossRef
  • Google Scholar

• 9

  DuB.LiH.XuJ.TangX.UherC. (2011). Enhanced thermoelectric performance and novel nanopores in AgSbTe₂ prepared by melt spinning. J. Solid State Chem. 184, 109–114. 10.1016/j.jssc.2010.10.036

  • CrossRef
  • Google Scholar

• 10

  FuL.YangY.PengJ.JiangQ.XiaoY.LuoY.et al. (2015). Enhancement of thermoelectric properties of Yb-filled skutterudites by a Ni-Induced “core-shell” structure. J. Mater. Chem. A3, 1010–1016. 10.1039/C4TA05083E

  • CrossRef
  • Google Scholar

• 11

  HicksL. D.DresselhausM. S. (1993). Thermoelectric figure of merit of a one-dimensional conductor. Phys. Rev. B Condens. Matter.47, 16631–16634. 10.1103/PhysRevB.47.16631

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 12

  HockingsE. F. (1959). The thermal conductivity of silver antimony telluride. J. Phys. Chem. Solids10, 341. 10.1016/0022-3697(59)90014-9

  • CrossRef
  • Google Scholar

• 13

  HsiungT. C.MouC. Y.LeeT. K.ChenY. Y. (2015). Surface-dominated transport and enhanced thermoelectric figure of merit in topological insulator Bi_1.5Sb_0.5Te_1.7Se_1.3. Nanoscale7, 518–523. 10.1039/C4NR05376A

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 14

  HsuK. F.LooS.GuoF.ChenW.DyckJ. S.UherC.et al. (2004). Cubic AgPb_mSbTe_2+m: bulk thermoelectric materials with high figure of merit. Science303, 818–821. 10.1002/chin.200417240

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 15

  IkedaT.CollinsL. A.RaviV.GascoinF. S.HaileS. M.SnyderG. J.et al. (2007). Self-assembled nanometer lamellae of thermoelectric PbTe and Sb₂Te₃ with epitaxy-like interfaces. Chem. Mater.19, 763–767. 10.1021/cm062121p

  • CrossRef
  • Google Scholar

• 16

  JovovicV.HeremansJ. P. (2009). Doping effects on the thermoelectric properties of AgSbTe2. J. Electron. Mater.38, 1504. 10.1007/s11664-009-0669-7

  • CrossRef
  • Google Scholar

• 17

  KimS.LeeK. H.MunH. A.KimH. S.HwangS. W.RohJ. W.et al. (2015). Dense dislocation arrays embedded in grain boundaries for high performance bulk thermoelectrics. Science348, 109–114. 10.1126/science.aaa4166

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 18

  LanT. W.ChenY. C.HoJ. C.ShyuS. G.ChenY. Y. (2012). Thermoelectric figure of merit enhancement in Bi₂Te₃-Coated Bi composites. J. Electron. Mater.41, 2326–2340. 10.1007/s11664-012-2154-y

  • CrossRef
  • Google Scholar

• 19

  LeeK. H.KimH. S.KimS. I.LeeE. S.LeeS. M.RhyeeJ. S.et al. (2012). Enhancement of thermoelectric figure of merit for Bi_0.5Sb_1.5Te₃ by metal nanoparticle decoration. J. Electron. Mater.41, 1165–1169. 10.1007/s11664-012-1913-0

  • CrossRef
  • Google Scholar

• 20

  LeeP. C.ChenH. C.TsengC. M.LaiW. C.LeeC. H.ChangC. S.et al. (2013). Thermoelectric properties of an individual Bi_1.75Sb_0.25Te_2.02 nanowire. Chin. J. Phys. 51, 854–861. 10.6122/CJP.51.854

  • CrossRef
  • Google Scholar

• 21

  LiH.TangX.ZhangQ.UherC. (2009). High performance In_xCe_yCo₄Sb₁₂ thermoelectric materials with in situ forming nanostructured InSb phase. Appl. Phys. Lett. 94, 102114. 10.1063/1.3099804

  • CrossRef
  • Google Scholar

• 22

  MaJ.DelaireO.MayA. F.CarltonC. E.McGuireM. A.VanBebberL. H.et al. (2013). Glass-like phonon scattering from a spontaneous nanostructure in AgSbTe₂. Nat. Nanotech. 2, 445–451. 10.1038/nnano.2013.95

  • CrossRef
  • Google Scholar

• 23

  MohanramanR.SankarR.BoopathiK. M.ChouF. C.ChuC. W.LeeC. H.et al. (2014b). Influence of In doping on the thermoelectric properties of an AgSbTe₂ compound with enhanced figure of merit. J. Mater. Chem. A2, 2839–2844. 10.1039/c3ta14547f

  • CrossRef
  • Google Scholar

• 24

  MohanramanR.SankarR.ChouF. C.LeeC. H.ChenY. Y. (2013). Enhanced thermoelectric performance in Bi-doped p-type AgSbTe₂ compounds. J. Appl. Phys. 114, 163712. 10.1063/1.4828478

  • CrossRef
  • Google Scholar

• 25

  MohanramanR.SankarR.ChouF. C.LeeC. H.IizukaY.MuthuselvamI. P.et al. (2014a). Influence of nanoscale Ag₂Te precipitates on the thermoelectric properties of the Sn doped P-type AgSbTe₂ compound. APL Mater. 2, 096114. 10.1063/1.4896435

  • CrossRef
  • Google Scholar

• 26

  MorelliD. T.JovovicV.HeremansJ. P. (2008). Intrinsically minimal thermal conductivity in cubic I-V-VI₂ semiconductors. Phys. Rev. Lett. 101:035901. 10.1103/PhysRevLett.101.035901

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 27

  PoudelB.HaoQ.MaY.LanY.MinnichA.YuB.et al. (2008). High thermoelectric performance of nanostructured bismuth antimony telluride bulk alloys. Science320, 634. 10.1126/science.1156446

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 28

  RoweD. M. (2006). Thermoelectrics Handbook: Macro to Nano. Boca Raton, FL: CRC.

  • Google Scholar

• 29

  WoodC. (1988). Materials for thermoelectric energy conversion. Rep. Prog. Phys. 51, 459–539. 10.1088/0034-4885/51/4/001

  • CrossRef
  • Google Scholar

• 30

  XieW.TangX.YanY.ZhangQ.TrittT. M. (2009). Unique nanostructures and enhanced thermoelectric performance of melt-spun BiSbTe alloys. Appl. Phys. Lett. 94, 102111. 10.1063/1.3097026

  • CrossRef
  • Google Scholar

• 31

  XiongZ.ChenX.HuangX.BaiS.ChenL. (2010). High thermoelectric performance of Yb_0.26Co₄Sb₁₂/yGaSb nanocomposites originating from scattering electrons of low energy. Acta Mater. 58, 3995–4002. 10.1016/j.actamat.2010.03.025

  • CrossRef
  • Google Scholar

• 32

  XuJ.LiH.DuB.TangX.ZhangQ.UherC.et al. (2010). High thermoelectric figure of merit and nanostructuring in bulk AgSbTe₂. J. Mater. Chem. 20, 6138–6143. 10.1039/c0jm00138d

  • CrossRef
  • Google Scholar

• 33

  YangJ.HaoQ.WangH.LanY. C.HeQ. Y.MinnichA.et al. (2009). Solubility study of Yb in n-type skutterudite Yb_xCo₄Sb₁₂ and their enhanced thermoelectric properties. Phys. Rev. B80:115329. 10.1103/PhysRevB.80.115329

  • CrossRef
  • Google Scholar

• 34

  YangS. H.ZhuT. H.SunT.HeJ.ZhangS. N.ZhaoX. B.et al. (2008). Nanostructures in high-performance (GeTe)_x(AgSbTe₂)_100−x thermoelectric materials. Nanotechnology19:245707. 10.1088/0957-4484/19/24/245707

  • Pubmed Abstract
  • CrossRef
  • Google Scholar

• 35

  ZhangS. N.ZhuT. J.YangS. H.YuC.ZhaoX. B. (2010). Improved thermoelectric properties of AgSbTe₂ based compounds with nanoscale Ag₂Te in situ precipitates. J. Alloys. Compd. 499, 215–220. 10.1016/j.jallcom.2010.03.170

  • CrossRef
  • Google Scholar

• 36

  ZhaoL. D.DravidV. P.KantzidisM. G. (2014). The panascopic approach to high performance thermoelectrics. Energy Environ. Sci. 7, 251–268. 10.1039/C3EE43099E

  • CrossRef
  • Google Scholar

• 37

  ZhaoX. B.JiX. H.ZhangY. H.ZhuT. J.TuJ. P.ZhangX. B.et al. (2005). Bismuth telluride nanotubes and the effects on the thermoelectric properties of nanotube-containing nanocomposites. Appl. Phys. Lett. 86, 062111. 10.1063/1.1863440

  • CrossRef
  • Google Scholar

• 38

  ZhaoX. Y.ShiX.ChenL. D.ZhangW. Q.BaiS. Q.PeiY. Z.et al. (2006). Synthesis of Yb_yCo₄Sb₁₂/Yb₂O₃ composites and their thermoelectric properties. Appl. Phys. Lett. 89, 092121. 10.1063/1.2345249

  • CrossRef
  • Google Scholar