Abstract
Environmental pollution as a result of urban and industrial wastewater has become an increasingly prominent issue. Rivers, lakes, and oceans that have become eutrophicated or polluted by suspended solids and hazardous substances in wastewater have endangered the environment. A root cause of this is the discharge of untreated urban and industrial wastewater into the ecosystem. As a solution to the pollution, wastewater treatment facilities have seen increasingly rapid development. Sewage pumps are designed to transport urban and industrial wastewater containing solid particles or hazardous substances to water treatment centers for purification and treatment. Sewage pumps are of great importance in the entire wastewater treatment system. Sewage in the environment where sewage pumps work usually contains sands, suspended particles, and plenty of saline ions. Flow passage components and sealing elements of the pump become vulnerable to abrasion and chemical corrosion, which further challenges operational stability of the pump. Research has remained focused on how to improve reliability of sewage pumps under severe conditions. Because of advances in materials science, the application of an increasing number of new materials has been witnessed, such as carbon-based composite materials and carbon nanomaterials, thanks to their fine self-lubrication performance, heat resistance, thermal and electrical conductivity, chemical stability, heat and seismic resistance, as well as plasticity. These properties contribute to enormous potential that new carbon-based composite materials and carbon nanomaterials have to offer in terms of corrosion resistance. This paper outlines application scenarios, research progress, and the prospect of new materials in sewage pumps.
Introduction
As urban areas are becoming increasingly populated (McNabb, 2019) along with urbanization, it is expected that by 2050, a total of over 900 million people will be living in cities. By then, a soaring increase of domestic and industrial wastewater (Solon et al., 2017) will adversely cause wastewater pollution (Yan et al., 2015). Over 80% of wastewater in developing countries is discharged without treatment, resulting in river, lake, ocean, and soil eutrophication or pollution caused by suspended solids and hazardous substances. These sources of pollution are extremely detrimental to natural biology and mankind (Venkateswaran et al., 2007; Fan and Zhang, 2014; Savriama et al., 2015; Chen et al., 2017; Bougnom et al., 2019), contributing to untreated discharge of urban and industrial wastewater (Kadiya et al., 2013). In recent years we have witnessed increasingly-rapid development of wastewater treatment facilities as a solution to pollution issues (Sun et al., 2020, 2021). Among other solutions, sewage pumps, a type of centrifugal pump for sewage transport, are mainly designed to transport urban and industrial wastewater containing solid particles or hazardous substances, to water treatment centers for purification and treatment. The sewage pumps are of great importance in the entire wastewater treatment system. Conventional sewage pumps, in general, are made of stainless steel. Exposed to urban and industrial wastewater—which usually contains plenty of saline ions and slurry in solid particles—conventional materials, such as stainless steel, are vulnerable to abrasion and corrosion. Under the influence of solid particles and saline ions, flow passage components of the pump tend to fail partially, the size of the abrasion and corrosion increases and operational efficiency of the centrifugal pump decreases, resulting in enormous energy waste. Statistics show that electric energy consumed by the centrifugal pump accounts for 25–60% of total consumption (Sahoo and Guharoy, 2009). In the worst scenarios, the centrifugal pump may fail or trip, causing additional and significant maintenance costs (equals up to 50% of routine maintenance cost) (Sahoo and Guharoy, 2009). Abrasion and corrosion of the components from solid particles are deemed to be one of the leading contributors to pump failure (Kwok et al., 2000; Guo et al., 2005; Wood, 2006; Barik et al., 2009). Therefore, it is crucial to diagnose and take preventative actions at an early stage, to prolong service life of the pump and to reduce the economic loss to the greatest extent. Such abrasion may be defined as abrasion of structural members (mainly including blades of hydraulic turbine, pressure pipeline, hydraulic seal, and casing) from flowing solid particles that impact target surfaces at a very high speed (Padhy and Saini, 2009). As we are aware of the presence of abundant solids in pumped liquids, we should replace internal materials of the pump with materials with higher corrosion resistance, such as carbon steel, high-chromium iron, hardened stainless steel, ceramics, tungsten alloy, or other hard coatings that are frequently used as alternatives. Carbon-based composite materials and carbon nanomaterials, distinguished for fine mechanical property under high temperature, heat resistance, abrasion and corrosion resistance, and low thermal expansion (Schmidt et al., 1999; Wang et al., 2003; Chen et al., 2010; Sun et al., 2019), are good options for upgrading the reliability of sewage pumps. For this purpose, this paper elaborates on abrasion and corrosion resistance, chemical stability, and other aspects of carbon-based materials, and outlines their application prospects to improve reliability and service life of sewage pumps.
Abrasion Resistance of Carbon-Based Composite Materials
Abrasion of metallic materials refers to the materials' loss of volume as a result of corrosion, cavitation, fouling, particle surface impact, etc. Centrifugal sewage and slurry pumps are often observed with material loss from particle impact, corrosion, erosion, etc. Depending on the shape, pump abrasion from particles contained in wastewater can be divided into sliding abrasion and impact abrasion (Wilson and Clift, 2006). Abrasion on such rotary parts as impellers is almost uniform, while that on a pump case is not (Roco et al., 1984), with abrasion at the cut-water particularly being the worst (Pagalthivarthi et al., 1990). Mueller et al. (1978) observed how badly a specimen stuck to the inner side of the pump case had been abraded, and they also assessed its corrosion. Among all the eight types of materials with different levels of hardness, they identified that the hard alloy stood out in the abrasion resistance test. Therefore, they proposed to coat the volute-shaped inner wall and impeller surface of the sewage pump with a layer of hard material, so that it could help the pump build higher resistance to abrasion at a low angle of impact. According to studies of Walker et al. (1994), impeller of the sewage pump was more likely to break down when exposed to larger solid particles, while the front shroud was more vulnerable to abrasion when exposed to smaller solid particles.
Owing to their superior abrasive resistance, new carbon-based materials demonstrate a great prospect of their application in sewage pumps for abrasion resistance purposes. Chen et al. (2019) designed an impeller of a centrifugal pump with new SiCNFs- carbon-carbon composite materials, and they found that abrasion resistance of the impeller became significantly upgraded, with abrasion loss considerably lower than that of ordinary carbon-carbon composite materials, particularly abrasion in a vertical direction. According to Shi et al. (2018) study on how the content of carbon fiber impacted anti-abrasion performance of a nickel-based composite coating, the structure of the material layers was found to be the most uniformly distributed and the abrasion resistance was 1.7 times that of the Ni-based coating without a carbon fiber, when the carbon fiber content reached 6%. Compared with an ordinary stellite without a carbon fiber, the type of stellite composite material prepared by Khoddamzadeh et al. (2014) with 5% carbon fiber, gained significant improvement in terms of hardness and abrasion resistance. In comparison with copper-based composite materials without a carbon fiber, as studied by Tang et al. (2008), the same materials with a short carbon fiber had a considerably higher abrasion resistance, and a dramatically lower friction coefficient and abrasion loss, yet with a slightly lower microhardness. Algul et al. (2015) finding reveals that the higher the content of graphene was, the significantly higher the microhardness and abrasion resistance of the nickel-based composite materials would be. Contributing to the higher abrasion resistance was the superior mechanical strength and lubricating effect that graphene had to offer. Wu et al. (2015) prepared a uniform graphene oxide coating on a low-carbon steel surface and discovered that graphene oxide in some concentrations were positive to abrasion resistance and microhardness of the coating. The graphite-copper composite material prepared by Moustafa et al. (2002) under a powder metallurgy process, demonstrated a lower abrasion rate and friction coefficient than pure copper and could withstand a 500N load when graphite content reached 20%. Du et al. (2004) abrasion test of Al2O3 composite materials with different contents of short fiber showed that, the lowest abrasion rate of the materials could be reached when the content of short fiber was 12%. Bushueva et al. (2019) studied texture, mechanical and tribological property of modified coating on chromium-nickel austenitic steel surface, and concluded that carbide could notably contribute to higher microhardness of materials and a 1.4 times higher abrasion resistance, when compared with ordinary materials without the coating. As for stainless steel, the surface of which was coated with reinforced nickel-based composite materials by laser cladding technique, Lei et al. (2017) studied and concluded that carbon fiber could work to effectively improve corrosion and abrasion resistance of a nickel-based coating. Suresh et al. (in press) managed to combine carbon fiber and aluminum oxide packing, and concluded that coating prepared by a thermal evaporation technique is an incredibly efficient solution to abrasion resistance under any load. From the study on abrasive performance of reinforced vinyl ester composite material with carbon fiber, Suresha and Kumar (2009) inferred that the abrasion rate of the material reached only 40% of the same material with glass.
Corrosion Resistance of Carbon-Based Composite Materials
Centrifugal sewage pumps in urban, industrial, mining, and other applications are usually made of stainless steel 304 which primarily consists of iron, carbon, and at least 11% chromium. Among others, chromium is known as a corrosion-resistant element and helps improve anti-strip performance, strength, and abrasion resistance of materials. High corrosion resistance of alloy is dependent on a layer of invisible film, a passivation coating that is stable, durable, of adhesive power, and self-repair ability (Ilevbare and Burstein, 2003). Despite its very high corrosion resistance in a variety of mediums, austenitic stainless steel still could not avoid corrosive pitting when exposed to chlorides (Fossati et al., 2006). Chloridion is the main contributor to this corrosion (Meguid et al., 2000; Yang and Luo, 2001; El-Egamy and Badaway, 2004). Some theoretical explanations for the occurrence of this corrosive pitting, for example local acidification (Galvele, 1978), depassivation-repassivation behaviors (Richardson and Wood, 1970; Dawson and Ferreira, 1986), point defect model (Chao et al., 1981; Macdonald and Urquidi-Macdonald, 1985), and anion-permeable membrane/migration (Okamoto, 1973), are available, but they all suppose that chloridion is absorbed onto the metal surface. Coating works to isolate the steel surface from corrosive environment and prevents diffusion of oxygen, vapor or ion (Liu et al., 2003). As an inorganic non-metallic material, carbon fiber remained unaffected by oxygen in the wastewater and avoided falling off under the effect of ions in the solution on one hand; and served as an anti-corrosion film and provided fine abrasion resistance and hardness on the other hand, making metal protection less vulnerable to degradation from abrasion and falling of solid particles.
Ge et al. (2020) added carbon fiber packing into zinc-rich epoxy coating to increase its electrical conductivity, and found that this coating could protect copper-based material in 3.5% NaCl solution for up to 50 days, much longer than the protection duration by carbon-fiber-free zinc-rich epoxy coating. Liu et al. (2016) introduction of 0.5% graphene to the epoxy coating promoted its resistance to corrosion, with the corrosion rate being an order of a magnitude lower than graphene-free coating. According to Zhou et al. (2019) findings, graphene oxide worked to effectively prolong the duration of zinc-rich epoxy cathodic protection and fully protected metals, thanks to its superior conductivity. After adding a 0.5% graphene nanosheet, Chen et al. (2017) made a conclusion that the excellent mechanical and barrier properties of graphene nanosheet could considerably improve corrosion resistance of coating. Lei et al. (2017) studied and proved that carbon fiber on the surface could work to upgrade nickel-based coating's resistance to corrosion in an effective way (e.g., corrosion current density of composite coating was only 7% that of nickel-based coating). Cheng et al. (2019) proposed a type of new technology for preparing composite films with adhesive protein and graphene, as their graphene film demonstrated strong adhesive force to carbon steel, which could notably improve corrosion resistance of carbon steel. Jiang et al. (2017) adopted a ultrasonic vibration direct-current electrodeposition technique and prepared a nanometer Ni-Mo/graphene oxide composite material on the surface of low-carbon steel, and proved that the material had been considerably improved in terms of resistance to corrosion and oxidization.
Conclusions and Prospect
In light of their extensive application in wastewater treatment systems and the extremely adverse environment that they are intended to work in, it has become a an area of focus for researchers to try figure out how to improve the sewage pumps' resistance to abrasion and corrosion, reliability, and service life. In pursuit of solutions, researchers have been devoted to studies on abrasion and corrosion resistance of carbon fiber, carbon-carbon composite materials, and carbon nanocomposite, as well as on how to reduce abrasion and corrosion from particles. Unlike conventional metal materials, weaknesses, however, persist and limit continuous high-quality production of carbon composite materials, as their development and application started at a later stage. Considering that a great many novel carbon composite materials are still under study and undergoing experiments, and the growth mechanism of some carbon materials is yet to be elucidated, carbon materials are restricted in terms of mass production and application without having a clear understanding of how to restructure or control the material structure. Therefore, it becomes imperative to delve into abrasion and corrosion-resistant carbon materials and to develop distinctive carbon materials on the basis of their features and superior performance. Future studies should focus on how to develop special carbon materials with more resistance to heat, abrasion and corrosion, chemical stability, high weight-rigidity ratio, fine self-lubrication, etc. In the future, the application of carbon nanocomposites in ultra-high abrasion-resistant coatings, stable and durable seals, and bearings made of special materials in the field of centrifugal pump abrasion from solid particles will become the hotspot.
Statements
Author contributions
XJ and ZZ contributed to the conception of the study. XJ and SY wrote the article. BL, HM, JY, and CW researched the information. SY and YZ edited the article. All authors contributed to the article and approved the submitted version.
Funding
This work was supported by the National Natural Science Foundation of China (No. 51876110 and No. 51876103), and the Zhejiang Provincial Natural Science Foundation of China (No. LQ19E060011).
Conflict of interest
BL was employed by the company Hangzhou Weiguang Electronic Co., Ltd, Hangzhou, China. HM was employed by the company Hangzhou Dalu Industry Co., Ltd, Hangzhou, China. CW was employed by the company Zhejiang Institute of Mchanical & Electrical Engineering Co., Ltd, Hangzhou, China. The remaining authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.
References
1
AlgulH.TokurM.OzcanS.UysalM.CetinkayaT.AkbulutH.et al. (2015). The effect of graphene content and sliding speed on the wear mechanism of nickel-graphene nanocomposites. Appl. Surf. Sci. 359, 340–348. 10.1016/j.apsusc.2015.10.139
2
BarikR. C.WhartonJ. A.WoodR. J. K.StokesK. R. (2009). Electromechanical interactions during erosion-corrosion. Wear267, 1900–1908. 10.1016/j.wear.2009.03.011
3
BougnomB.McNallyA.EtoaF. X.PiddockL. (2019). Antibiotic resistance genes are abundant and diverse in raw sewage used for urban agriculture in Africa and associated with urban population density. Environ. Pollut. 251, 146–154. 10.1016/j.envpol.2019.04.056
4
BushuevaE.KuzinP.DrobyazE.GrinbergB. (2019). Wear resistance increasing of austenitic steel by the surface hardening with titanium carbide. Mater. Today Proc. 11, 342–347. 10.1016/j.matpr.2018.12.155
5
ChaoC.LinL.MacdonaldD. (1981). A point defect model for anodic passive films i. film growth kinetics. J. Electrochem. Soc. 128:2127591. 10.1149/1.2127591
6
ChenC.QiuS. H.CuiM. J.QinS. L.YanG. P.ZhaoH. C.et al. (2017). Achieving high performance corrosion and wear resistant epoxy coatings via incorporation of noncovalent functionalized graphene. Carbon114, 356–366. 10.1016/j.carbon.2016.12.044
7
ChenJ.LiuR. T.XiongX. (2019). Friction and wear behaviors of SiCNF modified carbon/carbon sealing materials. J. Mater. Res. Technol. 8, 5133–5139. 10.1016/j.jmrt.2019.08.036
8
ChenJ.XiongX.XiaoP.ZhangH. B. (2010). The catalytic effect of boric acid on polyacrylonitrile-based carbon fibers and the thermal conductivity of carbon/carbon composites produced from them. Carbon48, 2341–2346. 10.1016/j.carbon.2010.03.012
9
ChengJ.ChenS. L.ZhangF.ShenB.LuX. C.PanJ. S. (2019). Corrosion- and wear-resistant composite film of graphene and mussel adhesive proteins on carbon steel. Corros. Sci. 164:108351. 10.1016/j.corsci.2019.108351
10
DawsonJ. L.FerreiraM. (1986). Crevice corrosion on 316 stainless steel in 3 % sodium chloride solution. Corros. Sci. 26, 1027–1040. 10.1016/0010-938X(86)90131-9
11
DuJ.LiuY. H.YuS. R.LiW. F. (2004). Dry sliding friction and wear properties of Al2O3 and carbon short fibres reinforced Al−12Si alloy hybrid composites. Wear257, 930–940. 10.1016/j.wear.2004.05.009
12
El-EgamyS. S.BadawayW. A. (2004). Passivity and passivity breakdown of 304 stainless steel in alkaline sodium sulphate solutions. J. Appl. Electrochem. 34, 1153–1158. 10.1007/s10800-004-1709-x
13
FanM. H.ZhangG. M. (2014). Emerging contaminants in surface waters in China-A short review. Environ. Res. Lett. 9:074018. 10.1088/1748-9326/9/7/074018
14
FossatiA.BorgioliF.GalvanettoE.BacciT. (2006). Corrosion resistance properties of glow-discharge nitrided AISI 316L austenitic stainless steel in NaCl solutions. Corros. Sci.48, 1513–1527. 10.1016/j.corsci.2005.06.006
15
GalveleJ. (1978). Effect of molybdenum on the pitting potential of high purity 18% Cr ferritic stainless steels. J. Electrochem. Soc. 125, 1204–1208. 10.1149/1.2131650
16
GeT. H.ZhaoW. J.WuX. D.LanX. J.ZhangY. G.QiangY. J.et al. (2020). Incorporation of electroconductive carbon fibers to achieve enhanced anti-corrosion performance of zinc rich coatings. J. Colloid Interface Sci. 567, 113–125. 10.1016/j.jcis.2020.02.002
17
GuoH. X.LuB. T.LuoJ. L. (2005). Interaction of mechanical and electrochemical factors in erosion–corrosion of carbon steel. Electrochim. Acta51, 315–323. 10.1016/j.electacta.2005.04.032
18
IlevbareG. O.BursteinG. T. (2003). The inhibition of pitting corrosion of stainless steels by chromate and molybdate ions. Corros. Sci.45, 1545–1569. 10.1016/S0010-938X(02)00229-9
19
JiangJ. B.FengC. Q.QianW.ZhuL. Y.HanS.LinH. L. (2017). Effect of graphene oxide nanosheets and ultrasonic eletrodeposition technique on Ni–Mo/graphene oxide composite coatings. Mater. Chem. Phys. 199, 239–248. 10.1016/j.matchemphys.2017.07.010
20
KadiyaC.AlejandroG. M.CintaG. SFranciscoO.BelénRJesúsG. L. (2013). Archaeal diversity in biofilm technologies applied to treat urban and industrial wastewater: recent advances and future prospects. Int. J. Mol. Sci.14, 18572–18598. 10.3390/ijms140918572
21
KhoddamzadehA.LiuR.LiangM.YangQ. (2014). Wear resistant carbon fibre reinforced stellite alloy composites. Mater. Des. 56, 487–494. 10.1016/j.matdes.2013.11.034
22
KwokC. T.ChengF. T.ManH. C. (2000). Synergistic effects on cavitation erosion and corrosion of various engineering alloys in 3.5% NaCl solution. Mater. Sci. Eng. A290, 145–154. 10.1016/S0921-5093(00)00899-6
23
LeiJ. B.ShiC.ZhouS. F.GuZ. J.ZhangL. C. (2017). Enhanced corrosion and wear resistance properties of carbon fiber reinforced Ni-based composite coating by laser cladding. Surf. Coat. Tech. 334, 274–285. 10.1016/j.surfcoat.2017.11.051
24
LiuC.BiQ.LeylandA.MatthewsA. (2003). An electrochemical impedance spectroscopy study of the corrosion behaviour of PVD coated steels in 0.5 N NaCl aqueous solution: Part I. Establishment of equivalent circuits for EIS data modelling. Corros. Sci. 45, 1243–1256. 10.1016/S0010-938X(02)00213-5
25
LiuS.GuL.ZhaoH. C.ChengJ. M.YuH. B. (2016). Corrosion resistance of graphene-reinforced waterborne epoxy coatings. J. Mater. Sci. Technol. 32, 425–431. 10.1016/j.jmst.2015.12.017
26
MacdonaldD. D.Urquidi-MacdonaldM. (1985). Application of kramers—kronig transforms in the analysis of electrochemical systems I. polarization resistance. J. Electrochem. Soc. 132, 2316–2319. 10.1149/1.2113570
27
McNabbD. E. (2019). “The population growth barrier,” in Global Pathways to Water Sustainability (London: Palgrave Macmillan), 67–81. 10.1007/978-3-030-04085-7_5
28
MeguidE. A.MahmoudN. A.RehimS. S. (2000). The effect of some sulphur compounds on the pitting corrosion of type 304 stainless steel. Mater. Chem. Phys. 63, 67–74. 10.1016/S0254-0584(99)00206-0
29
MoustafaS.El-BadryS.SanadA.KiebackB. (2002). Friction and wear copper-graphite composites made with Cu-coated and uncoated graphite powders. Wear253, 699–710. 10.1016/S0043-1648(02)00038-8
30
MuellerJ. J.WrightI. G.DavisD. E. (1978). Erosion evaluation of materials for service in liquifaction coal slurry feed pumps. Proceedings of 3rd International Technical Conference on Slurry Transport. (Las-Vegas), 107–116
31
OkamotoG. (1973). Passive film of 18-8 stainless steel structure and its function. Corros. Sci. 13. 471–489. 10.1016/0010-938X(73)90031-0
32
PadhyM.SainiR. P. (2009). Effect of size and concentration of silt particles on erosion of Pelton turbine buckets. Energy34, 1477–1483. 10.1016/j.energy.2009.06.015
33
PagalthivarthiK.DesaiP.AddieG. (1990). Particulate motion and concentration fields in centrifugal slurry pumps. Particul. Sci. Technol. 8, 77–96. 10.1080/02726359008906557
34
RichardsonJ. A.WoodG. C. (1970). A study of the pitting corrosion of Al byscanning electron microscopy. Corros. Sci. 10, 313–323. 10.1016/S0010-938X(70)80023-3
35
RocoM. C.AddieG. R.DennisJ.NairP. (1984). Modeling Erosion Wear in Centrifugal Slurry Pumps. Hydrotransport 9. Rome: BHRA Fluid Engineering. Paper G1.
36
SahooT.GuharoyA. (2009). Energy cost savings with centrifugal pumps. World Pumps2009. 35–37. 10.1016/S0262-1762(09)70104-X
37
SavriamaY.StigeL.GerberS.PérezT.PaulA.DavidB. (2015). Impact of sewage pollution on two species of sea urchins in the Mediterranean Sea (Cortiou, France): radial asymmetry as a bioindicator of stress. Ecol. Indic. 54. 39–47. 10.1016/j.ecolind.2015.02.004
38
SchmidtD. L.DavidsonK. E.TheibertL. S. (1999). Unique applications of carbon-carbon composite materials. SAMPE J. 35. 27–39.
39
ShiC.LeiJ. B.ZhouS. F.DaiX. Q.ZhangL. C. (2018). Microstructure and mechanical properties of carbon fibers strengthened Ni-based coatings by laser cladding: the effect of carbon fiber contents. J. Alloys Compd. 744, 146–155. 10.1016/j.jallcom.2018.02.063
40
SolonK.Flores-AlsinaX.VaneeckhauteC.IkumiD.VolckeE. I. P.EkamaG.et al. (2017). Plant-wide modelling of phosphorus transformations in wastewater treatment systems: impacts of control and operational strategies. Water Res. 113, 97–110. 10.1016/j.watres.2017.02.007
41
SunS. S.WanM. S.WangH.ZhangY.XuX. M. (2019). Study of component high cycle bending fatigue based on a new critical distance approach. Eng. Fail. Anal. 102, 395–406. 10.1016/j.engfailanal.2019.04.050
42
SunX.LiuJ.JiL.WangG.ZhaoS.YoonJ. Y.et al. (2020). A review on hydrodynamic cavitation disinfection: the current state of knowledge. Sci. Total Environ. 737:139606. 10.1016/j.scitotenv.2020.139606
43
SunX.XuanX.SongY.JiaX.JiL.ZhaoS.et al. (2021). Experimental and numerical studies on the cavitation in an advanced rotational hydrodynamic cavitation reactor for water treatment. Ultrason. Sonochem. 70, 105311. 10.1016/j.ultsonch.2020.105311
44
SureshG.SrinivasanT.ChidambaramC. T.SanthoshpriyaK.VijayakumarK. R.MadheswaranD. K. (in press). A study on sliding wear behaviour of carbon fiber reinforced IPN composites. Materialstoday Proc.10.1016/j.matpr.2020.05.124
45
SureshaB.KumarK. (2009). Investigations on mechanical and two-body abrasive wear behaviour of glass/carbon fabric reinforced vinyl ester composites. Mater. Des. 30, 2056–2060. 10.1016/j.matdes.2008.08.038
46
TangY.LiuH. Z.ZhaoH. J.LiuL.WuY. T. (2008). Friction and wear properties of copper matrix composites reinforced with short carbon fibers. Mater. Des. 29, 257–261. 10.1016/j.matdes.2006.11.011
47
VenkateswaranP.VellaichamyS.PalaniveluK. (2007). Speciation of heavy metals in electroplating industry sludge and wastewater residue using inductively coupled plasma. Int. J. Environ. Sci. Technol. 4, 497–504. 10.1007/BF03325986
48
WalkerC. I.WellsP. J.Bodkin G. C. (1994), The Effect of Flow Rate Solid Particle Size on the Wear of Centrifugal Slurry Pumps.New York, NY: American Society of Mechanical Engineers. https://www.osti.gov/biblio/110086
49
WangH. J.WangQ. H.GuX. J. (2003). Actuality and prospect in research of oxidation-resistant properties for carbon/carbon composites. Mater. Sci. Eng. 21, 117–121 Available online at: http://en.cnki.com.cn/Article_en/CJFDTotal-CLKX200301030.htm
50
WilsonK. C.AddieG. R.SellgrenA.CliftR. (2006). Slurry Transport Using Centrifugal Pumps. Boston, MA: Springer.
51
WoodR. (2006). Erosion–corrosion interactions and their effect on marine and offshore materials. Wear261, 1012–1023. 10.1016/j.wear.2006.03.033
52
WuH. H.LiuF.GongW. B.YeF. Y.HaoL. F.JiangJ. B.et al. (2015). Preparation of Ni-P-GO composite coatings and its mechanical properties. Surf. Coat. Tech. 272, 25–32. 10.1016/j.surfcoat.2015.04.028
53
YanC. A.ZhangW. C.ZhangZ. J.LiuY. M.DengC.NieN. (2015). Assessment of water quality and identification of polluted risky regions based on field observations & GIS in the Honghe River Watershed, China. PLoS ONE10:e0119130. 10.1371/journal.pone.0119130
54
YangQ.LuoJ. L. (2001). Effects of hydrogen and tensile stress on the breakdown of passive films on type 304 stainless steel. Electrochim. Acta46, 851–859. 10.1016/S0013-4686(00)00661-7
55
ZhouS. G.WuY. M.ZhaoW. J.YuJ. J.JiangF. W.WuY. H.et al. (2019). Designing reduced graphene oxide/zinc rich epoxy composite coatings for improving the anticorrosion performance of carbon steel substrate. Mater. Des. 169:107694. 10.1016/j.matdes.2019.10769
Summary
Keywords
carbon materials, abrasion resistance, corrosion resistance, sewage pump, prospect
Citation
Jia X, Yuan S, Li B, Miu H, Yuan J, Wang C, Zhu Z and Zhang Y (2020) Carbon Nanomaterials: Application and Prospects of Urban and Industrial Wastewater Pollution Treatment Based on Abrasion and Corrosion Resistance. Front. Chem. 8:600594. doi: 10.3389/fchem.2020.600594
Received
30 August 2020
Accepted
06 October 2020
Published
12 November 2020
Volume
8 - 2020
Edited by
Xingtao Xu, National Institute for Materials Science, Japan
Reviewed by
Lulu Zheng, Henan Institute of Science and Technology, China; Songsong Sun, Nanjing Forestry University, China
Updates
Copyright
© 2020 Jia, Yuan, Li, Miu, Yuan, Wang, Zhu and Zhang.
This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY). The use, distribution or reproduction in other forums is permitted, provided the original author(s) and the copyright owner(s) are credited and that the original publication in this journal is cited, in accordance with accepted academic practice. No use, distribution or reproduction is permitted which does not comply with these terms.
*Correspondence: XiaoQi Jia jiaxq@zstu.edu.cnZuChao Zhu zhuzuchao01@163.com
This article was submitted to Green and Sustainable Chemistry, a section of the journal Frontiers in Chemistry
Disclaimer
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.